Abstract: | It is observed that reclamation of natural rubber latex based rubber using 2,2'-dibenzamidodiphenvldisulphide as reclaiming agent is an optional methodology for recycling of waste latex rubber (WLR). For progressive replacement of virgin natural rubber by the reclaim, two alternatives curing system were investigated: adjustment or reduction of the curing system with increasing reclaim content, to compensate for the extra amount of curatives brought along by the reclaim. For fixed curing system, as if the reclaim were equivalent to virgin NR. The cure behavior, final crosslink density and distribution, mechanical properties, and dynamic viscoelastic properties of the blends with reclaimed WLR are measured and compared with the virgin compound. The morphology of the blends, sulfur migration, and final distribution are analyzed.The mechanical and dynamic viscoelastic properties deteriorate for both curing systems, but to a lesser extent for fixed curing system compared to adjusted curing system. With the fixed cure system, many properties like tensile strength and compression set do still deteriorate, but tan 6 and Mrrr„/Murxr, representative for the rolling resistance of tires are improved. On the other hand, with the adjusted cure system both mechanical and dynamic properties still deteriorate. |
URI: | http://dyuthi.cusat.ac.in/purl/820 |
Files | Size |
---|---|
V V Rajan and o ... cling of NR...,Feb2006.PDF | (9.335Mb) |
Abstract: | A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability. |
URI: | http://dyuthi.cusat.ac.in/purl/796 |
Files | Size |
---|---|
Beena Mary John ... recording...,march2005.PDF | (7.043Mb) |
Abstract: | ABSTRACT: The rheological and extrudate behaviour of natural rubber/latex reclaim blends were evaluated using a capillary viscometer . The study shows that the viscosity of natural rubber decreases marginally on the addition of latex reclaim while the variation of viscosity with shear rate is not affected. The temperature sensitivity of the blends is not affected significantly with the addition of latex reclaim . The extrudates of natural rubber/latex reclaim blends are smooth up to the addition of about 50 wt. percent latex reclaim in filled natural rubber compounds. |
URI: | http://dyuthi.cusat.ac.in/purl/842 |
Files | Size |
---|---|
Reena Susan Geo ... Rheological and..,1995.PDF | (5.735Mb) |
Abstract: | The rheological characteristics of short Nylon-6 fiber-reinforced Styrene Butadiene rubber (SBR) in the presence of epoxy resin-based bonding agent were studied with respect to the effect of shear rate, fiber concentration , and temperature on shear viscosity and die swell using a capillary rheonzeter. All the composites containing bonding agent showed a pseudoplastic nature, which decreased with increasing temperature. Shear viscosity was increased in the presence of fibers. The temperature sensitivity of the SBR matrices was reduced on introduction of fibers. The temperature sensitivity of the melts was found to be lower at higher shear rates. Die swell was reduced in the presence of fibers. Relative viscosity of the composites increased with shear rate. In the presence of epoxy resin bonding agent the temperature sensitivity of the mixes increased. Die swell was larger in the presence of bonding agent. |
URI: | http://dyuthi.cusat.ac.in/purl/893 |
Files | Size |
---|---|
SEEMA, A, S. K. ... ORT NYLON-6 FIBRE......PDF | (5.107Mb) |
Abstract: | The rheological behavior of a short-polyester-fiber-filled polyurethane elastomer composite containing different bonding agents has been studied in the temperature range 120-160°C and in the shear rate range 63-608 s-'. The composite with and without bonding agents showed a pseudoplastic behavior which decreased with the increase of temperature. Composites containing bonding agents based on polypropyleneglycol and 4,4'-diphenylmethanediisocyanate showed the lowest viscosity values at a particular shear rate, whereas composites containing a glycerol- (GL) based bonding agent showed the highest viscosity. The viscosity of the composite decreased sharply after a particular temperature (140°C) and the fall was less drastic in the composite containing a GL-based bonding agent. |
URI: | http://dyuthi.cusat.ac.in/purl/903 |
Files | Size |
---|---|
Suhara, F S K N ... poltester.............PDF | (4.516Mb) |
Abstract: | The rheological characteristics of short Nylon-6 fiber reinforced styrene butadiene rubber (SBR) were studied using a capillary rheometer. The study was done with respect to the effect of shear rate, fiber concentration, and temperature on shear viscosity and die swell. All the melts showed pseudoplastic nature, which decreased with increasing temperature. Shear viscosity increased in the presence of fibers. Introduction of fiber reduces the temperature sensitivity of the rubber matrix. A reduction in die swell was found in presence of fibers. |
URI: | http://dyuthi.cusat.ac.in/purl/894 |
Files | Size |
---|---|
SEEMA, A, S. K. ... REINFORCED............PDF | (6.615Mb) |
Abstract: | Fully burnt rice hull (rice hull ash) was tried as a low cost filler in place of precipitated silica in NBR/PVC based microcellular soles. The mechanical properties of the soles containing silica and ash are found to be comparable. The expansion is marginally higher in the presence of ash, which permits to reduce the amount of blowing agent. Cell structure of microcellular sheets remains unchanged when silica is replaced by ash. |
URI: | http://dyuthi.cusat.ac.in/purl/867 |
Files | Size |
---|---|
R Srilathakutty ... ,Rice hull ash...,2002.PDF | (4.693Mb) |
