| Abstract: | Rubber ferrite composites (RFC) are magnetic polymer composites and have a variety of applications as flexible magnets, pressure=photo sensors, and microwave absorbers. The mouldability into complex shapes is one of the advantages of these magnetic elastomers. They have the potential of replacing the conventional ceramic materials, due to theire flexible nature. In the present study, the incorporation of pre-characterized hexagonal ferrites, namely barium ferrite (BaFe12O19), into natural rubber matrix is carried out according to a suitable recipe for various loadings of the filler. The processability of these compounds was determined by evaluating the cure characteristics: scorch time, cure time, and minimum and maximum torque. It has been found that the addition of magnetic fillers does not affect the processability of the composites, whereas the physical properties are modified. The magnetic properties of these composites containing various loadings of the magnetic filler were also investigated. The magnetic properties of RFC can be controlled by the addition of appropriate amount of the ferrite filler. |
| Description: | International Journal of Polymeric Materials, 53:565–575, 2004 |
| URI: | http://dyuthi.cusat.ac.in/purl/4406 |
| Files | Size |
|---|---|
| Processability ... taining Barium Ferrite.pdf | (172.8Kb) |
| Abstract: | Rubber ferrite composites have the unique advantage of mouldability, which is not easily obtainable using ceramic magnetic materials. The incorporation of mixed ferrites in appropriate weight ratios into the rubber matrix not only modi es the dielectric properties of the composite but also imparts magnetic properties to it. Mixed ferrites belonging to the series of Mn(1 – x )Znx Fe2O4 have been synthesised with diVerent values of x in steps of 0·2, using conventional ceramic processing techniques. Rubber ferrite composites were prepared by the incorporation of these pre-characterised polycrystallineMn(1 – x )Znx Fe2O4 ceramics into a natural rubber matrix at diVerent loadings according to a speci c recipe. The processability of these elastomers was determined by investigating their cure characteristics. The magnetic properties of the ceramic llers as well as of the rubber ferrite composites were evaluated and the results were correlated. Studies of the magnetic properties of these rubber ferrite composites indicate that the magnetisation increases with loading of the ller without changing the coercive eld. The hardness of these composites shows a steady increase with the loading of the magnetic llers. The evaluation of hardness andmagnetic characteristics indicates that composites with optimummagnetisation and almost minimum stiVness can be achieved with a maximum loading of 120 phr of the ller at x=0·4. From the data on the magnetisation of the composites, a simple relationship connecting the magnetisation of the rubber ferrite composite and the ller was formulated. This can be used to synthesise rubber ferrite composites with predetermined magnetic properties |
| Description: | Plastics, rubber and composites,vol 31,issue 3,pp 106-113 |
| URI: | http://dyuthi.cusat.ac.in/purl/4378 |
| Files | Size |
|---|---|
| Processability, ... anganese zinc ferrites.pdf | (295.8Kb) |
| URI: | http://dyuthi.cusat.ac.in/purl/764 |
| Files | Size |
|---|---|
| ApplPhysLett_88_212103.pdf | (165.1Kb) |
| URI: | http://dyuthi.cusat.ac.in/purl/788 |
| Files | Size |
|---|---|
| Pulsed laser de ... pe _-AgGaO2 thin films.pdf | (785.6Kb) |
| Abstract: | Raman and FTIR spectra of [Cu(H2O)6](BrO3)2 and [Al(H2O)6](BrO3)3 · 3H2O are recorded and analyzed. The observed bands are assigned on the basis of BrO3 − and H2O vibrations. Additional bands obtained in the region of 3 and 1 modes in [Cu(H2O)6](BrO3)2 are due to the lifting of degeneracy of 3 modes, since the BrO3 − ion occupies a site of lower symmetry. The appearance 1 mode of BrO3 − anion at a lower wavenumber (771 cm−1) is attributed to the attachment of hydrogen to the BrO3 − anion. The presence of three inequivalent bromate groups in the [Al(H2O)6](BrO3)3 · 3H2O structure is confirmed. The lifting of degeneracy of 4 mode indicates that the symmetry of BrO3 − anion is lowered in the above crystal from C3v