Colossal thermoelectric power in Gd-Sr manganites

Abstract

Manganites belonging to the series Gd1−xSrxMnO3 (x=0.3, 0.4 and 0.5) were prepared by wet solid-state reaction and their thermoelectric power was evaluated. Thermoelectric power measurements revealed a peak value at ∼40 K. All the samples exhibited a colossal thermopower at ∼40K and in that Gd0.5Sr0.5MnO3 exhibited a maximum value of ∼35mV/K, which is the largest reported for these class of materials at this temperature. Temperaturedependent magnetisation measurements showed that the samples exhibit a phase transition from paramagnetic to spin-glass–like state at these temperatures. Plausible mechanisms responsible for the observed colossal thermoelectric power in Gd-Sr manganites are discussed