Abstract: | Nearly half of lanthanum sites in lanthanum manganites were substituted with monovalent ion-sodium and the compound possessed distorted orthorhombic structure. Ferromagnetic ordering at 300K and the magnetic isotherms at different temperature ranges were analyzed for estimating magnetic entropy variation. Magnetic entropy change of 1.5 J kg 1 K 1 was observed near 300 K. An appreciable magnetocaloric effect was also observed for a wide range of temperatures near 300K for small magnetic field variation. Heat capacity was measured for temperatures lower than 300K and the adiabatic temperature change increases with increase in temperature with a maximum of 0.62K at 280 K |
Description: | APPLIED PHYSICS LETTERS 104, 092407 (2014) |
URI: | http://dyuthi.cusat.ac.in/purl/4427 |
Files | Size |
---|---|
Near fifty perc ... mperature applications.pdf | (1.450Mb) |
Abstract: | Magnetic materials meant for audio/video recording applications necessitate that polycrystalline materials be in acicular shape. So preparation of acicular precursors for magnetic storage materials assumes significance. The employment of aqueous solutions do not produce needle shape crystallites. Glycerol is one of the complexing media used for the precipitation of ferrous oxalate dihydrate. An inexpensive method using starch for preparation of acicular particles is described. The influence of an additive namely Gd on acicularity is also investigated |
Description: | Bull. Mater. Sci., Vol. 20, No. 7, October 1997, pp. 975 980 |
URI: | http://dyuthi.cusat.ac.in/purl/4398 |
Files | Size |
---|---|
A new inexpensi ... gnetic recording media.pdf | (1.271Mb) |
Abstract: | In this letter, we report flexible, non corrosive, and light weight nickel nanoparticle@multi-walled carbon nanotube–polystyrene (Ni@MWCNT/PS) composite films as microwave absorbing material in the frequency range of S band (2-4 GHz). Dielectric permittivity and magnetic permeability of composites having 0.5 and 1.5 wt. % filler amount were measured using the cavity perturbation technique. Reflection loss maxima of 33 dB (at 2.7 GHz) and 24 dB (at 2.7 GHz) were achieved for 0.5 and 1.5 wt. % Ni@MWCNT/PS composite films of 6 and 4 mm thickness, respectively, suggesting that low concentrations of filler provide significant electromagnetic interference shielding |
Description: | APPLIED PHYSICS LETTERS 99, 113116 (2011) |
URI: | http://dyuthi.cusat.ac.in/purl/4363 |
Files | Size |
---|---|
Ni filled flexi ... nt microwave absorbers.pdf | (2.017Mb) |
Abstract: | Photothermal deflection technique (PTD) is a non-destructive tool for measuring the temperature distribution in and around a sample, due to various non-radiative decay processes occurring within the material. This tool was used to measure the carrier transport properties of CuInS2 and CuInSe2 thin films. Films with thickness <1 μm were prepared with different Cu/In ratios to vary the electrical properties. The surface recombination velocity was least for Cu-rich films (5×105 cm/s for CuInS2, 1×103 cm/s for CuInSe2), while stoichiometric films exhibited high mobility (0.6 cm2/V s for CuInS2, 32 cm2/V s for CuInSe2) and high minority carrier lifetime (0.35 μs for CuInS2, 12 μs for CuInSe2 |
Description: | Thin Solid Films 518 (2010) 1767–1773 |
URI: | http://dyuthi.cusat.ac.in/purl/4712 |
Files | Size |
---|---|
Non-destructive ... l deflection technique.pdf | (1.073Mb) |
Abstract: | Oxide free stable metallic nanofluids have the potential for various applications such as in thermal management and inkjet printing apart from being a candidate system for fundamental studies. A stable suspension of nickel nanoparticles of ∼5 nm size has been realized by a modified two-step synthesis route. Structural characterization by x-ray diffraction and transmission electron microscopy shows that the nanoparticles are metallic and are phase pure. The nanoparticles exhibited superparamagnetic properties. The magneto-optical transmission properties of the nickel nanofluid (Ni-F) were investigated by linear optical dichroism measurements. The magnetic field dependent light transmission studies exhibited a polarization dependent optical absorption, known as optical dichroism, indicating that the nanoparticles suspended in the fluid are non-interacting and superparamagnetic in nature. The nonlinear optical limiting properties of Ni-F under high input optical fluence were then analyzed by an open aperture z-scan technique. The Ni-F exhibits a saturable absorption at moderate laser intensities while effective two-photon absorption is evident at higher intensities. The Ni-F appears to be a unique material for various optical devices such as field modulated gratings and optical switches which can be controlled by an external magnetic field |