to C1. The appearance of additional bands in the stretching and bonding mode regions of water indicates the presence of hydrogen bonds of different strengths in both the crystals. Temperature dependent Raman spectra of single crystal [Cu(H2O)6](BrO3)2 are recorded in the range 77–523 K for various temperatures. A small structural rearrangement takes place in BrO3 − ion in the crystal at 391 K. Hydrogen bounds in the crystal are rearranging themselves leading to the loss of one water molecule at 485 K. This is preceded by the reorientation of BrO3 − ions causing a phase transition at 447 K. Changes in intensities and wavenumbers of the bands and the narrowing down of the bands at 77 K are attributed to the settling down of protons into ordered positions in the crystal |
| Description: | Spectrochimica Acta Part A 58 (2002) 899–909 |
| URI: | http://dyuthi.cusat.ac.in/purl/4554 |
| Files | Size |
|---|---|
| Raman and FTIR ... [Cu(H2O)6](BrO3)2 and.pdf | (240.6Kb) |
| Abstract: | Raman and FTIR spectra of CaFeTi(PO4)3 and CdFeTi(PO4)3 are recorded and analyzed. The observed bands are assigned in terms of vibrations of TiO6 octahedra and PO4 tetrahedra. The symmetry of TiO6 octrahedra and PO4 tetrahedra is lowered from their free ion symmetry. The presence of Fe3+ ion disrupts the Ti–O–P–O–Ti chain and leads to the distortion of TiO6 octrahedra and PO4 tetrahedra. The PO4 3 tetrahedra in both crystals are linearly distorted. The covalency bonding factor of PO4 3 polyanion of both the crystals are calculated from the Raman spectra and compared to that of other Nasicon-type systems. The numerical values of covalency bonding factor indicates that there is a reduction in redox energy and cell voltage and is attributed to strong covalency of PO4 3 polyanionin |
| Description: | Journal of Physics and Chemistry of Solids 69 (2008) 1985–1989 |
| URI: | http://dyuthi.cusat.ac.in/purl/4549 |
| Files | Size |
|---|---|
| Raman and FTIR ... eTi(PO4)3 [A ¼ Ca, Cd].pdf | (247.5Kb) |
| Abstract: | Raman and infrared spectra of Tl2NbO2PO4, Tl3NaNb4O9(PO4)2 and TlNbOP2O7 are reported. The observed bands are assigned in terms of vibrations of NbO6 octahedra and PO4 tetrahedra in the first two compounds and in terms of NbO6 octahedra and P2O7 4− anion in the third compound. The NbO6 octahedra in all the title compounds are found to be corner-shared and distorted. The higher wavenumber values of the ν1 (NbO6) mode and other stretching modes indicate that the NbO6 octahedra in them are distorted in the order TlNbOP2O7 > Tl2NbO2PO4 > Tl3NaNb4O9(PO4)2. The splitting of the ν3 (PO4) mode indicates that PO4 tetrahedra is distorted more in Tl2NbO2PO4 than in Tl3NaNb4O9(PO4)2. The symmetry of P2O7 4− anion in TlNbOP2O7 is lowered. Bands indicate that the P–O–P bridge in the above compound has a bent P–O–P bridge configuration |
| Description: | Materials Chemistry and Physics 73 (2002) 179–185 |
| URI: | http://dyuthi.cusat.ac.in/purl/4545 |
| Files | Size |
|---|---|
| Raman and infra ... O9(PO4)2 and TlNbOP2O7.pdf | (106.4Kb) |
| Abstract: | Raman spectra of the KTP single crystal are recorded in electric fields (dc and ac) applied along the polar axis c. Spectra with the laser beam focused near the cathode end, anode end and the centre of the crystal are recorded. The cathode end of the crystal develops a spot ‘grey track’ where the laser beam is focused after a lapse of 5 h from the application of a dc electric field of 38 V/cm. The spectra recorded at the cathode end after the application of field show variations in intensity of bands. A new band appears at 177 cm21. Changes in band intensities are explained on the basis of changes in polarizability of the crystal due to the movement of K1 ions along the polar axis. K1 ions accumulate at the cathode end, where the ‘Grey track’ formation occurs. The intensity enhancement observed for almost all bands in the ac field is attributed to the improvement of crystalline quality. |
| Description: | Journal of Physics and Chemistry of Solids 60 (1999) 1983–1988 |
| URI: | http://dyuthi.cusat.ac.in/purl/4548 |
| Files | Size |
|---|---|
| Raman spectra o ... in situ electric field.pdf | (348.1Kb) |