Abstract: | This paper presents the results of a study on the use of rice husk ash (RHA) for property modification of high density polyethylene (HDPE). Rice husk is a waste product of the rice processing industry. It is used widely as a fuel which results in large quantities of RHA. Here, the characterization of RHA has been done with the help of X-ray diffraction (XRD), Inductively Coupled Plasma Atomic Emission Spectroscopy (ICPAES), light scattering based particle size analysis, Fourier transform infrared spectroscopy (FTIR) and Scanning Electron Microscope (SEM). Most reports suggest that RHA when blended directly with polymers without polar groups does not improve the properties of the polymer substantially. In this study RHA is blended with HDPE in the presence of a compatibilizer. The compatibilized HDPE-RHA blend has a tensile strength about 18% higher than that of virgin HDPE. The elongation-at-break is also higher for the compatibilized blend. TGA studies reveal that uncompatibilized as well as compatibilized HDPERHA composites have excellent thermal stability. The results prove that RHA is a valuable reinforcing material for HDPE and the environmental pollution arising from RHA can be eliminated in a profitable way by this technique. |
Description: | Materials and Design 41 (2012) 1–7 |
URI: | http://dyuthi.cusat.ac.in/purl/4691 |
Files | Size |
---|---|
Rice husk ash – ... h density polyethylene.pdf | (725.3Kb) |
Abstract: | ABSTRACT: Rubber seed oil was used as a multipurpose ingredient in natural rubber (NR) and styrene butadiene rubber (SBR) compounds. The study shows that the oil, when substituted for conventional plasticiser, imparts excellent mechanical properties to NR and SBR vulcanizates. Further, it also improves aging resistance, reduces cure time, increases abrasion resistance and flex resistance, and reduces blooming. |
URI: | http://dyuthi.cusat.ac.in/purl/871 |
Files | Size |
---|---|
V Nandanan and ... er seed oil...,Aug1998.PDF | (4.054Mb) |
Abstract: | Rubber solutions were prepared and used for bonding wood pieces. The effect of the variation of chlorinated natural rubber (CNR) and phenolformaldehyde (PF) resin in the adhesive solutions on lap shear strength was determined. Natural rubber and neoprene-based adhesive solutions were compared for their lap shear strength. The storage stability of the adhesive prepared was determined. The change in lap shear strength before and after being placed in cold water, hot water, acid, and alkali was tested. The bonding character of these adhesives was compared with different commercially available solution adhesives. The room-temperature aging resistance of wood joints was also determined. In all the studies, the adhesive prepared in the laboratory was found to be superior compared to the commercial adhesives. |
URI: | http://dyuthi.cusat.ac.in/purl/859 |
Files | Size |
---|---|
Neetha John and ... er solution...,Oct1997.PDF | (3.485Mb) |
URI: | http://dyuthi.cusat.ac.in/purl/835 |
Files | Size |
---|---|
Rani Joseph an ... anning electron..,1987.PDF | (6.459Mb) |
Abstract: | Tear and wear properties of short kevlar fiber, thermoplastic polcurethane (TPU) composite with respect to fiber loading-and fiber onentation has been studied and the fracture surfaces were examined under scanning electron microscope (SEM). Tear strength first decreased up to 20 phr fiber loading and then gradually increased with increasing fiber loading. Anisotropy in tear strength was evident beyond a fiber loading of 20 phr. Tear fracture surface of unfilled TPU showed sinusoidal folding characteristics of high strength matrix. At low fiber loading the tear failure was mainly due to fibermatrix failure whereas at higher fiber loading the failure occurred by fiber breakage. Abrasion loss shows a continuous rise with increasing fiber loading, the loss in the transverse orientation of fibers being higher than that in the longitudinal orientation. The abraded surface showed lone cracks and ridges parallel to the direction of abrasion indicating an abrasive wear mechanism. In the presence of fber the abrasion loss was mainly due to fiber low. |
URI: | http://dyuthi.cusat.ac.in/purl/882 |
Files | Size |
---|---|
Golok , B, S K ... opy studies............PDF | (3.154Mb) |
Abstract: | A comprehensive overview of reclamation of cured rubber with special emphasis on latex reclamation is depicted in this paper. The latex industry has expanded over the years to meet the world demands for gloves, condoms, latex thread, etc. Due to the strict specifications for the products and the unstable nature of the latex as high as 15% of the final latex products are rejected. As waste latex rubber (WLR) represents a source of high-quality rubber hydrocarbon, it is a potential candidate for generating reclaimed rubber of superior quality. The role of the different components in the reclamation recipe is explained and the reaction mechanism and chemistry during reclamation are discussed in detail. Different types of reclaiming processes are described with special reference to processes, which selectively cleave the cross links in the vulcanized rubber. The state-of-the-art techniques of reclamation with special attention on latex treatment are reviewed. An overview of the latest development concerning the fundamental studies in the field of rubber recycling by means of low-molecular weight compounds is described. A mathematical model description of main-chain and crosslink scission during devulcanization of a rubber vulcanizate is also given. |
URI: | http://dyuthi.cusat.ac.in/purl/821 |
Files | Size |
---|---|
V V Rajan and o ... d techology...,Aug2006.PDF | (17.94Mb) |
