Abstract: | The electron donating properties of La2O3 activated at 300, 500 and 800·C and its mixed oxides with alumina are reported from the studies on adsorption of electron acceptors of varying electron affinity on La203. The electron acceptors with their electron affinity values given in parenthesis are: 7,7,8,8-tetracyanoquinodimethane (2.84 eV), 2,3,5,6-tetrachloro-I,4-benzoquinone (2.40 eV) and p-dinitrobenzene(l.77eV). The basicity of the oxide has been determined by titration with n-butylamine and Ho.max values are reported. The limit of electron transfer from the oxide to the electron acceptor is between 2.40 and 1.77 eV. It is observed that La203 promotes the surface electron properties of alumina without changing its limit of electron transfer. |
URI: | http://dyuthi.cusat.ac.in/purl/2217 |
Files | Size |
---|---|
Dyuthi-SS22.pdf | (236.1Kb) |
Abstract: | Lanthanum oxide, La2O3 has been found to be an effective catalyst for the liquid phase reduction of cyclohexanone. The catalytic activities of La2O3 activated at 300, 500 and 800·C and its mixed oxides with alumina for the reduction of cyclohexanone with 2-propanol have been determined and the data parallel that of the electron donating properties of the catalysts. The electron donating properties of the catalysts have been determined from the adsorption of electron acceptors of different electron affinities on the surface of these oxides. |
URI: | http://dyuthi.cusat.ac.in/purl/2220 |
Files | Size |
---|---|
Dyuthi-SS24.pdf | (275.1Kb) |
Abstract: | The limit of electron transfer in electron affinity from the oxide surface to the electron acceptor (EA) are reported from the adsorption of EA on DY203, mixed oxides of DY203 with alumina and mixed oxides of Y203 with y-alumina. The extent of electron transfer is understood from magnetic measurements. |
URI: | http://dyuthi.cusat.ac.in/purl/2275 |
Files | Size |
---|---|
Dyuthi-SS55.pdf | (210.7Kb) |