Now showing items 1-5 of 5
Abstract: | The spectroscopic analysis of the emission from the plasma produced by irradiating a highT c superconducting GdBa2Cu3O7 target with a high power Nd:YAG laser beam shows the existence of the bands from different oxides in addition to the lines from neutrals and ions of the constituent elements. The spectral emissions by oxide species in laser-induced plasma show considerable time delays as compared to those from neutral and ionic species. Recombination processes taking place during the cooling of the hot plasma, rather than the plasma expansion velocities, have been found to be responsible for the observed time delays in this case. The decays of emission intensities from various species are found to be non-exponential. |
URI: | http://dyuthi.cusat.ac.in/purl/2464 |
Files | Size |
---|---|
Dyuthi-P0293.pdf | (516.3Kb) |
Abstract: | A simple experimental set-up is described to measure the electromagnetic shielding property of high Tc superconducting samples. Measurements were performed using HTSC materials in the form of laser ablated thin films, powders and sintered pellets. Samples used were Gd-123 in pure and doped form as well as a few Bi-based superconducting ceramics. For comparison, similar measurements were carried out on metals like aluminium, copper and μ metal. Very effective shielding was observed for HTSC materials compared to the conventional materials mentioned above. However it also depended on the sample types and poor shielding was observed for powdered HTSC material in comparison to thin films prepared by laser ablation. |
URI: | http://dyuthi.cusat.ac.in/purl/2657 |
Files | Size |
---|---|
Dyuthi-P0338.pdf | (195.2Kb) |
Abstract: | Laser induced plasma emission spectra from highT c superconducting samples of YBa2Cu3O7 and GdBa2Cu3O7 obtained with 1.06µm radiation from a Q switched Nd:YAG laser beam has been analysed. The results clearly show the presence of diatomic oxides in addition to ionized species of the constituent metals in the plasma thus produced. |
URI: | http://dyuthi.cusat.ac.in/purl/2473 |
Files | Size |
---|---|
Dyuthi-P0284.pdf | (406.0Kb) |
Abstract: | In order to characterise the laser ablation process from high-Tc superconductors, the time evolution of plasma produced by a Q-switching Nd:YAG laser from a GdBa2Cu3O7 superconducting sample has been studied using spectroscopic and ion-probe techniques. It has been observed that there is a fairly large delay for the onset of the emission from oxide species in comparison with those from atoms and ions of the constituent elements present in the plasma. Faster decay occurs for emission from oxides and ions compared with that from neutral atoms. These observations support the view that oxides are not directly produced from the target, but are formed by the recombination process while the plasma cools down. Plasma parameters such as temperature and velocity are also evaluated. |
URI: | http://dyuthi.cusat.ac.in/purl/2425 |
Files | Size |
---|---|
Dyuthi-P0285.pdf | (500.6Kb) |
Abstract: | he phenomenon of single beam mirage effect, otherwise known as photothermal deflection (PTD) effect using a He–Ne laser beam has been employed to detect phase transitions in some liquid crystals. It has been observed that anomalous changes in amplitude occur in the PTD signal level near the transition temperature. The experimental details and the results of measurements made in liquid crystals E8, M21 and M24 are given in this paper. |
URI: | http://dyuthi.cusat.ac.in/purl/2394 |
Files | Size |
---|---|
Dyuthi-P0203.pdf | (115.9Kb) |
Now showing items 1-5 of 5