Abstract: | Cure characteristics of short polyester fiber-polyurethane composites with respect to different bonding agents (MD resins) based on 4, 4' diphenylmethanediisocyanate (MDI) and various diols like propyleneglycol (PG), polypropyleneglycol (PPG) and glycerol (GL) were studied. Tmax. - Tmin. of composites having MD resin were found to be higher than the composite without MD resin. Minimum torque and Tmax. - Tmin., scorch time and optimum cure time were increased with the increase of MDI equivalence. Optimum ratio of MDI / -of in the resin was found to be within the range of 1-1.5. It was observed from the cure characteristics that for getting better adhesion between short polyester fiber and the polyurethane matrix the best choice of MD resin was one based on MDI and 1:1 equivalent mixture of polypropyleneglycol and glycerol. |
URI: | http://dyuthi.cusat.ac.in/purl/902 |
Files | Size |
---|---|
Suhara, F S K N ... polyester..............PDF | (7.438Mb) |
Abstract: | Microcellular (MC) soles based on polybutadiene (BR) and low-density polyethylene (LDPE) blends for low-temperature applications were developed. A part of BR in BR-LDPE blend was replaced by natural rubber (NR) for property improvement. The BR-NR-LDPE blend-based MC sole shows good technical properties. Sulphur curing and DCP curing were tried in BR-LDPE and NR-BR-LDPE blends. Study shows that sulphur-cured MC sheets possess better technical properties than DCPcured MC sheets. 90/10 BR-LDPE and 60/30/10 BR-NR-LDPE blend combinations are found to be suitable for low-temperature applications. |
URI: | http://dyuthi.cusat.ac.in/purl/866 |
Files | Size |
---|---|
R Srilathakutty ... polybutadine..,Feb1999.PDF | (3.360Mb) |
Abstract: | We describe the synthesis of diblock and triblock copolymers by sequential atom transfer radical polymerization of styrene and acetoxymethylstyrene. Contrary to the usual block copolymerization involving isolation of the macroinitiator, a convenient one-pot procedure is developed. This is possible because of the preferential polymerization of acetoxymethylstyrene, even in the presence of residual styrene, as inferred from characterization of the intermediate polystyrenes and the block copolymers by size exclusion chromatography, 1H NMR, Fourier transform infrared spectroscopy, differential scanning calorimetry, and GPEC techniques. The latent acetoxy functionalities in these block copolymers are shown to be easily unmasked to OOH and OBr functionalities, with the potential for block ionomers and dense graft architectures. |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1995 |
Files | Size |
---|---|
Diblock and triblock....pdf | (136.8Kb) |
Abstract: | In this article, we report the preparation of conducting natural rubber (NR) with polyaniline (Pani). NR was made into a conductive material by the compounding of NR with Pani in powder form. NR latex was made into a conductive material by the in situ polymerization of aniline in the presence of NR latex. Different compositions of Pani- NR semi-interpenetrating networks were prepared, and the dielectric properties of all of the samples were determined in microwave frequencies. The cavity perturbation techpique was used for this study. A HP8510 vector network analyzer with a rectangular cavity resonator was used for this study. S bands 2-4 GHz in frequency were used. Thermal studies were also carried out with thermogravimetric analysis and differential scanning calorimetry. |
URI: | http://dyuthi.cusat.ac.in/purl/799 |
Files | Size |
---|---|
Honey John and ... ic behavior...,Jun2006.PDF | (3.772Mb) |
Abstract: | The dynamic mechanical properties such as storage modulus, loss modulus and damping properties of blends of nylon copolymer (PA6,66) with ethylene propylene diene (EPDM) rubber was investigated with special reference to the effect of blend ratio and compatibilisation over a temperature range –100°C to 150°C at different frequencies. The effect of change in the composition of the polymer blends on tanδ was studied to understand the extent of polymer miscibility and damping characteristics. The loss tangent curve of the blends exhibited two transition peaks, corresponding to the glass transition temperature (Tg) of individual components indicating incompatibility of the blend systems. The morphology of the blends has been examined by using scanning electron microscopy. The Arrhenius relationship was used to calculate the activation energy for the glass transition of the blends. Finally, attempts have been made to compare the experimental data with theoretical models. |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1998 |
Files | Size |
---|---|
Dynamic mechanical analysis...pdf | (518.2Kb) |
Abstract: | Compounding of styrene-butadiene copolymer/polybutadiene , natural rubber/ ethylene-propylene-diene terpolymer and natural rubber/butadiene-acrylonitrile copolymer blends was done in three different ways and their curing behaviour and the tensile properties of the es are compared. |
