Abstract: | Two stage processes consisting of precursor preparation by thermal evaporation followed by chalcogenisation in the required atmosphere is found to be a feasible technique for the PV materials such as n-Beta In2S3, p-CulnSe2, p-CulnS2 and p-CuIn(Sel_xSx)2. The growth parameters such as chalcogenisation temperature and duration of chalcogenisation etc have been optimised in the present study.Single phase Beta-In2S3 thin films can be obtained by sulfurising the indium films above 300°C for 45 minutes. Low sulfurisation temperatures required prolonged annealing after the sulfurisation to obtain single phase Beta-1n2S3, which resulted in high material loss. The maximum band gap of 2.58 eV was obtained for the nearly stoichiometric Beta-In2S3 film which was sulfurised at 350°C. This wider band gap, n type Beta-In2S3 can be used as an alternative to toxic CdS as window layer in photovoltaics .The systematic study on the structural optical and electrical properties of CuInSe2 films by varying the process parameters such as the duration of selenization and the selenization temperature led to the conclusion that for the growth of single-phase CuInSe2, the optimum selenization temperature is 350°C and duration is 3 hours. The presence of some binary phases in films for shorter selenization period and lower selenization temperature may be due to the incomplete reaction and indium loss. Optical band gap energy of 1.05 eV obtained for the films under the optimum condition.In order to obtain a closer match to the solar spectrum it is desirable to increase the band gap of the CulnSe2 by a few meV . Further research works were carried out to produce graded band gap CuIn(Se,S)2 absorber films by incorporation of sulfur into CuInSe2. It was observed that when the CulnSe2 prepared by two stage process were post annealed in sulfur atmosphere, the sulfur may be occupying the interstitial positions or forming a CuInS2 phase along with CuInSe2 phase. The sulfur treatment during the selenization process OfCu11 ln9 precursors resulted in Culn (Se,S)2 thin films. A band gap of 1.38 eV was obtained for the CuIn(Se,S)2.The optimised thin films n-beta 1n2S3, p-CulnSe2 and p-Culn(Sel-xSx)2 can be used for fabrication of polycrystalline solar cells. |
Description: | Department of Physics, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2520 |
Files | Size |
---|---|
Dyuthi-T0679.pdf | (6.437Mb) |
Abstract: | Mesoporous materials are of great interest to the materials community because of their potential applications for catalysis,separation of large molecules,medical implants,semiconductors,magnetoelectric devices.The thesis entitled 'Ordered Mesoporous Silica as supports for immobilization of Biocatalyst' presents how the pore size can be tuned without the loss in ordered structure for the entrapment of an industially important biocatalyst-amylase.Immobilization of enzymes on ordered mesoporous material has triggered new ooportunities for stabilizing enzymes with improved intrinsic and operational stabilities. |
Description: | Department of Applied Chemistry, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2864 |
Files | Size |
---|---|
Dyuthi-T0861.pdf | (4.497Mb) |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1978 |
Files | Size |
---|---|
Dyuthi-T0437.pdf | (6.330Mb) |
Description: | Department of Applied Chemistry, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2756 |
Files | Size |
---|---|
Dyuthi-T0781.pdf | (4.617Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/5219 |
Files | Size |
---|---|
Dyuthi T-2254.pdf | (6.371Mb) |
Abstract: | Catalysis is a technologically important field which determines the quality of life in future. Catalyst research in pharmaceutical industry,fine chemical synthesis and emission control demands supported catalysts in bulk quantities.In the present work it was observed that clay supported catalysts mentioned in various chapters could also be used for the synthesis of similar molecules. The K10Ti catalyst can be used for the synthesis similar substituted imidazole derivatives under solvent free conditions and synthetically important Mannich bases of substrates containing various substitutes.Al-pillared saponite can be used for acetalation of other polyhydroxy compounds like glycerol,mannitol etc.Cu-Pd KSF catalyst has found application in C-C bond forming reactions which can be applied to other reactions and similar methods can be adopted for the synthesis of other catalyst by changing the transition metals. Montmorillonite K10 catalysed synthesis of triarylpyridines can be extended to the synthesis tetrasubstuted pyroles.K10Ti can also be utilized for the synthesis of similar heterocycles. |
Description: | Dept.of Applied Chemistry,Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2934 |
Files | Size |
---|---|
Dyuthi-T0925.pdf | (2.726Mb) |
Abstract: | The reactions involving fulvenes and its derivatives have received a great deal of attention over the years in synthetic organic chemistry. Functionalizations of fulvenes provide versatile and powerful approaches to various polycyclic systems and natural products. They serve as versatile intermediates in the construction of various ring systems through inter- as well as intramolecular cycloadditions. Compared to the rich literature on the cycloaddition reactions of pentafulvenes, much less attention has been paid to the synthetic utilization of their cycloadducts. Tactical manipulations on the chosen adduct offer the prospects for designing a variety of useful molecular skeletons. Addition of heterodienophiles to fulvenes offers an efficient strategy towards the synthesis of azabicyclic olefins. However, there have been no serious attempts to study the synthetic utility of these substrates. In this context and with the intention of utilizing pentafulvenes towards synthetically important molecules, author decided to explore the reactivity of pentafulvene derived azabicyclic olefins. Our attention was focused on the synthetic potential associated with the ring opening of fulvene derived bicyclic hydrazines under palladium catalysis. It was envisioned that the desymmetrization of these adducts using various soft nucleophiles will provide a novel access to synthetically and biologically important alkylidene cyclopentenes. The investigations along this line form the focal theme of this thesis entitled “PALLADIUM CATALYZED CARBONCARBON/ CARBON-HETEROATOM BOND FORMATION REACTIONS UTILIZING PENTAFULVENE DERIVED BICYCLIC HYDRAZINES |
