Abstract: | The temperature and frequency dependence of dielectric permittivity and dielectric loss of nanosized Mn1−xZnxFe2O4 (for x = 0, 0.2, 0.4, 0.6, 0.8, 1) were investigated. The impact of zinc substitution on the dielectric properties of the mixed ferrite is elucidated. Strong dielectric dispersion and broad relaxation were exhibited by Mn1−xZnxFe2O4. The variation of dielectric relaxation time with temperature suggests the involvement of multiple relaxation processes. Cole–Cole plots were employed as an effective tool for studying the observed phenomenon. The activation energies were calculated from relaxation peaks and Cole–Cole plots and found to be consistent with each other and indicative of a polaron conduction |
Description: | J. Phys.: Condens. Matter 21 (2009) 146006 (12pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4393 |
Files | Size |
---|---|
On the dielectr ... se zinc mixed ferrites.pdf | (4.818Mb) |
Abstract: | Here we report the multiferroic nature of charge ordered manganite Gd0.5Sr0.5MnO3 for the first time. The temperature variation of dielectric constant shows broad relaxor type ferroelectric transition at around 210K and magnetization measurements shows weak ferromagnetism at 50K. The dielectric peak is very close to charge ordering temperature which is an evidence of the link between electronic state and increase of dielectric response. Butterfly variation of capacitance with voltage confirms ferroelectric nature of the sample at room temperature |
Description: | Ferroelectrics, 392:13–19, 2009 |
URI: | http://dyuthi.cusat.ac.in/purl/4415 |
Files | Size |
---|---|
Multiferroic Behavior of Gd Based Manganite.pdf | (1.542Mb) |
Abstract: | Mn1-xZnxFe2O4 nanoparticles (x=0-1) were synthesized by wet chemical co-precipitation techniques. X-ray diffraction, transmission electron microscopy and high-resolution transmission electron microscopy were effectively utilized to investigate the different structural parameters. The elemental analysis was conducted using energy-dispersive spectrum and inductively coupled plasma analysis. The magnetic properties such as magnetization and coercivity were measured using vibrating sample magnetometer. The observed magnetization values of the nanoparticles were found to be lower compared to the bulk counterpart. The magnetization showed a gradual decrease with zinc substitution except for a small increase from x=0.2 to 0.3. The Curie temperature was found to be enhanced in the case of ferrites in the nanoregime. The variation in lattice constant, reduced magnetization values, variation of magnetization with zinc substitution, the presence of a net magnetic moment for the zinc ferrite and the enhancement in Curie temperature in Mn1-xZnxFe2O4 all provide evidence to the existence of a metastable cation distribution together with possible surface effects at the nanoregime. |
URI: | http://dyuthi.cusat.ac.in/purl/2833 |
Files | Size |
---|---|
Dyuthi-P00389.pdf | (1.422Mb) |
Abstract: | Nickel–rubber nanocomposites were synthesized by incorporating ferromagnetic nickel nanoparticles in a natural rubber as well as neoprene rubber matrix. Complex dielectric permittivity and magnetic permeability of these composites were evaluated in the X-band microwave frequencies at room temperature using cavity perturbation technique. The dielectric loss in natural rubber is smaller compared to neoprene rubber. A steady increase in the dielectric permittivity is observed with increase in the content of nickel in both the composites. The magnetic permeability exhibits a steady decrease with increase in frequency and magnetic loss shows a relaxation at 8 GHz. The suitability of these composites as microwave absorbers is modeled based on the reflection loss which is dependant on the real and imaginary components of the complex dielectric permittivity and magnetic permeability. |
Description: | Appl Phys A (2009) 97: 157–165 |
URI: | http://dyuthi.cusat.ac.in/purl/4402 |
Files | Size |
---|---|
Effect of nicke ... n rubber in the X-band.pdf | (1.140Mb) |