URI: | http://dyuthi.cusat.ac.in/purl/841 |
Files | Size |
---|---|
Rani Joseph and ... of blending..,Oct1987.PDF | (4.364Mb) |
Abstract: | Isora fibre-reinforced natural rubber (NR) composites were cured at 80, 100, 120 and 150°C using a low temperature curing accelerator system. Composites were also prepared using a conventional accelerator system and cured at 150°C. The swelling behavior of these composites at varying fibre loadings was studied in toluene and hexane. Results show that the uptake of solvent and volume fraction of rubber due to swelling was lower for the low temperature cured vulcanizates which is an indication of the better fibre/rubber adhesion. The uptake of aromatic solvent was higher than that of aliphatic solvent, for all the composites. As the fibre content increased, the solvent uptake decreased, due to the superior solvent resistance of the fibre and good fibre-rubber interactions. The bonding agent improved the swelling resistance of the composites due to the strong interfacial adhesion. Due to the improved adhesion between the fibre and rubber, the ratio of the change in volume fraction of rubber due to swelling to the volume fraction of rubber in the dry sample (V,) was found to decrease in the presence of bonding agent. At a fixed fibre loading, the alkali treated fibre composite showed a lower percentage swelling than untreated one for both systems showing superior rubber-fibre interactions. |
URI: | http://dyuthi.cusat.ac.in/purl/806 |
Files | Size |
---|---|
Lovely Mathew a ... of curing...,July2005.PDF | (6.828Mb) |
Abstract: | In this paper we report the preparation and dielectric properties of poly o-toluidine:poly vinyl chloride composites in pellet and film forms. The composites were prepared using ammonium persulfate initiator and HCl dopant. The characterization is done by TGA and DSC. The dielectric properties including dielectric loss, conductivity, dielectric constant, dielectric heating coefficient, absorption coefficient, and penetration depth were studied in the microwave field. An HP8510 vector network analyzer with rectangular cavity resonator was used for the study. Sbands (2-4 GHz), C band (5-8 GHz), and X band (8-12 GHz) frequencies were used in the microwave field. Comparisons between the pellet and film forms of composites were also included. The result shows that the dielectric properties in the microwave field are dependent on the frequency and on the method of preparation. |
URI: | http://dyuthi.cusat.ac.in/purl/800 |
Files | Size |
---|---|
Honey John and ... ferent forms...Feb2006.PDF | (6.158Mb) |
Abstract: | The latex industry has expanded over the years to meet the world demands for gloves, condoms, latex thread etc. Because of the strict specifications for the products and the unstable nature of the latex, as high as 15%, of the final latex products are rejected. Since waste latex rubber (WLR) represents a source of high quality rubber hydrocarbon, it is a potential candidate for generating reclaimed rubber of superior quality. Two types of WLR with different amounts of polysulfidic bridges are used in these experiments, which are reclaimed with variation of the concentration of the reclaiming agents, the reclamation temperature and time, Di phenyldisultide, 2-aminophenyldisulfide and 2,2'-dibenzamidodiphenyldisulfide (DBADPDS) are used as reclaiming agents, and the effect of diphenyldisulfides (DPDS) with different substituents, on the reclamation efficiency of WLR is investigated. A kinetic study of the reclamation reaction with the three reclaiming agents is done. The reaction rates and activation energies are calculated and compared with literature values. The comparative study of the three different reclaiming agents shows that (DBADPDS) is able to break the crosslinks at temperature levels 20'C below the temperature levels normally used with DPDS. Another advantage of this reclaiming agent is the reduced smell during the reclamation process and of the final reclaims, one of the most important shortcomings of other disulfides used for this purpose. |
URI: | http://dyuthi.cusat.ac.in/purl/822 |
Files | Size |
---|---|
V V Rajan,Effec ... isulfides....Sept.2006.PDF | (12.78Mb) |
Abstract: | ABSTRACT: Polyaniline was synthesized by using ammonium persulfate initiator in the presence of 1M HC1. It was dried under different drying conditions like room temperature drying (for 48 h), oven drying (at 50-60°C for 8 h under a vacuum), and vacuum drying (at room temperature for 16 h). The conductivities of these samples were measured at microwave frequencies. These samples were also pelletized and the measurements were repeated. The cavity perturbation technique was used for the study. |
URI: | http://dyuthi.cusat.ac.in/purl/852 |