Description: | Nanotechnology 22 (2011) 375702 (7pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4391 |
Files | Size |
---|---|
Nonlinear and m ... c nickel nanoparticles.pdf | (921.0Kb) |
Abstract: | Materials belonging to the family of manganites are technologically important since they exhibit colossal magneto resistance. A proper understanding of the transport properties is very vital in tailoring the properties. A heavy rare earth doped manganite like Gd0·7Sr0·3MnO3 is purported to be exhibiting unusual properties because of smaller ionic radius of Gd. Gd0·7Sr0·3MnO3 is prepared by a wet solid state reaction method. The conduction mechanism in such a compound has been elucidated by subjecting the material to low temperature d.c. conductivity measurement. It has been found that the low band width material follows a variable range hopping (VRH) model followed by a small polaron hopping (SPH) model. The results are presented here |
Description: | Bull. Mater. Sci., Vol. 35, No. 1, February 2012, pp. 41–45. |
URI: | http://dyuthi.cusat.ac.in/purl/4432 |
Files | Size |
---|---|
On conduction m ... of Gd basedmanganites.pdf | (148.3Kb) |
Abstract: | Zinc aluminate nanoparticles with average particle size of 40 nm were synthesized using a sol–gel combustion method. X-ray diffractometry result was analysed by Rietveld refinement method to establish the phase purity of the material. Different stages of phase formation of the material during the synthesis were investigated using differential scanning calorimetry and differential thermogravimetric analysis. Particle size was determined with transmission electron microscopy and the optical bandgap of the nanoparticles was determined by absorption spectroscopy in the ultraviolet-visible range. Dielectric permittivity and a.c. conductivity of the material were measured for frequencies from 100 kHz to 8 MHz in the temperature range of 30–120◦C. The presence of Maxwell– Wagner type interfacial polarization was found to exist in the material and hopping of electron by means of quantum mechanical tunneling is attributed as the reason for the observed a.c. conductivity |
Description: | Bull. Mater. Sci., Vol. 34, No. 2, April 2011, pp. 251–259 |
URI: | http://dyuthi.cusat.ac.in/purl/4374 |
Files | Size |
---|---|
On structural, ... luminate nanoparticles.pdf | (577.6Kb) |
Abstract: | Activation energy for crystallization (Ec) is a pertinent parameter that decides the application potential of many metallic glasses and is proportional to the crystallization temperature. Higher crystallization temperatures are desirable for soft magnetic applications, while lower values for data storage purposes. In this investigation, from the heating rate dependence of peak crystallization temperature Tp, the Ec values have been evaluated by three different methods for metglas 2826 MB (Fe40Ni38B18Mo4) accurately. The Ec values are correlated with the morphological changes, and the structural evolution associated with annealing temperatures is discussed. |
URI: | http://dyuthi.cusat.ac.in/purl/2842 |
Files | Size |
---|---|
Dyuthi-P00395.pdf | (452.8Kb) |
Abstract: | The temperature and frequency dependence of dielectric permittivity and dielectric loss of nanosized Mn1−xZnxFe2O4 (for x = 0, 0.2, 0.4, 0.6, 0.8, 1) were investigated. The impact of zinc substitution on the dielectric properties of the mixed ferrite is elucidated. Strong dielectric dispersion and broad relaxation were exhibited by Mn1−xZnxFe2O4. The variation of dielectric relaxation time with temperature suggests the involvement of multiple relaxation processes. Cole–Cole plots were employed as an effective tool for studying the observed phenomenon. The activation energies were calculated from relaxation peaks and Cole–Cole plots and found to be consistent with each other and indicative of a polaron conduction |
Description: | J. Phys.: Condens. Matter 21 (2009) 146006 (12pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4393 |
Files | Size |
---|---|
On the dielectr ... se zinc mixed ferrites.pdf | (4.818Mb) |
