Sunil,K Narayanankutty(John Wiley & Sons. Inc., June 21, 2001)
[+]
[-]
Abstract:
The effect of diphenylmethane diisocyanate
(MDI) -polyethyleneglycol (PEG) resin on the cure characteristics and mechanical
properties of nitrile rubber/whole tyre eclaim-short nylon fiber
composite-was studied. At a constant loading of 5 phr, the resin composition
was varied. The minimum torque .,id (maximum - minimum) torque increased
with isocyanate concentration. Scorch time and cure time showed a reduction on
introduction of bonding agent. Properties like tensile strength, tear strength, and
abrasion resistance increased with increase in MDI/PEG ratio, and these
properties are higher in the longitudinal direction of fiber orientation.
Compression set increased with isocyanate concentration and the resilience
remain unchanged.
Eby Thomas, Thachil; Unnikrishnan, K P; Benny Cherian, A; Jenish, Paul(Universal Research Publications, December , 2011)
[+]
[-]
Abstract:
In this study, pendant epoxy functional poly dimethyl siloxanes were synthesized by the hydrosilylation reaction of pendant silyl hydride functional polydimethyl siloxane with allyl glycidyl ether. The hydrosilylation reaction was characterized by spectroscopic techniques. Samples of pendant epoxy functional poly dimethyl siloxanes and pendant silyl hydride functional polydimethyl siloxane were blended with commercial epoxy resin, diglycidyl ether of bis-phenol A, at various ratios using a polyamine as curing agent. The results show that the addition of functionalised poly dimethyl siloxanes increases the flexibility of the cross linked network and also the thermal stability and water resistance
Description:
Advances in Polymer Science and Technology: An International Journal 2011; 1 (2): 22-29