| Abstract: | A red rain phenomenon occurred in Kerala, India starting from 25th July 2001, in which the rainwater appeared coloured in various localized places that are spread over a few hundred kilometers in Kerala. Maximum cases were reported during the first 10 days and isolated cases were found to occur for about 2 months. The striking red colouration of the rainwater was found to be due to the suspension of microscopic red particles having the appearance of biological cells. These particles have no similarity with usual desert dust. An estimated minimum quantity of 50,000 kg of red particles has fallen from the sky through red rain. An analysis of this strange phenomenon further shows that the conventional atmospheric transport processes like dust storms etc. cannot explain this phenomenon. The electron microscopic study of the red particles shows fine cell structure indicat- ing their biological cell like nature. EDAX analysis shows that the major elements present in these cell like particles are carbon and oxygen. Strangely, a test for DNA using Ethidium Bromide dye fluorescence technique indicates absence of DNA in these cells. In the context of a suspected link between a meteor airburst event and the red rain, the possibility for the extraterrestrial origin of these particles from cometary fragments is discussed. |
| URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1976 |
| Files | Size |
|---|---|
| Red rain phenomenon of Kerala.pdf | (412.3Kb) |
| Abstract: | This work projects photoluminescence (PL) as an alternative technique to estimate the order of resistivity of zinc oxide (ZnO) thin films. ZnO thin films, deposited using chemical spray pyrolysis (CSP) by varying the deposition parameters like solvent, spray rate, pH of precursor, and so forth, have been used for this study. Variation in the deposition conditions has tremendous impact on the luminescence properties as well as resistivity. Two emissions could be recorded for all samples—the near band edge emission (NBE) at 380 nm and the deep level emission (DLE) at ∼500 nm which are competing in nature. It is observed that the ratio of intensities of DLE to NBE (𝐼DLE/𝐼NBE) can be reduced by controlling oxygen incorporation in the sample. 𝐼-𝑉 measurements indicate that restricting oxygen incorporation reduces resistivity considerably. Variation of 𝐼DLE/𝐼NBE and resistivity for samples prepared under different deposition conditions is similar in nature. 𝐼DLE/𝐼NBE was always less than resistivity by an order for all samples.Thus from PL measurements alone, the order of resistivity of the samples can be estimated. |
| Description: | International Journal of Photoenergy Volume 2013, Article ID 105796, 9 pages |
| URI: | http://dyuthi.cusat.ac.in/purl/4723 |
| Files | Size |
|---|---|
| Reliable and Da ... luminescence Technique.pdf | (1.904Mb) |
| Abstract: | A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability. |
| URI: | http://dyuthi.cusat.ac.in/purl/873 |
| Files | Size |
|---|---|
| Beena Mary John ... recording...,march2005.PDF | (7.043Mb) |
| Abstract: | A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is attractive on account of its reusability. |
| URI: | http://dyuthi.cusat.ac.in/purl/612 |
| Files | Size |
|---|---|
| Reusable medium MBPVA Vinyl acetate.pdf | (279.2Kb) |
| Abstract: | Effect of chlorine doping on the opto-electronic properties of β-In2S3 thin film, deposited by spray pyrolysis technique is studied for the first time. Chlorine was incorporated in the spray solution, using HCl. Pristine sample prepared using In(NO3)3 and thiourea as the precursors showed very low photosensitivity. But upon adding optimum quantity of chlorine, the photosensitivity increased by 3 orders. X-ray analysis revealed that crystallinity was also increasing up to this optimum level of Cl concentration. It was also observed that samples with high photosensitivity were having higher band gap. The present study proved that doping with chlorine was beneficial as this could result in forming crystalline and photosensitive films of indium sulfide. |
| Description: | Thin Solid Films 518 (2010) 1779–1783 |
| URI: | http://dyuthi.cusat.ac.in/purl/4711 |
| Files | Size |
|---|---|
| Role of chlorin ... of β-In2S3 thin films.pdf | (681.1Kb) |