Abstract: | Magnetic nanowires (NWs) are ideal materials for the fabrication of various multifunctional nanostructures which can be manipulated by an external magnetic fi eld. Highly crystalline and textured nanowires of nickel (Ni NWs) and cobalt (Co NWs) with high aspect ratio (~330) and high coercivity have been synthesized by electrodeposition using nickel sulphate hexahydrate (NiSO4·6H2O) and cobalt sulphate heptahydrate (CoSO4·7H2O) respectively on nanoporous alumina membranes. They exhibit a preferential growth along〈110〉. A general mobility assisted growth mechanism for the formation of Ni and Co NWs is proposed. The role of the hydration layer on the resulting one-dimensional geometry in the case of potentiostatic electrodeposition is verified. A very high interwire interaction resulting from magnetostatic dipolar interactions between the nanowires is observed. An unusual low-temperature magnetisation switching for fi eld parallel to the wire axis is evident from the peculiar high fi eld M(T) curve |
Description: | Nano Res (2008) 1: 465 473 |
URI: | http://dyuthi.cusat.ac.in/purl/4372 |
Files | Size |
---|---|
On the Growth M ... ir Magnetic Properties.pdf | (912.6Kb) |
Abstract: | Nickel nanocomposites were prepared by incorporating nickel nanoparticles in a neoprene matrix according to a specific recipe for various loadings of nickel particles. The dielectric properties of these composites were evaluated for different frequencies ranging from 100 kHz to 8MHz at different temperatures from 30 ◦C to 120 ◦C. The dielectric permittivity increases with increase of nickel concentration. Increase in temperature enhances the permittivity initially, till 40 ◦C and thereafter the permittivity decreases. The dielectric loss exhibits relaxation peaks and the peaks shift to lower frequencies with increase in volume fraction of the nickel nanoparticles in the matrix. The evaluation of magnetic and dielectric properties of these composites suggests that the dielectric permittivity can be tailored by an appropriate loading of the filler using semi-empirical equations and the magnetic properties vary according to simple mixture equations |
Description: | Materials Chemistry and Physics 121 (2010) 154–160 |
URI: | http://dyuthi.cusat.ac.in/purl/4408 |
Files | Size |
---|---|
On the magnetic ... eoprene nanocomposites.pdf | (1.316Mb) |
Abstract: | Rubber–nickel nanocomposites were synthesized by incorporating freshly prepared nanometric nickel particles in two different matrices namely natural rubber and neoprene rubber according to specific recipes for various loadings of nano nickel and the cure characteristics of these composites were evaluated. The maximum torque values register an increase with the increase in loading of nickel in both composites and this is attributed to the non-interacting nature of nickel nanoparticles with rubber matrices. The cure time of natural rubber composites decreases with increase in the content of nickel, and in neoprene rubber cure, time increases with increase in filler content. In natural rubber, the curing reaction seems to be activated by the presence of nickel particles. The magnetization studies of the composites reveal that the magnetic properties of nickel are retained in the composite samples. The elastic modulus of natural rubber and neoprene rubber are largely improved by the incorporation of nickel particles |
Description: | Polym. Bull. (2010) 64:907–923 |
URI: | http://dyuthi.cusat.ac.in/purl/4392 |
Files | Size |
---|---|
On the magnetic ... –nickel nanocomposites.pdf | (483.8Kb) |
Abstract: | Zinc ferrite belongs to the class of normal spinels where it is assumed to have a cation distribution of Zn2`(Fe3`)2(O2~)4, and it is purported to be showing zero net magnetisation. However, there have been recent reports suggesting that zinc ferrite exhibits anomaly in its magnetisation. Zinc ferrite samples have been prepared by two di¤erent routes and have been analysed using low energy ion scattering, Mo¬ ssbauer spectroscopy and magnetic measurements. The results indicate that zinc occupies octahedral sites, contrary to the earlier belief that zinc occupies only the tetrahedral sites in a normal spinel. The amount of zinc on the B site increases with decrease in particle size. The LEIS results together with the Mo¬ ssbauer results and the magnetic measurements lead to the conclusion that zinc occupies the B site and the magnetisation exhibited by ultraÞne particles of zinc is due to short range ordering |