Description: | Organic Chemistry Section, National Institute for Interdisciplinary Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/3536 |
Files | Size |
---|---|
Dyuthi-T1505.pdf | (2.395Mb) |
Abstract: | The discovery of the Photoacoustic (PA) effect was a remarkable achievement and was relegated to the scientific footnotes of the nineteenth century. However, after the advent of lasers and sophisticated electronics this effect was rediscovered and it has established itself as an important research and analytical tool in numerous areas, including physics, chemistry, biology and medicine. Quite recently, this phenomenon has made its impact in the field of laser technology for applications such as the developments of highly efficient active media for lasers, high quality optics and sensitive laser power monitoring devices. This thesis presents the work carried out by the author in this field during the past few years at the Department of Physics in Cochin University of Science and Technology. The studies discussed here are mostly based on the development of a sensitive PA laser power meter and its various applications using different laser systems available in the laboratory. This includes the development of a current regulated CW C0 laser and its application in material processing. The thesis contains seven chapters which by and large are self contained with separate abstracts and references. The first chapter which is divided into two parts presents an introduction to the PA effect and its present status. Part A reviews the basic theory of laser and gives a sum mary of various lasers and their applications. Part B presents a brief description of PA effect and its suitability as a spectroscopic tool followed by its applications to various branches of science and technology. |
Description: | Department of Physics, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/3388 |
Files | Size |
---|---|
Dyuthi-T1365.pdf | (4.026Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/1705 |
Files | Size |
---|---|
Dyuthi-T0209.pdf | (5.253Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/1700 |
Files | Size |
---|---|
Dyuthi-T0208.pdf | (5.832Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/1118 |
Files | Size |
---|---|
Madhusoodanan K N 1989.pdf | (2.690Mb) |
Abstract: | This thesis work has mainly concentrated on the investigation of the ,optical and thermal properties of binary semiconducting chalcogenide glasses belonging to the AivB¥5x and AZBXEX families. The technique used for these studies is a relatively new one namely, the photoacoustic (PA) technique. This technique is based on the detection of acoustic signal produced in an enclosed volume when the sample is irradiated by an intensity modulated radiation. The signal produced depends upon the optical properties of the sample, and the thermal properties of the sample, backing material and the surrounding gas. For the present studies an efficient signal beam gas-microphone PA spectrometer, consisting of a high power Xenon lamp, monochromator, light beam chopper, PA cell with microphone and lock-in amplifier, has been set up. Two PA cells have been fabricated: one for room temperature measurements and another for measurements at high temperatures. With the high temperature PA cell measurements can be taken upto 250°C. Provisions are incorporated. in both the cells to change the volume and to use different backing materials for the sample. The cells have been calibrated by measuring the frequency response of the cells using carbon black as the sample |
Description: | Department of physics, Cochin University of Science And Technology |
URI: | http://dyuthi.cusat.ac.in/purl/3335 |
Files | Size |
---|---|
Dyuthi-T1299.pdf | (2.637Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/1112 |
Files | Size |
---|---|
Satheesh Kumar M K 1988.pdf | (1.186Mb) |
Description: | Department of Applied Chemistry, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1943 |
Files | Size |
---|---|
Dyuthi-T0438.pdf | (3.661Mb) |
Abstract: | Photoconductivity (PC) processes may be the most suitable technique for obtaining information about the states in the gap. It finds applications in photovoItaics, photo detection and radiation measurements. The main task in the area of photovoltaics, is to increase the efficiency of the device and also to develop new materials with good optoelectronic properties useful for energy conversion, keeping the idea of cost effectiveness. Photoconduction includes generation and recombination of carriers and their transport to the electrodes. So thermal relaxation process, charge carrier statistics, effects of electrodes and several mechanisms of recombination are involved in photoconductivity.A major effect of trapping is to make the experimentally observed decay time of photocurrent, longer than carrier lifetime. If no trapping centers are present, then observed photocurrent will decay in the same way as the density of free carriers and the observed decay time will be equal to carrier lifetime. If the density of free carriers is much less than density of trapped carriers, the entire decay of photocurrent is effectively dominated by the rate of trap emptying rather than by the rate of recombination.In the present study, the decay time