Abstract:
|
ZnGa2O4:Dy3+ phosphor thin films were deposited on quartz substrates by radio frequency rf magnetron sputtering and the effect
of substrate temperature on its structural and luminescent properties was investigated. Polycrystalline film could be deposited even
at room temperature. The crystalline behavior, Zn/Ga ratio, and surface morphology of the films were found to be highly sensitive
to substrate temperature. Under UV illumination, the as-deposited films at and above 300°C gave white luminescence even
without any postdeposition treatments. The photoluminescent PL emission can be attributed to the combined effect of multicolor
emissions from the single luminescence center Dy3+ via host-sensitization. Maximum PL emission intensity was observed for the
film deposited at 600°C, and the CIE chromaticity coordinates of the emission were determined to be x,y = 0.34, 0.31 . |