Abstract: | An open cell configuration has been employed for the photoacoustic measurement of the thermal diffusivity of undoped Bi2Se3 crystals and Bi2Se3 crystals doped with various concentrations of Te. The amplitude of the photoacoustic signal obtained under heat transmission configuration as a function of chopping frequency is used to evaluate the numerical value of thermal diffusivity, α. Doped samples show a substantial reduction in the value of α compared to undoped samples. The variations in the thermal diffusivity of the doped samples are explained in terms of the phonon assisted heat transfer mechanism. It is seen that α is very sensitive to structural variations arising from doping. The experimentally observed results are correlated with X-ray diffraction studies. |
URI: | http://dyuthi.cusat.ac.in/purl/2440 |
Files | Size |
---|---|
Dyuthi-P0248.pdf | (225.1Kb) |
Abstract: | In this paper, we report the measurements of thermal diffusivity of nano Ag metal dispersed ceramic alumina matrix sintered at different temperatures using laser induced non-destructive photoacoustic technique. Measurements of thermal diffusivity also have been carried out on specimens with various concentration of nano metal. Analysis of the data is done on the basis of one-dimensional model of Rosencwaig and Gersho. The present measurements on the thermal diffusivity of nano metal dispersed ceramic alumina shows that porosity has a great influence on the heat transport and the thermal diffusivity value. The present analysis also shows that the inclusion of nano metal into ceramic matrix increases its interconnectivity and hence the thermal diffusivity value. The present study on the samples sintered at different temperature shows that the porosity of the ceramics varies considerably with the change in sintering temperature. The results are interpreted in terms of phonon assisted heat transfer mechanism and the exclusion of pores with the increase in sintering temperature. |
URI: | http://dyuthi.cusat.ac.in/purl/1785 |
Files | Size |
---|---|
Dyuthi-P0253.pdf | (75.60Kb) |
Abstract: | An open cell photoacoustic (PA) configuration has been employed to evaluate the thermal diffusivity of intrinsic InP as well as InP doped with tin and iron. Thermal diffusivity data have been evaluated from variation of phase of PA signal as a function of modulation frequency. In doped samples, we observe a reduced value for thermal diffusivity in comparison with intrinsic InP. We also observed that, while the phase of the PA signal varies linearly with the square root of chopping frequency for doped samples, the intrinsic material does not exhibit such behaviour in the experimental frequency range. These results have been interpreted in terms of the heat generation and phonon assisted heat diffusion mechanisms in semiconductors. |
URI: | http://dyuthi.cusat.ac.in/purl/2406 |
Files | Size |
---|---|
Dyuthi-P0240.pdf | (147.6Kb) |
Abstract: | An open-cell configuration of the photoacoustic (PA) technique is employed to determine the thermal and transport properties of intrinsic Si and Si doped with B (p-type) and P (n-type). The experimentally obtained phase of the PA signal under heat transmission configuration is fitted to that of theoretical model by taking thermal and transport properties, namely, thermal diffusivity, diffusion coefficient, and surface recombination velocity, as adjustable parameters. It is seen from the analysis that doping and also the nature of dopant have a strong influence on the thermal and transport properties of semiconductors. The results are interpreted in terms of the carrier-assisted and phonon-assisted heat transfer mechanisms in semiconductors as well as the various scattering processes occurring in the propagation of heat carriers. |
URI: | http://dyuthi.cusat.ac.in/purl/2486 |
Files | Size |
---|---|
Dyuthi-P0255.pdf | (729.3Kb) |
Abstract: | Complete thermal characterization of liquid crystal mixtures in the smectic phase consisting of various relative volume fractions of cholesterol and 1-hexadecanol have been carried out using the photoacoustic technique. Thermal diffusivity values of these liquid crystal mixtures are evaluated using the open cell photoacoustic technique whereas the thermal effusivity value is measured using the conventional photoacoustic technique. From the measured values of these transient thermophysical parameters, the thermal conductivity and heat capacity of the sample under investigation are calculated. Analyses of the results show that all the thermophysical parameters depend strongly on the volume fraction of the constituents. Results are interpreted in terms of enhanced hydrogen bonding and the consequent enhancement in cohesive thermal energy transport with increasing volume fraction of 1-hexadecanol |
URI: | http://dyuthi.cusat.ac.in/purl/1803 |
Files | Size |
---|---|
Photoacoustic studies on thermal.pdf | (435.4Kb) |