Files | Size |
---|---|
Dyuthi-P00420.pdf | (241.2Kb) |
Abstract: | Selected grades of low density polyethylene (LDPE) polystyrene (PS) were extruded in a laboratory extruder by varying the feeding rate at different revolutions per minute and temperatures. The mechanical properties of the extruded plastic sheets were determined. LDPE shows a marked variation in mechanical properties with feeding rate while PS shows a marginal change in mechanical properties with feeding rate. However, for both plastics there is a particular feeding rate in the starved region which results in maximum mechanical properties. |
URI: | http://dyuthi.cusat.ac.in/purl/863 |
Files | Size |
---|---|
P J Joseph Fran ... of feeding..,July1997.PDF | (8.184Mb) |
Abstract: | The effect of various processing parameters, such as nip gap, friction ratio and roll temperature, on the tensile properties of short Kevlar aramid fibre-thermoplastic polyurethane composite has been investigated and the tensile and tear fracture surfaces have been characterised using a scanning electron microscope. A nip gap of 0.45 mm, a friction ratio of 1.15 and a roll temperature of 62°C was found to give optimum mechanical properties. Scanning electron microscopy study revealed a higher extent of fibre orientation in the milling direction in the above condition. |
URI: | http://dyuthi.cusat.ac.in/purl/881 |
Files | Size |
---|---|
Golok , B, S K ... rs on the .............PDF | (5.366Mb) |
Abstract: | Chloroprene rubber was blended with whole tire reclaimed rubber (WTR) in presence of different levels of a coupling agent Si69 [bis- (3-(triethoxysilyl)propy1)tetrasuIfide] and the cure characteristics and mechanical properties were studied. The rate and state of cure were also affected by the coupling agent. While the cure time was increased, the cure rate and scorch time were decreased with increasing silane content. Tensile strength, tear strength, and abrasion resistance were improved in the presence of coupling agent. Compression set and resilience were adversely affected in presence of silane-coupling agent.Aging studies showed that the blends containing the coupling agent were inferior to the unmodified blends. |
URI: | http://dyuthi.cusat.ac.in/purl/888 |
Files | Size |
---|---|
NELSON P A, S. ... ILANE CUPLING AGENT....PDF | (5.467Mb) |
Abstract: | Blends of nitrile rubber and reclaimed rubber containing different levels of a coupling agent, Si 69 (bis(3- triethoxysilyl propyl)(tetrasulphide) were prepared and the cure characteristic's and mechanical properties were studied. Optimum loading of Si-69 was found to be a function of blend ratio. 3 phi- of Si 69 in a 70:30. Blend was found to be the optimum combination with respect to the mechanical properties. The rate and state of cure were also affected bv the conp/ing agent. Tensile strength, tear strength and abrasion resistance were improved in the presence of coupling agent. While the state of cure improved, the cure rate and scorch time decreased with increasing silane content. Ageing studies showed that the blends containing the coupling agent were inferior to the unmodified blends. |
URI: | http://dyuthi.cusat.ac.in/purl/887 |
Files | Size |
---|---|
NELSON P A, S. ... agents................PDF | (9.516Mb) |
Abstract: | Prevulcanized natural rubber latex was prepared by the heating of the latex compound at 55°C for different periods of time (2, 4, 6, 8, and 10 h). The changes in the colloidal stability and physical properties were evaluated during the course of prevulcanization. The prevulcanized latex compounds were stored for 300 days, and the properties were monitored at different storage intervals (0, 20, 40, 60, 120, 180, 240, and 300 days). During prevulcanization, the mechanical stability time increased, and the viscosity remained almost constant. The tensile strength increased during storage for a period of 20 days. The degree of crosslinking, modulus, elongation at break, and chloroform number were varied with the time of storage. |
URI: | http://dyuthi.cusat.ac.in/purl/803 |
Files | Size |
---|---|
K K Sasidharan ... fect of the...,Dec2004.PDF | (5.168Mb) |
Abstract: | The cure characteristics and mechanical properties of short nylon fiber- styrene /whole tyre reclaim (SBR/WTR) composites with and without an interfacial bonding agent based on 4,4 diphenyl methane diisocyanate and polyethylene glycol (MDI/PEG) have been studied. An 80:40 blend of SBR/ WTR reinforced with 20 phr of short nylon fiber has been selected and the MDI/ PEG ratio has been changed from 0.67:1 to 2:1. The minimum and maximum torques increased with isocyanate concentration. The scorch time and cure time showed an initial reduction. The cure rate showed an initial improvement. Tensile strength, tear strength and abrasion resistance increased with MDI/PEG ratio, these values were higher in longitudinal direction. Resilience and compression set increased with isocyanate concentration. |
