Anantharaman, M R; Sethulakshmi, N; Al-Omari, I A; Suresh, K G(AIP Publishing, March 5, 2014)
[+]
[-]
Abstract:
Nearly half of lanthanum sites in lanthanum manganites were substituted with monovalent
ion-sodium and the compound possessed distorted orthorhombic structure. Ferromagnetic ordering
at 300K and the magnetic isotherms at different temperature ranges were analyzed for estimating
magnetic entropy variation. Magnetic entropy change of 1.5 J kg 1 K 1 was observed near 300 K.
An appreciable magnetocaloric effect was also observed for a wide range of temperatures near
300K for small magnetic field variation. Heat capacity was measured for temperatures lower than
300K and the adiabatic temperature change increases with increase in temperature with a
maximum of 0.62K at 280 K