of carriers was measured using photoconductive decay (PCD) technique. For the measurements, the film was loaded in a liquid Helium cryostat and the temperature was controlled using Lakshore Auto tuning temperature controller (Model 321). White light was used to illuminate the required area of the sample. Heat radiation from the light source was avoided by passing the light beam through a water filter. The decay current. after switching off the illumination. was measured using a Kiethely 2000 multi meter. Sets of PCD measurements were taken varying sample temperature, sample preparation temperature, thickness of the film, partial pressure of Oxygen and concentration of a particular element in a compound. Decay times were calculated using the rate window technique, which is a decay sampling technique particularly suited to computerized analysis. For PCD curves with two well-defined regions, two windows were chosen, one at the fast decay region and the other at the slow decay region. The curves in a particular window were exponentially fitted using Microsoft Excel 2000 programme. These decay times were plotted against sample temperature and sample preparation temperature to study the effect of various defects in the film. These studies were done in order to optimize conditions of preparation technique so as to get good photosensitive samples. useful for photovoltaic applications.Materials selected for the study were CdS, In2Se3, CuIn2Se3 and CuInS2• Photoconductivity studies done on these samples are organised in six chapters including introduction and conclusion. |
Description: | Department of Physics, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2324 |
Files | Size |
---|---|
Dyuthi-T0598.pdf | (5.320Mb) |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1979 |
Files | Size |
---|---|
Dyuthi-T0439.pdf | (8.882Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/5222 |
Files | Size |
---|---|
Dyuthi T-2257.pdf | (81.59Mb) |
Abstract: | Determining the morphological parameters that describe galaxies has always been a challenging task. The studies on the correlations between different photometric as well as spectroscopic parameters of the galaxies help in understanding their structure, properties of the stars and gas which constitute the galaxy, the various physical and chemical processes which determine the properties, and galaxy formation and evolution. In the last few decades, the advent of Charge Coupled Devices (CCDs) and near infrared arrays ha\·e provided quick and reliable digitized data acquisition, in the optical and near infrared bands. This has provided an avalanche of data, which can be processed using sophisticated image analysis techniques to obtain information about the morphology of galaxies. The photometric analysis performed in this thesis involve the extraction of structural parameters of early type gala.xies imaged in the near infrared K (2.2ttm) band, obtaining correlations between these, parameters and using them to constrain the large scale properties of galaxi,~s. |
Description: | Department of Physics, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/3816 |
Files | Size |
---|---|
Dyuthi-T1747.pdf | (2.706Mb) |
Abstract: | This thesis presents in detail. the theoretical developments and calculations which are used for the simultaneous determination of thermal parameters, namely thermal diffusivity (a). thermal effusivity (e), thermal conductivity (K) and heat capacity (cr ) employing photopyroelectric technique. In our calculations. we have assumed that the pyroelectric detector is supported on a copper backing. so that there will be sufficient heat exchange between the heated pyroelectric detector and the backing so that the signal fluctuations are reduced to a minimum. Since the PPE signal depends on the properties of the detector that are also temperature dependent. a careful temperature calibration of the system need to be carried out. APPE cell has been fabricated for the measurements that can be used to measure the thermal properties of solid samples from ~ 90 K to ~ 350 K. The cell has been calibrated using standard samples and the accuracy of the technique is found to be of the order of± 1%.In this thesis, we have taken up work n photopyroelectric investigation of thermal parameters of ferroelectric crystals such as Glycine phosphite (NH3CH2COOH3P03), Triglycine sulfate and Thiourea as well as mixed valence perovskites samples such as Lead doped Lanthanum Manganate (Lal_xPb~Mn03) Calcium doped (Lal_xCaxMnOJ) and Nickel doped Lanthanum Stroncium Cobaltate (Lao~Sro5Ni,Col_x03).The three ferroelectric crystals are prepared by the slow evaporation technique and the mixed valence perovskites by solid state reaction technique.Mixed valence perovskites, with the general formula RI_xA~Mn03 (R = La. Nd or Pr and A = Ba, Ca, Sr or Pb) have been materials of intense experimental and theoretical studies over the past few years. These materials show . colossal magneloresis/ance' (CMR) in samples with 0.2 < x < 0.5 in such a doping region, resistivity exhibits a peak at T = T p' the metal - insulator transition temperature. The system exhibits metallic characteristics with d %T > Oabove Tp (wherep is the resistivity) and insulating characteristics with d % T < 0 above T p. Despite intensive investigations on the CMR phenomena and associated electrical properties. not much work has been done on the variation of thermal properties of these samples. We have been quite successful in finding out the nature of anomaly associated with thermal properties when the sample undergoes M-I transition.The ferroelectric crystal showing para-ferroelectric phase transitions - Glycine phosphite. Thiourea and Triglycine sulfate - are studied in detail in order to see how well the PPE technique enables one to measure the thermal parameters during phase transitions. It is seen that the phase transition gets clearly reflected in the variation of thermal parameters. The anisotropy in thermal transport along different crystallographic directions are explained in terms of the elastic anisotropy and lattice contribution to the thermal conductivity. Interesting new results have been obtained on the above samples and are presented in three different chapters of the thesis.In summary. we have carried investigations of the variations of the thermal parameters during phase transitions employing photopyroelectric technique. The results obtained on different systems are important not only in understanding the physics behind the transitions but also in establishing the potentiality of the PPE tool. The full potential of PPE technique for the investigation of optical and thermal properties of materials still remains to be taken advantage of by workers in this field. |