Abstract: | Magnetic heterostructures with carbon nanotubes having multiple functionalities are fascinating materials which can be manipulated by means of an external magnetic field. In this paper we report our investigations on the synthesis and optical limiting properties of pristine cobalt nanotubes and high coercivity cobalt-in-carbon nanotubes (a new nanosystem where carbon nanotubes are filled with cobalt nanotubes). A general mobility assisted growth mechanism for the formation of one-dimensional nanostructures inside nanopores is verified in the case of carbon nanotubes. The open-aperture z-scan technique is employed for the optical limiting measurements in which nanosecond laser pulses at 532 nm have been used for optical excitation. Compared to the benchmark pristine carbon nanotubes these materials show an enhanced nonlinear optical absorption, and the nonlinear optical parameters calculated from the data show that these materials are efficient optical limiters. To the best of our knowledge this is the first report where the optical limiting properties of metal nanotubes are compared to those of carbon nanotubes |
Description: | Nanotechnology 20 (2009) 285702 (7pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4370 |
Files | Size |
---|---|
The synthesis o ... cal limitingproperties.pdf | (1.704Mb) |
Abstract: | Two-dimensional electronic systems play a crucial role in modern electronics and offer a multitude of opportunities to study the fundamental phenomena at low dimensional physics. A quantum well heterostructure based on polyaniline (P) and iodine doped polyaniline (I) thin films were fabricated using radio frequency plasma polymerization on indium tin oxide coated glass plate. Scanning probe microscopy and scanning electron microscopy studies were employed to study the morphology and roughness of the polymer thin films. Local electronic density of states (LDOS) of the P–I–P heterostructures is probed using scanning tunnelling spectroscopy (STS). A step like LDOS is observed in the P–I–P heterostructure and is attributed to the quantum well confinement of electrons in the polymer heterostructure. |
Description: | J. Phys. D: Appl. Phys. 42 (2009) 165309 (7pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4416 |
Files | Size |
---|---|
Fabrication of ... erized aniline and its.pdf | (853.9Kb) |
Abstract: | Mn1−xZnxFe2O4 nanoparticles (x = 0 to 1) were synthesized by the wet chemical co-precipitation technique. X-ray diffraction and transmission electron microscopy and high resolution transmission electron microscopy were effectively utilized to investigate the different structural parameters. The ac conductivity of nanosized Mn1−xZnxFe2O4 were investigated as a function of frequency, temperature and composition. The frequency dependence of ac conductivity is analysed by the power law σ(ω)ac = Bωn which is typical for charge transport by hopping or tunnelling processes. The temperature dependence of frequency exponent n was investigated to understand the conduction mechanism in different compositions. The conduction mechanisms are mainly based on polaron hopping conduction |
Description: | J. Phys. D: Appl. Phys. 42 (2009) 165005 (8pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4397 |
Files | Size |
---|---|
Mechanism of ac ... se zinc mixed ferrites.pdf | (2.619Mb) |
Abstract: | We investigated the influence of substrate surface roughness on the structural and magnetic properties of obliquely deposited amorphous nanocolumns of Fe–Ni. Experiments showed that the surface roughness of the substrate greatly determines the morphology of the columnar structures and this in turn has a profound influence on the magnetic properties. Nucleation of Fe–Ni nanocolumns on a smooth silicon substrate was at random, while that on a rough glass substrate was defined by the irregularities on the substrate surface. It has been found that magnetic interaction between the nanocolumns prepared on a silicon substrate was due to their small inter-column separation. Well separated nanocolumns on a glass substrate resulted in exchange isolated magnetic domains. The size, shape and the distribution of nanocolumns can be tailored by appropriately choosing the surface roughness of the substrate. This will find potential applications in thin film magnetism. |
Description: | J. Phys. D: Appl. Phys. 42 (2009) 215005 (8pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4405 |
Files | Size |
---|---|
Influence of su ... s nanocolumns of Fe–Ni.pdf | (1.327Mb) |