Abstract: | The self adhesion behaviour of thermoplastic polyurethane (TPU) in itself and its composite with short Kevlar fibre with respect to contact time, temperature, pressure, and fibre loading has been studied. The adhesion strength showed two linear increments of different slopes with respect to the square root of time: with temperature and pressure of contact, the adhesion strength was improved. The maximum strength was obtained with 20 phr of short fibre in only one of the mating substrates in the peel test sample. The duration for wetting and diffusion was shifted to longer time intervals with fibres loaded in both the substrates. |
URI: | http://dyuthi.cusat.ac.in/purl/883 |
Files | Size |
---|---|
Golok , B, S K ... short kevlar...........PDF | (5.744Mb) |
Abstract: | Short fiber reinforced thermoplastics have generated much interest these days since fibrous materials tend to increase both mechanical and thermal properties, such as tensile strength, flexural strength, flexural modulus, heat deflection temperature, creep resistance, and some times impact strength of thermoplastics. If the matrix and reinforcement are both based on polymers the composite are recyclable. The rheological behavior of recyclable composites based on nylon fiber reinforced polypropylene (PP) is reported in this paper. The rheological behavior was evaluated both using a capillary rheometer and a torque rheometer. The study showed that the composite became pseudoplastic with fiber content and hence fiber addition did not affect processing adversely at higher shear rates. The torque rheometer data resembled that obtained from the capillary rheometer. The energy of mixing and activation energy of mixing also did not show much variation from that of PP alone. |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1999 |
Files | Size |
---|---|
Short nylon fibre....pdf | (438.5Kb) |
Abstract: | Filled and gum compounds of Isobutylene-Isoprene rubber were extruded through a laboratory extruder at various feeding rates, different temperatures and revolutions per minute. The extruded compounds were vulcanized up to their optimum cure times and the mechanical properties of the vulcanizates were determined. The properties suggest that there is a particular feeding rate in the starved fed region, which results in maximum mechanical properties. The study shows that running the extruder at a slightly starved condition is an attractive means of improving the physical properties. |
URI: | http://dyuthi.cusat.ac.in/purl/864 |
Files | Size |
---|---|
P J Joseph Fran ... icance of..,Dec1996PDF.PDF | (6.623Mb) |
Abstract: | Reactive extrusion is an attractive means of polymer processing since the shaping and reaction take place in a single operation. In this paper we report the silane grafting of polyethylenes in a single screw extruder. The optimum conditions for silane grafting, viz. temperature, shear rate, silane and DCP concentrations, were determined on a torque rheometer and then actual extrusion was performed using these conditions. The study shows that an optimum low level of grafting/ crosslinking can be introduced into polyethylene during its extrusion for better mechanical behavior and=or thermal stability without affecting the processability. |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1997 |
Files | Size |
---|---|
Silance grafting....pdf | (386.9Kb) |
Abstract: | Filled compounds of natural rubber, isobutylene-isoprene rubber and styrene-butadiene rubber compounds were extruded through a laboratory extruder by varying the feeding rate at different temperatures and revolutions per minute. The extruded compounds were vulcanized up to their optimum cure times and the mechanical properties of the vulcanizates were determined. The properties suggest that there is a particular feeding rate in the starved fed region which results in maximum mechanical properties. The study shows that running the extruder at a slightly starved condition is an attractive means of improving the physical properties. |
URI: | http://dyuthi.cusat.ac.in/purl/831 |
Files | Size |
---|---|
P J Joseph Fran ... rved extrusion...,1997.PDF | (7.505Mb) |
Abstract: | Gum and filled compounds of styrene-butadiene rubber are extruded through a laboratory extruder by varying the feeding rase at different temperatures and screw speed (rpm). The extruded compounds are vulcanized up4o their optimum cure times and the mechanical properties of the vulcanizates are determined. From the properties data obtained it Is concluded that there is a specific feeding rate wit in the starved fed region, which results In maximum Improved mechanical properties . The enhancement In properties is found to be due to better thermal and shear homogeneity. |
URI: | http://dyuthi.cusat.ac.in/purl/865 |
Files | Size |
---|---|
P J Joseph fran ... rved feeding..,Jan1997.PDF | (4.492Mb) |
Abstract: | The stress relaxation behavior of polyurethane elastomer and short polyester fiber filled elastomer composites with and without bonding agents at different strain levels and strain rates was studied. It was found that these compounds exhibit a multistage relaxation mechanism and that the rate of relaxation and cross-over time depend on the strain level and strain rate. The incorporation of fibers reduced the stage-I relaxation rate and increased the cross-over time of the gum vulcanisate. A higher rate of relaxation (first stage) was shown by the composites with longitudinal fiber orientation and composites with bonding agents. |
URI: | http://dyuthi.cusat.ac.in/purl/904 |
Files | Size |
---|---|
Suhara, F S K N ... lyester fibre..........PDF | (5.093Mb) |