Abstract: | The aim of catalysis research is to apply the catalyst successfully in economically important reactions in an environmentally friendly way. The present work focuses on the modification of structural and surface properties of ceria and ceria-zirconia catalysts by the incorporation of transition metals. The applications of these catalysts in industrially important reactions like ethylbenzene oxidation, alkylation of aromatics are also investigated.Sol-gel method is effective for the preparation of transition metal modified ceria and ceria-zirconia mixed oxide since it produces catalyst with highly dispersed incorporated metal. Unlike that of impregnation method plugging of pores is not prominent for sol-gel derived catalyst materials. This prevents loss of surface area on metal modification as evident for BET surface area measurements.The powder X-ray diffraction analysis confirms the cubic structure of transition metal modified ceria and ceria-zirconia catalysts. The thermal stability is evident from TGA/DTA analysis. DR UV-vis spectra provide information on the coordination environment of the incorporated metal. EPR analysis ofCr, Mn and Cu modified ceria and a ceria-zirconia catalyst reveals the presence of different oxidation states of incorporated metal.Temperature programmed desorption of ammonia and thermogravimetric desorption of 2,6-dimethyl pyridine confirms the enhancement of acidity on metal incorporation. High a-methyl styrene selectivity in cumene cracking reaction implies the presence of comparatively more number of Lewis acid sites with some amount of Bronsted acid sites. The formation of cyclohexanone during cyclohexanol decomposition confirms the presence of basic sites on the catalyst surface.Mn and Cr modified catalysts show better activity towards ethylbenzene oxidation. A redox mechanism through oxometal pathway is suggested.All the catalysts were found to be active towards benzylation of toluene and a-xylene. The selectivity towards monoalkylated products remains almost 100%. The catalytic activity is correlated with the Lewis acidity of the prepared systems.The activity of the catalysts towards methylation of phenols depends on the strength acid sites as well as the redox properties of the catalysts. A strong dependence of methylation activity on the total acidity is illustrated. |
Description: | Department of Applied Chemistry, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2748 |
Files | Size |
---|---|
Dyuthi-T0773.pdf | (3.735Mb) |
Abstract: | This research project aims at developing new applications for CNSL in the polymer field. Cashew nut shell liquid (CNSL) is a cheap agro-byproduct and renewable resource which consists mainly of substituted phenols. By using CNSL in place of phenol, phenol derived from petrochemicals can be conserved and a cheap agro-byproduct utilized.In this study CNSL based resin is prepared by condensing a mixture of phenol and CNSL with hexamethylenetetramine and the effect of P: F ratio and CNSL: P ratio on the properties of synthesized resin is studied. The adhesive properties of CNSL based resin in combination with neoprene rubber are investigated. The effect of varying the stoichiometric ratios between total phenol and formaldehyde and CNSL and phenol of the resin, resin content, choice and extent of fillers and adhesion promoters in the adhesive formulation are studied. The effect of resin on the ageing properties of various elastomers is also studied by following changes in tensile strength, elongation at break, modulus, tear strength, swelling index and acetone soluble matter. Crude CNSL and resins with different P: F ratios and CNSL: P ratios are incorporated into elastomers. Lastly, utility of CNSL based resin as binder for making particleboard is investigated.The results show that CNSL based resin is an effective ingredient in adhesives for bonding aluminium to aluminium. The resin used for adhesive fonnulation gives the best performance at 45 to 55 phr resin and a total phenol: formaldehyde of l:2.9. The resin when added at a rate of l5 phr improves ageing characteristics of elastomers with respect to mechanical properties. The reaction mixture of CNSL and hexa and the resin resulting from the condensation of CN SL, phenol and hexa can be used as effective binders for moulding particleboard. |
Description: | Department of Polymer Science and Rubber Technology, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2926 |
Files | Size |
---|---|
Dyuthi-T0917.pdf | (8.725Mb) |
Description: | School of Environmental Studies, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/xmlui/purl/2086 |
Files | Size |
---|---|
Dyuthi-T0452.pdf | (3.850Mb) |
Abstract: | Catalysis is a mature field with extensive practical applications in today's society.indeed,the catalysis of petroleum refining,fine chemical synthesis and emission control demands the production of catalysts in bulk quantities.Future improvement of these well established processes is likely to be incremental.On the other hand,the continuous demand for new products will require additional novel and innovative processes.The need for pollution abatement and prevention also imposes new demands on catalysis, and new processes are periodically advanced for the control of emission of gases as well as for remediation processes such as the cleaning of underground waters. The number of problems where catalysis can have a big impact is constantly growing.In general,science stimulated by the technology has enriched the field of catalysis in a way that has had broad and lasting value.The thesis"Transition metal and rare earth metal modified sol-gel titania: a versatile catalyst for organic transformations" accounts the preparation and characterization studies of both transition metals and rare earth metals modified sol-gel titania and its applications in industrially useful organic reactions. |
Description: | Department of Applied Chemistry, Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/2376 |
Files | Size |
---|---|
Dyuthi-T0648.pdf | (13.53Mb) |