| Abstract: | The study was carried out to understand the effect of silver-silica nanocomposite (Ag-SiO2NC) on the cell wall integrity, metabolism and genetic stability of Pseudomonas aeruginosa, a multiple drugresistant bacterium. Bacterial sensitivity towards antibiotics and Ag-SiO2NC was studied using standard disc diffusion and death rate assay, respectively. The effect of Ag-SiO2NC on cell wall integrity was monitored using SDS assay and fatty acid profile analysis while the effect on metabolism and genetic stability was assayed microscopically, using CTC viability staining and comet assay, respectively. P. aeruginosa was found to be resistant to β-lactamase, glycopeptidase, sulfonamide, quinolones, nitrofurantoin and macrolides classes of antibiotics. Complete mortality of the bacterium was achieved with 80 μgml-1 concentration of Ag-SiO2NC. The cell wall integrity reduced with increasing time and reached a plateau of 70 % in 110 min. Changes were also noticed in the proportion of fatty acids after the treatment. Inside the cytoplasm, a complete inhibition of electron transport system was achieved with 100 μgml-1 Ag-SiO2NC, followed by DNA breakage. The study thus demonstrates that Ag-SiO2NC invades the cytoplasm of the multiple drug-resistant P. aeruginosa by impinging upon the cell wall integrity and kills the cells by interfering with electron transport chain and the genetic stability |
| Description: | Letters in applied microbiology, vol.56; 2012; 57-62 |
| URI: | http://dyuthi.cusat.ac.in/purl/4420 |
| Files | Size |
|---|---|
| Sequential inte ... ic resistant bacterium.pdf | (809.8Kb) |
| Abstract: | Incorporation of silver ions into a dye-sensitized poly(vinyl alcohol)/acrylamide photopolymer is observed to give better performance compared to other metal-ion-doped photopolymer holographic recording media. Plane-wave transmission gratings were recorded in the photopolymer films using a He–Ne laser, and various holographic parameters were optimized so as to explore maximum potential of the material for various holographic applications. Silver-doped films showed good energy sensitivity, and gratings recorded in optimized film exhibited a diffraction efficiency of more than 75%. The potential of the material for holographic data storage applications is also studied using peristrophic multiplexing |
| Description: | 20 April 2009 / Vol. 48, No. 12 / APPLIED OPTICS |
| URI: | http://dyuthi.cusat.ac.in/purl/4715 |
| Files | Size |
|---|---|
| Silver-doped ph ... holographic recording.pdf | (787.8Kb) |
| Abstract: | Silver silica nanocomposites were obtained by the sol–gel technique using tetraethyl orthosilicate (TEOS) and silver nitrate (AgNO3) as precursors. The silver nitrate concentration was varied for obtaining composites with different nanoparticle sizes. The structural and microstructural properties were determined by x-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM). X-ray photoelectron spectroscopic (XPS) studies were done for determining the chemical states of silver in the silica matrix. For the lowest AgNO3 concentration, monodispersed and spherical Ag crystallites, with an average diameter of 5 nm, were obtained. Grain growth and an increase in size distribution was observed for higher concentrations. The occurrence of surface plasmon resonance (SPR) bands and their evolution in the size range 5–10 nm is studied. For decreasing nanoparticle size, a redshift and broadening of the plasmon-related absorption peak was observed. The observed redshift and broadening of the SPR band was explained using modified Mie scattering theory |
| Description: | Nanotechnology 19 (2008) 075710 (7pp) |
| URI: | http://dyuthi.cusat.ac.in/purl/4352 |
| Files | Size |
|---|---|
| Size-dependent ... silica nanocomposites.pdf | (858.7Kb) |
| Abstract: | Sol–gel glasses with Fe3O4 nanoparticles having particle sizes laying in the range 10–20 nm were encapsulated in the porous network of silica resulting in nanocomposites having both optical and magnetic properties. Spectroscopic and photoluminescence studies indicated that Fe3O4 nanocrystals are embedded in the silica matrix with no strong Si–O–Fe bonding. The composites exhibited a blue luminescence. The optical absorption edge of the composites red shifted with increasing concentration of Fe3O4 in the silica matrix. There is no obvious shift in the position of the luminescence peak with the concentration of Fe3O4 except that the intensity of the peak is decreased. The unique combinations of magnetic and optical properties are appealing for magneto–optical applications. |