Description: | Journal of Magnetism and Magnetic Materials 189 (1998) 83-88 |
URI: | http://dyuthi.cusat.ac.in/purl/4348 |
Files | Size |
---|---|
On the magnetic ... ltra-Þne zinc ferrites.pdf | (88.12Kb) |
Abstract: | Polyaniline is a widely studied conducting polymer and is a useful material in its bulk and thin film form for many applications, because of its excellent optical and electrical properties. Pristine and iodine doped polyaniline thin films were prepared by a.c. and rf plasma polymerization techniques separately for the comparison of their optical and electrical properties. Doping of iodine was effected in situ. The structural properties of these films were evaluated by FTIR spectroscopy and the optical band gap was estimated from UV-vis-NIR measurements. Comparative studies on the structural, optical and electrical properties of a.c. and rf polymerization are presented here. It has been found that the optical band gap of the polyaniline thin films prepared by rf and a.c. plasma polymerization techniques differ considerably and the band gap is further reduced by in situ doping of iodine. The electrical conductivity measurements on these films show a higher value of electrical conductivity in the case of rf plasma polymerized thin films when compared to the a.c. plasma polymerized films. Also, it is found that the iodine doping enhanced conductivity of the polymer thin films considerably. The results are compared and correlated and have been explained with respect to the different structures adopted under these two preparation techniques |
Description: | Bull. Mater. Sci., Vol. 29, No. 2, April 2006, pp. 159–163 |
URI: | http://dyuthi.cusat.ac.in/purl/4353 |
Files | Size |
---|---|
On the optical ... of rf and a.c. plasma.pdf | (98.18Kb) |
Abstract: | Multiwall carbon nanotubes (MWCNTs) possessing an average inner diameter of 150 nm were synthesized by template assisted chemical vapor deposition over an alumina template. Aqueous ferrofluid based on superparamagnetic iron oxide nanoparticles (SPIONs) was prepared by a controlled co-precipitation technique, and this ferrofluid was used to fill the MWCNTs by nanocapillarity. The filling of nanotubes with iron oxide nanoparticles was confirmed by electron microscopy. Selected area electron diffraction indicated the presence of iron oxide and graphitic carbon from MWCNTs. The magnetic phase transition during cooling of the MWCNT–SPION composite was investigated by low temperature magnetization studies and zero field cooled (ZFC) and field cooled experiments. The ZFC curve exhibited a blocking at ∼110 K. A peculiar ferromagnetic ordering exhibited by the MWCNT–SPION composite above room temperature is because of the ferromagnetic interaction emanating from the clustering of superparamagnetic particles in the constrained volume of an MWCNT. This kind of MWCNT–SPION composite can be envisaged as a good agent for various biomedical applications |
Description: | Nanotechnology 20 (2009) 055607 (7pp) |
URI: | http://dyuthi.cusat.ac.in/purl/4379 |
Files | Size |
---|---|
On the synthesi ... article nanocomposites.pdf | (1.113Mb) |
Abstract: | Effect of varying spray rate on the structure and optoelectronic properties of spray pyrolysed ZnO film is analysed. ZnO films were characterised using different techniques such as X-ray diffraction (XRD), photoluminescence, electrical resistivity measurement, and optical absorption. The XRD analysis proved that, with the increase in spray rate, orientation of the grains changed from (1 0 1) plane to (0 0 2) plane. The films exhibited luminescence in two regions—one was the ‘near band-edge’ (NBE) (∼380 nm) emission and the other one was the ‘blue-green emission’ (∼503 nm). Intensity of the blue-green emission decreased after orientation of grains shifted to (0 0 2) plane. Scanning electron microscope (SEM) analysis of the films asserts that spray rate has major role in improving the crystallographic properties of the films. Moreover resistivity of the films could be lowered to 2.4×10−2 cm without any doping or post-deposition annealing |
Description: | Applied Surface Science 256 (2010) 6025–6028 |
URI: | http://dyuthi.cusat.ac.in/purl/4714 |
Files | Size |
---|---|
On tuning the o ... rolysed ZnO thin films.pdf | (464.4Kb) |