Abstract: | Hybrid magnetic nanostructures with high coercivity have immense application potential in various fields. Nickel (Ni) electrodeposited inside Cobalt (Co) nanotubes (a new system named Ni @ Co nanorods) were fabricated using a two-step potentiostatic electrodeposition method. Ni @ Co nanorods were crystalline, and they have an average diameter of 150 nm and length of *15 lm. The X-ray diffraction studies revealed the existence of two separate phases corresponding to Ni and Co. Ni @ Co nanorods exhibited a very high longitudinal coercivity. The general mobility-assisted growth mechanism proposed for the growth of one-dimensional nanostructures inside nano porous alumina during potentiostatic electrodeposition is found to be valid in this case too |
Description: | Nanoscale Res Lett (2010) 5:164–168 |
URI: | http://dyuthi.cusat.ac.in/purl/4375 |
Files | Size |
---|---|
Synthesis of Hi ... ir Magnetic Properties.pdf | (349.6Kb) |
Abstract: | Rubber–nickel nanocomposites were synthesized by incorporating freshly prepared nanometric nickel particles in two different matrices namely natural rubber and neoprene rubber according to specific recipes for various loadings of nano nickel and the cure characteristics of these composites were evaluated. The maximum torque values register an increase with the increase in loading of nickel in both composites and this is attributed to the non-interacting nature of nickel nanoparticles with rubber matrices. The cure time of natural rubber composites decreases with increase in the content of nickel, and in neoprene rubber cure, time increases with increase in filler content. In natural rubber, the curing reaction seems to be activated by the presence of nickel particles. The magnetization studies of the composites reveal that the magnetic properties of nickel are retained in the composite samples. The elastic modulus of natural rubber and neoprene rubber are largely improved by the incorporation of nickel particles |
Description: | Polym. Bull. (2010) 64:907–923 |
URI: | http://dyuthi.cusat.ac.in/purl/4392 |
Files | Size |
---|---|
On the magnetic ... –nickel nanocomposites.pdf | (483.8Kb) |
Abstract: | Rubber ferrite composites were prepared by incorporating nickel ferrite in a neoprene rubber matrix. Kinetics of the cure reaction were determined from the rheometric torque values and found to follow first-order kinetics. Analysis of the swelling behavior of the rubber ferrite composites in toluene elucidates the mechanism of solvent penetration and sorption characteristics, and reveals the extent of the physical interaction of the ferrite particles with the neoprene rubber matrix. Mechanical properties of rubber ferrite composites were determined, which support the reinforcing nature of nickel ferrite to the neoprene rubber matrix. These results show that magnetic composites with the required processing safety can be prepared economically by incorporating higher amounts of nickel ferrite in the neoprene rubber matrix |
Description: | International Journal of Polymeric Materials, 59:173–183, 2010 |
URI: | http://dyuthi.cusat.ac.in/purl/4425 |
Files | Size |
---|---|
Cure Kinetics a ... ber Ferrite Composites.pdf | (327.4Kb) |
Abstract: | Metallic glass alloy Metglas 2826 MB based amorphous magnetic thin films were fabricated by the thermal evaporation technique. Transmission electron micrographs and electron diffraction pattern showed the amorphous nature of the films. Composition of the films was analyzed employing X-ray photoelectron spectroscopy and energy dispersive X-ray spectroscopy techniques. The film was integrated to a long period fibre grating. It was observed that the resonance wavelength of the fibre grating decreased with an increase in the magnetic field. Change in the resonance wavelength was minimal at higher magnetic fields. Field dependent magnetostriction values revealed the potential application of these films in magnetostrictive sensor devices. |
URI: | http://dyuthi.cusat.ac.in/purl/2840 |
Files | Size |
---|---|
Dyuthi-P00393.pdf | (556.3Kb) |