| Description: | Journal of Nanoparticle Research (2008) 10:203–206 |
| URI: | http://dyuthi.cusat.ac.in/purl/4389 |
| Files | Size |
|---|---|
| Spectroscopic a ... on sol–gel glass Fe3O4.pdf | (250.1Kb) |
| Abstract: | Sol–gel glasses with Fe3O4 nanoparticles having particle sizes laying in the range 10–20 nm were encapsulated in the porous network of silica resulting in nanocomposites having both optical and magnetic properties. Spectroscopic and photoluminescence studies indicated that Fe3O4 nanocrystals are embedded in the silica matrix with no strong Si–O–Fe bonding. The composites exhibited a blue luminescence. The optical absorption edge of the composites red shifted with increasing concentration of Fe3O4 in the silica matrix. There is no obvious shift in the position of the luminescence peak with the concentration of Fe3O4 except that the intensity of the peak is decreased. The unique combinations of magnetic and optical properties are appealing for magneto–optical applications. |
| URI: | http://dyuthi.cusat.ac.in/purl/2843 |
| Files | Size |
|---|---|
| Dyuthi-P00396.pdf | (261.0Kb) |
| Abstract: | In this paper, we report the results of investigations on the potential of spray pyrolysis technique in depositing electron selective layer over larger area for the fabrication of inverted bulk-heterojunction polymer solar cells. The electron selective layer (In2S3) was deposited using spray pyrolysis technique and the linear heterojunction device thus fabricated exhibited good uniformity in photovoltaic properties throughout the area of the device. An MEH-PPV:PCBM inverted bulk-heterojunction device with In2S3 electron selective layer (active area of 3.25 3.25 cm2) was also fabricated and tested under indoor and outdoor conditions. Fromthe indoor measurements employing a tungsten halogen lamp (50mW/cm2 illumination), an opencircuit voltage of 0.41V and a short-circuit current of 5.6mA were obtained. On the other hand, the outdoor measurements under direct sunlight (74mW/cm2) yielded an open-circuit voltage of 0.46V and a short-circuit current of 9.37mA |
| Description: | Phys. Status Solidi A 209, No. 1, 199–203 (2012) |
| URI: | http://dyuthi.cusat.ac.in/purl/4721 |
| Files | Size |
|---|---|
| Spray pyrolysed ... on polymer solar cells.pdf | (429.7Kb) |
| Abstract: | Nano magnetic oxides are promising candidates for high density magnetic storage and other applications. Nonspherical mesoscopic iron oxide particles are also candidate materials for studying the shape, size and strain induced modifications of various physical properties viz. optical, magnetic and structural. Spherical and nonspherical iron oxides having an aspect ratio, ~2, are synthesized by employing starch and ethylene glycol and starch and water, respectively by a novel technique. Their optical, structural, thermal and magnetic properties are evaluated. A red shift of 0⋅24 eV is observed in the case of nonspherical particles when compared to spherical ones. The red shift is attributed to strain induced changes in internal pressure inside the elongated iron oxide particles. Pressure induced effects are due to the increased overlap of wave functions. Magnetic measurements reveal that particles are superparamagnetic. The marked increase in coercivity in the case of elongated particles is a clear evidence for shape induced anisotropy. The decreased specific saturation magnetization of the samples is explained on the basis of weight percentage of starch, a nonmagnetic component and is verified by TGA and FTIR studies. This technique can be modified for tailoring the aspect ratio and these particles are promising candidates for drug delivery and contrast enhancement agents in magnetic resonance imaging |
| Description: | Bull. Mater. Sci., Vol. 31, No. 5, October 2008, pp. 759–766 |
| URI: | http://dyuthi.cusat.ac.in/purl/4387 |
| Files | Size |
|---|---|
| Strain induced ... edby a novel technique.pdf | (1.595Mb) |