Abstract: | The optical and carrier transport properties of amorphous transparent zinc indium tin oxide (ZITO)(a-ZITO) thin films and the characteristics of the thin-film transistors TFTs were examined as a function of chemical composition. The as-deposited films were very conductive and showed clear free carrier absorption FCA . The analysis of the FCA gave the effective mass value of 0.53 me and a momentum relaxation time of 3.9 fs for an a-ZITO film with Zn:In:Sn = 0.35:0.35:0.3. TFTs with the as-deposited channels did not show current modulation due to the high carrier density in the channels. Thermal annealing at 300°C decreased the carrier density and TFTs fabricated with the annealed channels operated with positive threshold voltages VT when Zn contents were 25 atom % or larger. VT shifted to larger negative values, and subthreshold voltage swing increased with decreasing the Zn content, while large on–off current ratios 107–108 were kept for all the Zn contents. The field effect mobilities ranged from 12.4 to 3.4 cm2 V−1 s−1 for the TFTs with Zn contents varying from 5 to 48 atom %. The role of Zn content is also discussed in relation to the carrier transport properties and amorphous structures. |
URI: | http://dyuthi.cusat.ac.in/purl/785 |
Files | Size |
---|---|
Optical and Car ... perties of Cosputtered.pdf | (724.2Kb) |
Abstract: | Structural, electronic, and optical properties of amorphous and transparent zinc tin oxide films deposited on glass substrates by pulsed laser deposition (PLD) were examined for two chemical compositions of Zn:Sn=1:1 and 2:1 as a function of oxygen partial pressure PO2 used for the film deposition and annealing temperature. Different from a previous report on sputter-deposited films Chiang et al., Appl. Phys. Lett. 86, 013503 2005 , the PLD-deposited films crystallized at a lower temperature 450 °C to give crystalline ZnO and SnO2 phases. The optical band gaps Tauc gaps were 2.80−2.85 eV and almost independent of oxygen PO2 , which are smaller than those of the corresponding crystals 3.35−3.89 eV . Films deposited at low PO2 showed significant subgap absorptions, which were reduced by postthermal annealing. Hall mobility showed steep increases when carrier concentration exceeded threshold values and the threshold value depended on the film chemical composition. The films deposited at low PO2 2 Pa had low carrier concentrations. It is thought that the low PO2 produced high-density oxygen deficiencies and generated electrons, but these electrons were trapped in localized states, which would be observed as the subgap absorptions. Similar effects were observed for 600 °C crystallized films and their resistivities were increased by formation of subgap states due to the reducing high-temperature condition. High carrier concentrations and large mobilities were obtained in an intermediate PO2 region for the as-deposited films. |
URI: | http://dyuthi.cusat.ac.in/purl/786 |
Files | Size |
---|---|
Optical and ele ... transistor application.pdf | (837.2Kb) |
Abstract: | Highly conductive and transparent thin films of amorphous zinc indium tin oxide are prepared at room temperature by co-sputtering of zinc 10 oxide and indium tin oxide. Cationic contents in the films are varied by adjusting the power to the sputtering targets. Optical transmission study of 11 films showed an average transmission greater than 85% across the visible region. Maximum conductivity of 6×102 S cm−1 is obtained for Zn/In/ 12 Sn atomic ratio 0.4/0.4/0.2 in the film. Hall mobility strongly depends on carrier concentration and maximum mobility obtained is 18 cm2 V−1 s−1 13 at a carrier concentration of 2.1×1020 cm−3. Optical band gap of films varied from 3.44 eV to 3 eV with the increase of zinc content in the film 14 while the refractive index of the films at 600 nm is about 2.0. |
URI: | http://dyuthi.cusat.ac.in/purl/792 |
Files | Size |
---|---|
TSF_24084.pdf | (673.9Kb) |
Abstract: | Optical emission spectroscopic studies were carried out on the plasma produced by ablation of zinc oxide target using the third harmonic 355 nm of Q-switched Nd:YAG laser, in vacuum and at three different ambient gas oxygen pressures. The spatial variations of electron density Ne and electron temperature Te were studied up to a distance of 20 mm from the target surface. The kinematics of the emitted particles and the expansion of the plume edge are discussed. The optimum conditions favorable for the formation of high quality zinc oxide thin films are thereby suggested. |
URI: | http://dyuthi.cusat.ac.in/purl/787 |
Files | Size |
---|---|
Optical emissio ... ated zinc oxide plasma.pdf | (95.83Kb) |