Now showing items 1-2 of 2
Abstract: | Metallic glass alloy Metglas 2826 MB based amorphous magnetic thin films were fabricated by the thermal evaporation technique. Transmission electron micrographs and electron diffraction pattern showed the amorphous nature of the films. Composition of the films was analyzed employing X-ray photoelectron spectroscopy and energy dispersive X-ray spectroscopy techniques. The film was integrated to a long period fibre grating. It was observed that the resonance wavelength of the fibre grating decreased with an increase in the magnetic field. Change in the resonance wavelength was minimal at higher magnetic fields. Field dependent magnetostriction values revealed the potential application of these films in magnetostrictive sensor devices. |
URI: | http://dyuthi.cusat.ac.in/purl/2840 |
Files | Size |
---|---|
Dyuthi-P00393.pdf | (556.3Kb) |
Abstract: | Thermal diffusivity of the composites of camphor sulphonic acid (CSA) doped polyaniline (PANI) and its composites with cobalt phthalocyanine (CoPc) has been measured using open cell photoacoustic technique. Analysis of the data shows that the effective thermal diffusivity value can be tuned by varying the relative volume fraction of the constituents. It is seen that polaron assisted heat transfer mechanism is dominant in CSA doped PANI and these composites exhibit a thermal diffusivity value which is intermediate to that of CSA doped PANI and CoPc. The results obtained are correlated with the electrical conductivity and hardness measurements carried out on the samples |
URI: | http://dyuthi.cusat.ac.in/purl/1827 |
Files | Size |
---|---|
Dyuthi-P00385.pdf | (45.66Kb) |
Now showing items 1-2 of 2
Dyuthi Digital Repository Copyright © 2007-2011 Cochin University of Science and Technology. Items in Dyuthi are protected by copyright, with all rights reserved, unless otherwise indicated.