Abstract: | Bio-compatible magnetic fluids having high saturation magnetization find immense applications in various biomedical fields. Aqueous ferrofluids of superparamagnetic iron oxide nanoparticles with narrow size distribution, high shelf life and good stability is realized by controlled chemical co-precipitation process. The crystal structure is verified by X-ray diffraction technique. Particle sizes are evaluated by employing Transmission electron microscopy. Room temperature and low-temperature magnetic measurements were carried out with Superconducting Quantum Interference Device. The fluid exhibits good magnetic response even at very high dilution (6.28 mg/cc). This is an advantage for biomedical applications, since only a small amount of iron is to be metabolised by body organs. Magnetic field induced transmission measurements carried out at photon energy of diode laser (670 nm) exhibited excellent linear dichroism. Based on the structural and magnetic measurements, the power loss for the magnetic nanoparticles under study is evaluated over a range of radiofrequencies. |
URI: | http://dyuthi.cusat.ac.in/purl/2964 |
Files | Size |
---|---|
Dyuthi-P00409.pdf | (443.7Kb) |
Abstract: | Nickel nanocomposites were prepared by incorporating nickel nanoparticles in a neoprene matrix according to a specific recipe for various loadings of nickel particles. The dielectric properties of these composites were evaluated for different frequencies ranging from 100 kHz to 8MHz at different temperatures from 30 ◦C to 120 ◦C. The dielectric permittivity increases with increase of nickel concentration. Increase in temperature enhances the permittivity initially, till 40 ◦C and thereafter the permittivity decreases. The dielectric loss exhibits relaxation peaks and the peaks shift to lower frequencies with increase in volume fraction of the nickel nanoparticles in the matrix. The evaluation of magnetic and dielectric properties of these composites suggests that the dielectric permittivity can be tailored by an appropriate loading of the filler using semi-empirical equations and the magnetic properties vary according to simple mixture equations |
Description: | Materials Chemistry and Physics 121 (2010) 154–160 |
URI: | http://dyuthi.cusat.ac.in/purl/4408 |
Files | Size |
---|---|
On the magnetic ... eoprene nanocomposites.pdf | (1.316Mb) |
Abstract: | The carrier transport mechanism of polyaniline (PA) thin films prepared by radio frequency plasma polymerization is described in this paper. The mechanism of electrical conduction and carrier mobility of PA thin films for different temperatures were examined using the aluminium–PA–aluminium (Al–PA–Al) structure. It is found that the mechanism of carrier transport in these thin films is space charge limited conduction. J –V studies on an asymmetric electrode configuration using indium tin oxide (ITO) as the base electrode and Al as the upper electrode (ITO–PA–Al structure) show a diode-like behaviour with a considerable rectification ratio |
Description: | J. Phys. D: Appl. Phys. 43 (2010) 055403 (6pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4401 |
Files | Size |
---|---|
Determination o ... izedaniline thin films.pdf | (402.7Kb) |
Abstract: | The magnetocaloric properties of cobalt ferrite nanoparticles were investigated to evaluate the potential of these materials as magnetic refrigerants. Nanosized cobalt ferrites were synthesized by the method of sol–gel combustion. The nanoparticles were found to be spherical with an average crystallite size of 14 nm. The magnetic entropy change ( Sm) calculated indirectly from magnetization isotherms in the temperature region 170–320 K was found to be negative, signifying an inverse magnetocaloric effect in the nanoparticles. The magnitudes of the Sm values were found to be larger when compared to the reported values in the literature for the corresponding ferrite materials in the nanoregime. |
Description: | Appl Phys A (2010) 99: 497–503 |
URI: | http://dyuthi.cusat.ac.in/purl/4365 |
Files | Size |
---|---|
Inverse magneto ... rived nanosized cobalt.pdf | (807.0Kb) |
