Sunil,K Narayanankutty(Technomic Publishing Co., Inc., April , 1998)
[+]
[-]
Abstract:
The stress relaxation behavior of polyurethane elastomer and
short polyester fiber filled elastomer composites with and without bonding
agents at different strain levels and strain rates was studied. It was found that
these compounds exhibit a multistage relaxation mechanism and that the rate
of relaxation and cross-over time depend on the strain level and strain rate.
The incorporation of fibers reduced the stage-I relaxation rate and increased
the cross-over time of the gum vulcanisate. A higher rate of relaxation (first
stage) was shown by the composites with longitudinal fiber orientation and
composites with bonding agents.
Sunil,K Narayanankutty(Elsevier Science Limited, May 17, 1997)
[+]
[-]
Abstract:
The thermal degradation of short polyester fiber reinforced polyurethane composites
with and without different bonding agents has been studied by thermogravimetric
analysis . It was found that degradation of the polyurethane takes
place in two steps and that of the composites takes place in three steps. With
the incorporation of 30 phr of fiber in the matrix , the onset of degradation was
shifted from 230 to 238 ° C. The presence of bonding agents in the virgin elastomer
and the composite gave an improved thermal stability . Results of kinetic studies
showed that the degradation of polyurethane and the reinforced composites with
and without bonding agents follows first -order reaction kinetics