Rani, Joseph(OPA (Overseas Publishers Association), July 15, 1994)
[+]
[-]
Abstract:
The mechanical properties of filled natural rubber latex vulcanizates were found to be improved by the
addition of polyethylene glycols of different molecular weight and glycerol. There is a slight reduction
in the optimum cure times of the compounds containing PEG/Glycerol. The morphology study shows
that the filler distribution is more uniform in the compounds containing PEG/Glycerol.
Rani, Joseph(Indian Academy of Sciences., September 30, 2005)
[+]
[-]
Abstract:
Natural rubber/isora fibre composites were cured at various temperatures. The solvent swelling
characteristics of natural rubber composites containing both untreated and alkali treated fibres were investigated
in aromatic and aliphatic solvents like toluene, and n-hexane. The diffusion experiments were conducted by
the sorption gravimetric method. The restrictions on elastomer swelling exerted by isora fibre as well as the
anisotropy of swelling of the composite have been confirmed by this study. Composite cured at 100°C shows
the lowest percentage swelling. The uptake of aromatic solvent is higher than that of aliphatic solvent for the
composites cured at all temperatures. The effect of fibre loading on the swelling behaviour of the composite was
also investigated in oils like petrol, diesel, lubricating oil etc. The % swelling index and swelling coefficient of
the composite were found to decrease with increase in fibre loading. This is due to the increased hindrance exerted
by the fibres at higher fibre loadings and also due to the good fibre-rubber interactions. Maximum uptake
of solvent was observed with petrol followed by diesel and then lubricating oil. The presence of bonding agent in
the composites restrict the swelling considerably due to the strong interfacial adhesion. At a fixed fibre loading,
the alkali treated fibre composite showed lower percentage swelling compared to the untreated one.
Zinc salts of ethyl, isopropyl and butyl xanthates were prepared in the laboratory. The
effect of these xanthates with zinc diethyldithiocarbamate (ZDC) on the vulcanization
of HAF filled NR compound has been studied at different temperatures. The
rubber compounds with the three xanthate accelerators and ZDC were cured at various
temperatures from 60°C to 150°C. The sheets were moulded and properties such as tensile
strength , tear strength , cross-link density, elongation -at-break, compression set, heat
build up, abrasion resistance, flex resistance , etc. were evaluated . The properties
showed that zinc xanthate/ZDC accelerator combination has a positive synergistic effect
on the mechanical properties of NR compounds. The curing of HAF filled NR compound
containing zinc xanthate /ZDC is slightly slower than the curing of the corresponding gum
compounds . It is observed that, by gradually increasing the amount of the accelerator, the
cure time of black filled NR compound can be made equal to that of the gum compou
Rani, Joseph(John Wiley & Sons, Inc., November 1, 2000)
[+]
[-]
Abstract:
ABSTRACT: p-Phenylenediamine was chemically attached to low molecular weight chlorinated
paraffin wax. The polymer-bound p-phenylenediamine was characterized by
vapor-phase osmometry (VPO), proton magnetic resonance spectroscopy ('H-NMR),
infrared spectroscopy (IR), and thermogravimetric analysis (TGA). The efficiency and
permanence of the polymer-bound p-phenylenediamine as an antioxidant was compared
with a conventional amine-type antioxidant in natural rubber vulcanizates. The
vulcanizates showed improved aging resistance in comparison to vulcanizates containing
a conventional antioxidant. The presence of liquid polymer-bound p-phenylenediamine
also reduces the amount of the plasticizer required for compounding.
Rani, Joseph(Huthig & Wepf Verlag, Basel, April 29, 1986)
[+]
[-]
Abstract:
Tribasic lead sulphate is tried as a practical curing agent for polychloroprene. The
cure characteristics of the compounds as well as the technical properties of the
vulcanizates show that it can act as a potential curative.
Rani, Joseph(OPA (Overseas Publishers Association), May 28, 1995)
[+]
[-]
Abstract:
Amine Terminated Liquid Natural Rubber (ATNR) was used as a plasticiser in filled NR and NBR
compounds replacing oil/DOP. The scorch time and cure time were found to be lowered when ATNR
was used as the plasticiser. ATNR was found to improve the mechanical properties like tensile strength,
tear strength and modulus of the vulcanizates . The ageing resistance of the vulcanizates containing ATNR
was superior compared to the vulcanizates containing oil/DOP.
Carboxy Terminated Liquid Natural Rubber (CTNR) was
prepared by photochemical reaction using maleic anhydride and masticated
natural rubber (NR). The use of CTNR as an adhesive in bonding rubber to
rubber and rubber to metal was studied. The peel strengths and lap shear
strengths of the adherends which were bonded using CTNR were determined.
The effect of using a tri isocyanate with CTNR in rubber to metal bonding was
also studied. It is found that CTNR can effectively be used in bonding rubber to
rubber and rubber to mild steel.
Rani, Joseph(Gordon and Breach Science Publishers S.A., October 16, 1992)
[+]
[-]
Abstract:
Butyl (IIR) tube reclaim (RR) was mixed with carbon black filled natural rubber (NR) compounds at
various percentages. The blend containing a low percentage of RR was found to show improved ageing
resistance and improved processability with out much reduction in the mechanical properties.
Rani, Joseph(Huthig & Wepf Verlag,Basel, April 16, 1993)
[+]
[-]
Abstract:
Scrap latex products contain rubber hydrocarbon of very high quality, that is only
slightly crosslinked. A novel economic technique for converting such latex waste into
a processible material is developed. This paper reports the effect of adding this latex
reclaim to natural rubber. It is shown that latex reclaim can replace raw natural rubber
up to about 50 wt.% without affecting mechanical properties.
Waste latex products are converted to a processabto material by a novel
economical process developed in our laboratory , It contains rubber hydrocarbon
of very high quality and Is lightly cross -linked. Styrene-butadlene
rubber is mixed with latex reclaim In different proportions . The mechanical
properties are found to be improved up to 60 percent replacement of
styrene-butadlene rubber by latex reclaim . The curing of styrene-butadiene
rubber Is found to be accelerated by the addition of latex reclaim. The
processablllty study shows that the blends can be processed similar to
SBRINR blends.
Rani, Joseph(John Wiley & Sons, Inc., March 20, 2000)
[+]
[-]
Abstract:
ABSTRACT: Zinc salts of ethyl, isopropyl, and butyl xanthates were prepared in the
laboratory. They were purified by reprecipitation and were characterized by IR, NMR,
and thermogravimetric analysis techniques. The melting points were also determined.
The rubber compounds with different xanthate accelerators were cured at temperatures
from 30 to 150°C. The sheets were molded and properties such as tensile strength,
tear strength, crosslink density, elongation at break, and modulus at 300% elongation
were evaluated. The properties showed that all three xanthate accelerators are effective
for room temperature curing.