Poly(6-tert-butyl-3,4-dihydro-2H-1,3-benzoxazine) was synthesized by
thermally activated cationic ring opening polymerization. The structure of the
polymer was confirmed by spectral and thermal studies. The highest occupied
molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) were
estimated using cyclic voltammetry and optical absorption. Modulated photocurrent
measurement technique was employed to study the spectral and field dependence of
photocurrent. Photocurrent of the order of 1.5 micro A/m2 was obtained for polymer at a
biasing electric field of 40 V/mico m.
A new photopolymerizable recording media is introduced based on poly
(vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed
that this MBPVA/VAc system can be reused a number of times without
significant decrease in diffraction . The PVA-VAc ratio was optimized
at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye
concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is
attractive on account of its reusability.
A new photopolymerizable recording media is introduced based on poly
(vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed
that this MBPVA/VAc system can be reused a number of times without
significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized
at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye
concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is
attractive on account of its reusability.
This manuscript describes the first example of silver ion complex of a dendritic tetranitrile ligand catalyzed
one-pot three component Mannich reaction and 1,5-benzodiazepine synthesis. The catalyst can be separated from the
products by a change in the solvent. The catalyst is reusable.