Abstract: | The microwave dielectric properties of (I -x)CaTiO3-xSm(Mg1/2Tit,2)O3(0.1 <-x< 1.0) have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 86 to 25 as x varies from 0.1 to 1.0. The Qxf varies non-linearly and increases for composition with x> 0.6. The nonmonotonic variation with composition x is more pronounced in Tt than in er. The microwave dielectric properties indicate the possibility of a phase transformation for x between 0.4 and 0.5 |
URI: | http://dyuthi.cusat.ac.in/purl/1453 |
Files | Size |
---|---|
Microwave diele ... 3 [0. 1 _x 1] ceramics.PDF | (2.946Mb) |
Abstract: | Ceramic dielectric resonators in the BaO-RE2O3-TiO2 (RE = rare earth) system have been prepared by the conventional solid state ceramic route. The dielectric properties have been tailored by substitution of different rare earth oxides and by bismuth oxide addition. The dielectric constants increased with Bi addition whereas the 0 decreased. The temperature coefficient of the resonant frequency improved with bismuth addition |
URI: | http://dyuthi.cusat.ac.in/purl/1445 |
Files | Size |
---|---|
Tailoring the m ... mpositional variations.PDF | (4.793Mb) |
Abstract: | The microwave dielectric properties of ZnAl2O4 spinels were investigated and their properties were tailored by adding different mole fractions of Ti02. The samples were synthesized using the mixed oxide rout.e. The phase purity and crystal structure were identified using X-ray diffraction technique. The sintered specimens were characterized in the microwave frequency range (3-13 GHz). The ZnA12O4 ceramics exhibited interesting dielectric properties (dielectric constant (e,.) = 8.5, unloaded quality factor (Q.) = 4590 at 12.27 GHz and temperature coefficient of resonant frequency (Tf) = -79 ppm/°C). Addition of Ti02 into the spinel improved its properties and the Tf approached zero for 0.83ZnAl2O4- 0.17TiO2• This temperature compensated composition has excellent microwave dielectric properties (Cr _ 12.67, Q, = 9950 at 10.075 GHz) which can be exploited for microwave substrate applications |
URI: | http://dyuthi.cusat.ac.in/purl/1492 |
Files | Size |
---|---|
Temperature sta ... substrate applications.PDF | (3.226Mb) |