Abstract: | We report a photoacoustic (PA) study of the thermal and transport properties of a GaAs epitaxial layer doped with Si at varying doping concentration, grown on GaAs substrate by molecular beam epitaxy. The data are analyzed on the basis of Rosencwaig and Gersho’s theory of the PA effect. The amplitude of the PA signal gives information about various heat generation mechanisms in semiconductors. The experimental data obtained from the measurement of the PA signal as a function of modulation frequency in a heat transmission configuration were fitted with the phase of PA signal obtained from the theoretical model evaluated by considering four parameters—viz., thermal diffusivity, diffusion coefficient, nonradiative recombination time, and surface recombination velocity—as adjustable parameters. It is seen from the analysis that the photoacoustic technique is sensitive to the changes in the surface states depend on the doping concentration. The study demonstrates the effectiveness of the photoacoustic technique as a noninvasive and nondestructive method to measure and evaluate the thermal and transport properties of epitaxial layers. |
URI: | http://dyuthi.cusat.ac.in/purl/2479 |
Files | Size |
---|---|
Dyuthi-P0244.pdf | (714.6Kb) |
Abstract: | Laser-induced nondestructive photoacoustic (PA) technique has been employed to determine the thermal diffusivity of nanometal (Ag) dispersed ceramic alumina matrix sintered at different temperatures. The thermal diffusivity values are evaluated by knowing the transition frequency from the amplitude spectrum of PA signal using the one-dimensional heat flow model of Rosencwaig and Gersho. Analysis of the data shows that heat transport and hence the thermal diffusivity value is greatly affected by the influence of incorporation of foreign atom. It is also seen that sintering temperature affects the thermal diffusivity value in a substantial manner. The results are interpreted in terms of variation in porosity and carrier-assisted heat transport mechanism in nanometal dispersed ceramics. |
URI: | http://dyuthi.cusat.ac.in/purl/2478 |
Files | Size |
---|---|
Dyuthi-P0271.pdf | (885.0Kb) |
Abstract: | The laser induced non-destructive photoacoustic technique has been employed to measure the thermal diffusivity of lanthanum phosphate ceramics prepared by the sol–gel route. The thermal diffusivity value was evaluated by knowing the transition frequency between the thermally thin to thermally thick region from the log–log plot of photoacoustic amplitude versus chopping frequency. Analysis of the data was carried out on the basis of the one-dimensional model of Rosencwaig and Gersho. The present investigation reveals that the sintering temperature has great influence on the propagation of heat carriers and hence on the thermal diffusivity value. The results were interpreted in terms of variations in porosity with sintering temperature as well as with changes in grain size. |
URI: | http://dyuthi.cusat.ac.in/purl/2419 |
Files | Size |
---|---|
Dyuthi-P0266.pdf | (180.5Kb) |
Abstract: | In this paper, we report the in-plane and cross-plane measurements of the thermal diffusivity of double epitaxial layers of n-type GaAs doped with various concentrations of Si and a p-type Be-doped GaAs layer grown on a GaAs substrate by the molecular beam epitaxial method, using the laser-induced nondestructive photothermal deflection technique. The thermal diffusivity value is evaluated from the slope of the graph of the phase of the photothermal deflection signal as a function of pump-probe offset. Analysis of the data shows that the cross-plane thermal diffusivity is less than that of the in-plane thermal diffusivity. It is also seen that the doping concentration has a great influence on the thermal diffusivity value. Measurement of p-type Be-doped samples shows that the nature of the dopant also influences the effective thermal diffusivity value. The results are interpreted in terms of a phonon-assisted heat transfer mechanism and the various scattering process involved in the propagation of phonons. |
URI: | http://dyuthi.cusat.ac.in/purl/1808 |
Files | Size |
---|---|
Photothermal de ... GaAs epitaxial layers.pdf | (221.8Kb) |
Abstract: | Two-photon absorption spectrum of aniline is recorded using thermal lens effect with optical parametric oscillator as the pump source. Studies show that the two-photon absorption spectrum observed corresponds to I Al -. I B2 transition of aniline. |
URI: | http://dyuthi.cusat.ac.in/purl/2471 |
Files | Size |
---|---|
Dyuthi-P0245.pdf | (376.1Kb) |
Abstract: | A sensitive method based on the principle of photothermal phenomena to study the energy transfer processes in organic dye mixtures is presented. A dual beam thermal lens method can be very effectively used as an alternate technique to determine the molecular distance between donor and acceptor in fluorescein–rhodamine B mixture using optical parametric oscillator. |
URI: | http://dyuthi.cusat.ac.in/purl/2416 |
Files | Size |
---|---|
Dyuthi-P0257.pdf | (172.7Kb) |