URI: | http://dyuthi.cusat.ac.in/purl/898 |
Files | Size |
---|---|
sreeja T D, S. ... e cure.................PDF | (7.222Mb) |
Abstract: | Blends of chlorobutyl rubber (CIIR) with two grades of ethylene-propylene diene monomer rubber (EPDM) were prepared and the effect of blend ratio on the cure characteristics, hot air ageing resistance, steam ageing resistance, and mechanical properties were evaluated. The blend of CIIR with EPDM grade 301 T showed additive behavior and the blend with the other grade of EPDM (NDR 4640) showed synergistic behavior. |
URI: | http://dyuthi.cusat.ac.in/purl/815 |
Files | Size |
---|---|
Sunil Jose and Rani Joseph,2008.PDF | (8.594Mb) |
Abstract: | Unsaturated polyester resins (UPRs) are used widely in the fiber-reinforced plastics (FRPs) industry. These resins have the disadvantages of brittleness and poor resistance to crack propagation. In this study, hybrid polymer networks (HPNs) based on UPR and epoxidized phenolic novolacs (EPNs) were prepared by reactive blending. A HPN is composed of a backbone polymer containing two types of reactive groups that can take part in crosslinking reactions via different mechanisms. EPNs were prepared by glycidylation of novolacs using epichlorohydrin. The novolacs had varying phenol: formaldehyde ratios. Blends of unsaturated polyester with EPN were then prepared. The physical properties of the cured blends were compared with those of the control resin. EPN shows good miscibility and compatibility with the resin and improves the toughness and impact resistance substantially. Considerable enhancement of tensile strength is also noticed at about 5% by weight of epoxidized novolac resin. TGA, DMA, and DSC were used to study the thermal properties of the toughened resin and the fracture behavior was studied using SEM. The blends are also found to have better thermal stability. Blending with EPN can be a useful and cost-effective technique for modification of UPR |
Description: | Journal of Applied Polymer Science, Vol. 100, 457–465 (2006) |
URI: | http://dyuthi.cusat.ac.in/purl/4690 |
Files | Size |
---|---|
Epoxidized Phen ... urated Polyester Resin.pdf | (237.1Kb) |
Abstract: | Hybrid polymer networks (HPNs) based on unsaturated polyester resin (UPR) and epoxy resins were synthesized by reactive blending. The epoxy resins used were epoxidised phenolic novolac (EPN), epoxidised cresol novolac (ECN) and diglycidyl ether of bisphenol A (DGEBA). Epoxy novolacs were prepared by glycidylation of the novolacs using epichlorohydrin. The physical, mechanical, and thermal properties of the cured blends were compared with those of the control resin. Epoxy resins show good miscibility and compatibility with the UPR resin on blending and the co-cured resin showed substantial improvement in the toughness and impact resistance. Considerable enhancement of tensile strength and toughness are noticed at very low loading of EPN. Thermogravimetric analysis (TGA), dynamic mechanical analysis (DMA) and diVerential scanning calorimetry (DSC) were employed to study the thermal properties of the toughened resin. The EPN/ UPR blends showed substantial improvement in thermal stability as evident from TGA and damping data. The fracture behaviour was corroborated by scanning electron microscopy (SEM). The performance of EPN is found to be superior to other epoxy resins |
Description: | European Polymer Journal 43 (2007) 1460–1469 |
URI: | http://dyuthi.cusat.ac.in/purl/4687 |
Files | Size |
---|---|
Epoxy-modiWed, ... yester hybrid networks.pdf | (714.5Kb) |
Abstract: | Ash-based polymer composites are assuming increasing importance because of the pollutant potential, fine particle size, and low price of ash. Fly ash and rice husk ash are two prominent ash materials on which some investigations have already been done for potential use in polymer composites. This article highlights the results of a study on the use of wood ash in HDPE. Wood ash is mainly a mixture of various metallic compounds and some silica. Here, the characterization of wood ash has been done with the help of XRD, ICPAES, light scattering based particle size analysis, FTIR, and SEM. The results show that wood ash particle size has an average value of 293 nm, much lower than other categories of ash. When blended with HDPE in the presence of a compatibilizer, wood ash gives rise to vastly improved mechanical properties over that of the base polymer. The results prove that wood ash is a valuable reinforcing material for HDPE and the environmental pollution due to wood ash can be solved in a most profitable way by this technique. |
Description: | Journal of Applied Polymer Science, Vol. 124, 1659–1667 (2012) |
URI: | http://dyuthi.cusat.ac.in/purl/4719 |
Files | Size |
---|---|
HDPE-Ash Nanocomposites.pdf | (1.043Mb) |