Description: | Department of Instrumentation, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2484 |
Files | Size |
---|---|
Dyuthi-T0667.pdf | (7.710Mb) |
Abstract: | Material synthesizing and characterization has been one of the major areas of scientific research for the past few decades. Various techniques have been suggested for the preparation and characterization of thin films and bulk samples according to the industrial and scientific applications. Material characterization implies the determination of the electrical, magnetic, optical or thermal properties of the material under study. Though it is possible to study all these properties of a material, we concentrate on the thermal and optical properties of certain polymers. The thermal properties are detennined using photothermal beam deflection technique and the optical properties are obtained from various spectroscopic analyses. In addition, thermal properties of a class of semiconducting compounds, copper delafossites, arc determined by photoacoustic technique.Photothermal technique is one of the most powerful tools for non-destructive characterization of materials. This forms a broad class of technique, which includes laser calorimetry, pyroelectric technique, photoacollstics, photothermal radiometric technique, photothermal beam deflection technique etc. However, the choice of a suitable technique depends upon the nature of sample and its environment, purpose of measurement, nature of light source used etc. The polynler samples under the present investigation are thermally thin and optically transparent at the excitation (pump beam) wavelength. Photothermal beam deflection technique is advantageous in that it can be used for the detennination of thermal diffusivity of samples irrespective of them being thermally thick or thennally thin and optically opaque or optically transparent. Hence of all the abovementioned techniques, photothemlal beam deflection technique is employed for the successful determination of thermal diffusivity of these polymer samples. However, the semi conducting samples studied are themlally thick and optically opaque and therefore, a much simpler photoacoustic technique is used for the thermal characterization.The production of polymer thin film samples has gained considerable attention for the past few years. Different techniques like plasma polymerization, electron bombardment, ultra violet irradiation and thermal evaporation can be used for the preparation of polymer thin films from their respective monomers. Among these, plasma polymerization or glow discharge polymerization has been widely lIsed for polymer thin fi Im preparation. At the earlier stages of the discovery, the plasma polymerization technique was not treated as a standard method for preparation of polymers. This method gained importance only when they were used to make special coatings on metals and began to be recognized as a technique for synthesizing polymers. Thc well-recognized concept of conventional polymerization is based on molecular processcs by which thc size of the molecule increases and rearrangemcnt of atoms within a molecule seldom occurs. However, polymer formation in plasma is recognized as an atomic process in contrast to the above molecular process. These films are pinhole free, highly branched and cross linked, heat resistant, exceptionally dielectric etc. The optical properties like the direct and indirect bandgaps, refractive indices etc of certain plasma polymerized thin films prepared are determined from the UV -VIS-NIR absorption and transmission spectra. The possible linkage in the formation of the polymers is suggested by comparing the FTIR spectra of the monomer and the polymer. The thermal diffusivity has been measured using the photothermal beam deflection technique as stated earlier. This technique measures the refractive index gradient established in the sample surface and in the adjacent coupling medium, by passing another optical beam (probe beam) through this region and hence the name probe beam deflection. The deflection is detected using a position sensitive detector and its output is fed to a lock-in-amplifIer from which the amplitude and phase of the deflection can be directly obtained. The amplitude and phase of the deflection signal is suitably analyzed for determining the thermal diffusivity.Another class of compounds under the present investigation is copper delafossites. These samples in the form of pellets are thermally thick and optically opaque. Thermal diffusivity of such semiconductors is investigated using the photoacoustic technique, which measures the pressure change using an elcctret microphone. The output of the microphone is fed to a lock-in-amplificr to obtain the amplitude and phase from which the thermal properties are obtained. The variation in thermal diffusivity with composition is studied. |
Description: | Department of Physics, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2343 |
Files | Size |
---|---|
Dyuthi-T0616.pdf | (6.243Mb) |