Abstract: | An open cell photoacoustic configuration has been employed to evaluate the thermal diffusivity of pure InP as well as InP doped with sulphur and iron. Chopped optical radiation at 488 nm from an Ar-ion laser has been used to excite photoacoustic signals which been detected by a sensitive electret microphone. Thermal diffusivity value have been calculated from phase versus chopping frequency plots. Doped sample are found to show a reduced value for thermal diffusivity in comparison with intrinsically pure sample. The results have been interpreted in terms of the mechanisms of heat generation and transmission in semiconductors. |
URI: | http://dyuthi.cusat.ac.in/purl/2469 |
Files | Size |
---|---|
Dyuthi-P0232.pdf | (657.8Kb) |
Abstract: | Thermal diffusivity of the composites of camphor sulphonic acid (CSA) doped polyaniline (PANI) and its composites with cobalt phthalocyanine (CoPc) has been measured using open cell photoacoustic technique. Analysis of the data shows that the effective thermal diffusivity value can be tuned by varying the relative volume fraction of the constituents. It is seen that polaron assisted heat transfer mechanism is dominant in CSA doped PANI and these composites exhibit a thermal diffusivity value which is intermediate to that of CSA doped PANI and CoPc. The results obtained are correlated with the electrical conductivity and hardness measurements carried out on the samples. |
URI: | http://dyuthi.cusat.ac.in/purl/1828 |
Files | Size |
---|---|
Thermal charact ... s composites with CoPc.pdf | (45.66Kb) |
Abstract: | An open photoacoustic cell operating in the low range of chopping frequency has been employed to evaluate the thermal diffusivity values of intrinsic InP and InP doped with S, Sn and Fe. The experimental set-up is calibrated by the evaluation of thermal diffusivity value of pure Si and GaAs. The present investigation shows that doped samples show a reduced value for thermal diffusivity compared to intrinsic sample. From the analysis of data it is also seen that nature of dopant clearly influences the thermal diffusivity value of semiconductors. The results are explained in terms of phonon assisted heat transfer mechanism in semiconductors |
URI: | http://dyuthi.cusat.ac.in/purl/1831 |
Files | Size |
---|---|
Thermal charact ... hotoacoustic technique.pdf | (64.36Kb) |
Abstract: | A laser-induced photoacoustic technique was employed to investigate thermal transport through nanocrystalline CePO4 samples prepared via the sol–gel route. Evaluation of thermal diffusivity was carried out using the one-dimensional model of Rosencwaig and Gersho for the reflection configuration of the photoacoustic method. Structural analyses of samples revealed that they are nanoporous in nature, possessing micron-sized grains. Analysis of results shows that thermal diffusivity value varies with sintering temperature. Results are explained in terms of the variation in porosity with sintering temperature and the effects of various scattering mechanisms on the propagation of phonons through the nanoporous ceramic matrix. Further analyses confirm that apart from porosity, grain boundary resistance and interface thermal resistance influence the effective value of thermal diffusivity of the samples under investigation. |
URI: | http://dyuthi.cusat.ac.in/purl/2423 |
Files | Size |
---|---|
Dyuthi-P0275.pdf | (543.3Kb) |
Abstract: | The wavelength dependence of thermal lens signal from organic dyes are studied using dual beam thermal lens technique. It is found that the profile of thermal lens spectrum widely differ from the conventional absorption spectrum in the case of rhodamine B unlike in the case of crystal violet. This is explained on the basis of varying contribution of nonradiative relaxations from the excited vibronic levels. |
URI: | http://dyuthi.cusat.ac.in/purl/2413 |
Files | Size |
---|---|
Dyuthi-CPG28.pdf | (160.1Kb) |
Abstract: | The wavelength dependence of thermal lens signal from organic dyes are studied using dual beam thermal lens technique. It is found that the profile of thermal lens spectrum widely differ from the conventional absorption spectrum in the case of rhodamine B unlike in the case of crystal violet. This is explained on the basis of varying contribution of nonradiative relaxations from the excited vibronic levels. |
URI: | http://dyuthi.cusat.ac.in/purl/2470 |
Files | Size |
---|---|
Dyuthi-P0243.pdf | (339.8Kb) |
Abstract: | The effect of pH on the fluorescence efficiency of fluorescein is evaluated using thermal lens technique. Fluorescence efficiency increases as the sample becomes more and more alkaline. But when fluorescein is mixed with rhodamine B fluorescence quenching of fluorescein takes place with the excitation of rhodamine B. The electronic energy transfer in this mixture is investigated using Optical Parametric Oscillator as the excitation source. The effect of pH on the efficiency of energy transfer in fluorescein–rhodamine B mixture is presented. |
URI: | http://dyuthi.cusat.ac.in/purl/2418 |
Files | Size |
---|---|
Dyuthi-P0265.pdf | (334.2Kb) |
Now showing items 1-18 of 18
Dyuthi Digital Repository Copyright © 2007-2011 Cochin University of Science and Technology. Items in Dyuthi are protected by copyright, with all rights reserved, unless otherwise indicated.