Abstract: | Sedimentary biomarker pigments around Cochin estuary situated in the southwest coast of India were determined by HPLC. Fucoxanthin, an indicator of diatom was observed to be the most abundant carotenoid pigment in the estuary. Dinoflagellate derived carotenoid pigment peridinin was confined in the southern part of estuary and zeaxanthin pigment indicative of cyanobacteria were more found in sites influenced by anthropogenic activities. One compound having close similarity to fucoxanthin was also detected. Alloxanthin (cryptophyceae), chl b (green algae), canthaxanthin, neoxanthin, lutein and peridinin isomer were also detected by spectra and corresponding algal class were identified. The highest concentration of chl a (11.01 mg g 1) found near to the anthropogenic affected area while the lowest chl a (0.65 mg g 1) was recorded in industrial area. Degradation products of chl a, such as pheophorbide and pheophytin were observed and principal mode of mechanism of degradation were derived. Higher pheopigments content than chl a, reflects a density trapping of dead cells and early degradation of phytopigments from grazing activities |
Description: | Estuarine, Coastal and Shelf Science 99 (2012) 182-190 |
URI: | http://dyuthi.cusat.ac.in/purl/4618 |
Files | Size |
---|---|
Biomarker pigme ... th west coast of India.pdf | (961.9Kb) |
Abstract: | Mechanical properties and thermal degradation characteristics of natural rubber compounds captaining coconut oil were compared with that of a control compound containing naphthenic oil. Cure time was marginally lower in the case of coconut oil mixes, probably due to the presence of free fatty acids. Tensile strength , tear strength, resilience and abrasion resistance were better than the naphthenic oil-based compounds . Compression set and hardness were marginally inferior The coconut oil mixes had a crosslink density comparable to that of the reference compound. Thermal studies showed that the temperature of initiation of degradation was increased by 10°C and the temperature at which the peak rate of degradation occured was increased by 7°C. The peak rate of degradation was compa rable to the control compound. |
URI: | http://dyuthi.cusat.ac.in/purl/891 |
Files | Size |
---|---|
RAJU,P, NANDANA ... OIL AS PLASTICISERPDF.PDF | (4.469Mb) |
Abstract: | The great potential for the culture of non-penaeid prawns, especially Macrobrachium rosenbergii in brackish and low saline areas of Indian coastal zone has not yet been fully exploited due to the non availability of healthy seed in adequate numbers and that too in the appropriate period. In spite of setting up several prawn hatcheries around the country to satiate the ever growing demands for the seed of the giant fresh water prawn, the supply still remains fear below the requirement mainly due to the mortality of the larvae at different stages of the larval cycle. In a larval rearing system of Macrobrachium rosenbergii, members of the family Vibrionaceae were found to be dominant flora and this was especially pronounced during the times of mortality However, to develop any sort of prophylactic and therapeutic measures, the pathogenic strains have to be segregated from the lot. This would never be possible unless they were clustered based on the principles of numerical taxonomy It is with these objectives and requirements that the present work involving phenotypic characterization of the isolates belonging to the family Vibrionaceae and working out the numerical taxonomy, determination of mole % G+C ratio, segregation of the pathogenic strains and screening antibiotics as therapeutics at times of emergency, was carried out. |
Description: | School of Environmental Studies.Cochin University of Science and Technology |
URI: | http://dyuthi.cusat.ac.in/purl/3788 |
Files | Size |
---|---|
Dyuthi-T1734.pdf | (5.966Mb) |
Abstract: | The thermal degradation of short polyester fiber reinforced polyurethane composites with and without different bonding agents has been studied by thermogravimetric analysis . It was found that degradation of the polyurethane takes place in two steps and that of the composites takes place in three steps. With the incorporation of 30 phr of fiber in the matrix , the onset of degradation was shifted from 230 to 238 ° C. The presence of bonding agents in the virgin elastomer and the composite gave an improved thermal stability . Results of kinetic studies showed that the degradation of polyurethane and the reinforced composites with and without bonding agents follows first -order reaction kinetics |
URI: | http://dyuthi.cusat.ac.in/purl/906 |