Abstract: | Potential applications of nickel nanoparticles demand the synthesis of self-protected nickel nanoparticles by different synthesis techniques. A novel and simple technique for the synthesis of self-protected nickel nanoparticles is realized by the inter-matrix synthesis of nickel nanoparticles by cation exchange reduction in two types of resins. Two different polymer templates namely strongly acidic cation exchange resins and weakly acidic cation exchange resins provided with cation exchange sites which can anchor metal cations by the ion exchange process are used. The nickel ions which are held at the cation exchange sites by ion fixation can be subsequently reduced to metal nanoparticles by using sodium borohydride as the reducing agent. The composites are cycled repeating the loading reduction cycle involved in the synthesis procedure. X-Ray Diffraction, Scanning Electron Microscopy, Transmission Electron microscopy, Energy Dispersive Spectrum, and Inductively Coupled Plasma Analysis are effectively utilized to investigate the different structural characteristics of the nanocomposites. The hysteresis loop parameters namely saturation magnetization and coercivity are measured using Vibrating Sample Magnetometer. The thermomagnetization study is also conducted to evaluate the Curie temperature values of the composites. The effect of cycling on the structural and magnetic characteristics of the two composites are dealt in detail. A comparison between the different characteristics of the two nanocomposites is also provided |
Description: | Nanoscale Res Lett (2010) 5:889–897 |
URI: | http://dyuthi.cusat.ac.in/purl/4390 |
Files | Size |
---|---|
Template-Assist ... edNickel Nanoparticles.pdf | (815.2Kb) |
Abstract: | Plasma polymerization is found to be an excellent technique for the preparation of good quality, pinhole-free, polymer thin films from different monomer precursors. The present work describes the preparation and characterization of polypyrrole (PPy) thin films by ac plasma polymerization technique in their pristine and in situ iodine doped forms. The electrical conductivity studies of the aluminiumpolymeraluminium (AlpolymerAl) structures have been carried out and a space charge limited conduction (SCLC) mechanism is identified as the most probable mechanism of carrier transport in these polymer films. The electrical conductivity shows an enhanced value in the iodine doped sample. The reduction of optical band gap by iodine doping is correlated with the observed conductivity results. |
URI: | http://dyuthi.cusat.ac.in/purl/2835 |
Files | Size |
---|---|
Dyuthi-P00391.pdf | (582.5Kb) |
Abstract: | Manganites belonging to the series Gd1−xSrxMnO3 (x=0.3, 0.4 and 0.5) were prepared by wet solid-state reaction and their thermoelectric power was evaluated. Thermoelectric power measurements revealed a peak value at ∼40 K. All the samples exhibited a colossal thermopower at ∼40K and in that Gd0.5Sr0.5MnO3 exhibited a maximum value of ∼35mV/K, which is the largest reported for these class of materials at this temperature. Temperaturedependent magnetisation measurements showed that the samples exhibit a phase transition from paramagnetic to spin-glass–like state at these temperatures. Plausible mechanisms responsible for the observed colossal thermoelectric power in Gd-Sr manganites are discussed |
Description: | EPL (Europhysics Letters),vol 91,issue 1,17008 |
URI: | http://dyuthi.cusat.ac.in/purl/4414 |
Files | Size |
---|---|
Colossal thermo ... er in Gd-Sr manganites.pdf | (361.9Kb) |
Abstract: | Rubber ferrite composites (RFC) are magnetic polymer composites and have a variety of applications as flexible magnets, pressure=photo sensors, and microwave absorbers. The mouldability into complex shapes is one of the advantages of these magnetic elastomers. They have the potential of replacing the conventional ceramic materials, due to theire flexible nature. In the present study, the incorporation of pre-characterized hexagonal ferrites, namely barium ferrite (BaFe12O19), into natural rubber matrix is carried out according to a suitable recipe for various loadings of the filler. The processability of these compounds was determined by evaluating the cure characteristics: scorch time, cure time, and minimum and maximum torque. It has been found that the addition of magnetic fillers does not affect the processability of the composites, whereas the physical properties are modified. The magnetic properties of these composites containing various loadings of the magnetic filler were also investigated. The magnetic properties of RFC can be controlled by the addition of appropriate amount of the ferrite filler. |
Description: | International Journal of Polymeric Materials, 53:565–575, 2004 |
URI: | http://dyuthi.cusat.ac.in/purl/4406 |
Files | Size |
---|---|
Processability ... taining Barium Ferrite.pdf | (172.8Kb) |