Abstract: | Rubber ferrite composites (RFCs) containing powdered nickel zinc ferrite (Ni1 – xZnxFe2O4 ) in a natural rubber matrix have been prepared and their mechanical and dielectric properties have been evaluated. Variations in the relative permittivity of both the ferrite ceramics and RFCs have been studied over a range of frequencies, ceramic compositions, ceramic ller loadings, and temperatures, and the results have been correlated. Appropriate mixture equations have been formulated to calculate the dielectric permittivity of the composite from the dielectric permittivity of its constituents. Values calculated using these equations have been compared with experimental data on relative permittivity, and the two have been found to be in good agreement. In the present investigationit was also observed that for x=0·4 and for the maximum ferrite loading, the composite sample exhibits maximum magnetisation and optimum exibility |
Description: | Plastics, Rubber and Composites 2002 Vol. 31 No. 10,449-457 |
URI: | http://dyuthi.cusat.ac.in/purl/4395 |
Files | Size |
---|---|
Dielectric and ... ber ferrite composites.pdf | (733.2Kb) |
Abstract: | Magnetic nanocomposites containing iron oxide particles embedded in a polymer matrix have been synthesized using the method of ion exchange. They have been characterized by using low temperature and room temperature magnetic measurements and Mo¨ ssbauer spectroscopy. The iron content in these samples has also been determined. The results have been analysed and explained. The physical and chemical properties of these nanocomposite materials are different from those of the bulk. Some of the unique properties of these materials find application in information storage, color imaging, ferrofluids and magnetic refrigeration |
Description: | JOURNAL OF MATERIALS SCIENCE 36 (2001) 821– 824 |
URI: | http://dyuthi.cusat.ac.in/purl/4367 |
Files | Size |
---|---|
Effect of cycli ... ic nanocomposite based.pdf | (57.94Kb) |
Abstract: | The effect of frequency, composition and temperature on the a.c. electrical conductivity were studied for the ceramic, Ni1–xZnxFe2O4, as well as the filler (Ni1–xZnxFe2O4) incorporated rubber ferrite composites (RFCs). Ni1–xZnxFe2O4 (where x varies from 0 to 1 in steps of 0×2) were prepared by usual ceramic techniques. They were then incorporated into a butyl rubber matrix according to a specific recipe. The a.c. electrical conductivity (sa.c.) calculations were carried out by using the data available from dielectric measurements and by employing a simple relationship. The a.c. conductivity values were found to be of the order of 10–3 S/m. Analysis of the results shows that sa.c. increases with increase of frequency and the change is same for both ceramic Ni1–xZnxFe2O4 and RFCs. sa.c. increases initially with the increase of zinc content and then decreases with increase of zinc. Same behaviour is observed for RFCs too. The dependence of sa.c. on the volume fraction of the magnetic filler was also studied and it was found that the a.c. conductivity of RFCs increases with increase of volume fraction of the magnetic filler. Temperature dependence of conductivity was studied for both ceramic and rubber ferrite composites. Conductivity shows a linear dependence with temperature in the case of ceramic samples |
Description: | Bull. Mater. Sci., Vol. 25, No. 7, December 2002, pp. 599–607 |
URI: | http://dyuthi.cusat.ac.in/purl/4355 |
Files | Size |
---|---|
Evaluation of a ... ielectric measurements.pdf | (232.7Kb) |
Abstract: | Preparatiun or aci cular maghemi te containing dopan ls li ke Mg. i and Gd and their characleris,llion us ing different analytica l techniques have been reported. These in vestigat ions reveal that the addition of dopants li ke Mg. Ni and Gd modifies the magnetic properties without cfrecting any structural changes. The opt ical bandgaps of these doped compositions have ,li S() hecn determ ined. Evidence is ,li so av,li lab le from spectroscopic investi gations suggest ing thalmaghcllli te prepared vi,l the ()xa l,ltc precursor route does nm exhi bit a hydrogen fe rrite structure |
Description: | Ind ian Joum,ll of Pure & Applied Phys ics Vol. 37. November 1999. pr. 842-847 |
URI: | http://dyuthi.cusat.ac.in/purl/4435 |
Files | Size |
---|---|
Influence of do ... roperties of maghemite.pdf | (1.171Mb) |
Abstract: | Polycrystalline single phasic mixed ferrites belonging to the series Ni1−xZnxFe2O4 for various values of x have been prepared by conventional ceramic techniques. Pre-characterized nickel zinc ferrites were then incorporated into a natural rubber matrix according to a specific recipe for various loadings. The processability and cure parameters were then determined. The magnetic properties of the ceramic filler as well as the ferrite loaded rubber ferrite composites (RFC) were evaluated and compared. A general equation for predicting the magnetic properties was also formulated. The validity of these equations were then checked and correlated with the experimental data. The coercivity of the RFCs almost resemble that of the ceramic component in the RFC. Percolation threshold is not reached for a maximum loading of 120 phr (parts per hundred rubber by weight) of the filler. These studies indicate that flexible magnets can be made with appropriate magnetic properties namely saturation magnetisation (Ms) and magnetic field strength (Hc) by a judicious choice of x and a corresponding loading. These studies also suggest that there is no possible interaction between the filler and the matrix at least at the macroscopic level. The formulated equation will aid in synthesizing RFCs with predetermined magnetic |
Description: | JOURNAL OF MATERIALS SCIENCE 36 (2001) 5551 – 5557 |
URI: | http://dyuthi.cusat.ac.in/purl/4358 |
Files | Size |
---|---|
Magnetic and pr ... bber and mixed ferrite.pdf | (144.6Kb) |
Abstract: | Zinc ferrite belongs to the class of normal spinels where it is assumed to have a cation distribution of Zn2`(Fe3`)2(O2~)4, and it is purported to be showing zero net magnetisation. However, there have been recent reports suggesting that zinc ferrite exhibits anomaly in its magnetisation. Zinc ferrite samples have been prepared by two di¤erent routes and have been analysed using low energy ion scattering, Mo¬ ssbauer spectroscopy and magnetic measurements. The results indicate that zinc occupies octahedral sites, contrary to the earlier belief that zinc occupies only the tetrahedral sites in a normal spinel. The amount of zinc on the B site increases with decrease in particle size. The LEIS results together with the Mo¬ ssbauer results and the magnetic measurements lead to the conclusion that zinc occupies the B site and the magnetisation exhibited by ultraÞne particles of zinc is due to short range ordering |
Description: | Journal of Magnetism and Magnetic Materials 189 (1998) 83-88 |
URI: | http://dyuthi.cusat.ac.in/purl/4348 |
Files | Size |
---|---|
On the magnetic ... ltra-Þne zinc ferrites.pdf | (88.12Kb) |
Abstract: | The objectives of the proposed work are preparation of ceramic nickel zinc ferrite belonging to the series Ni1-XZnXFe2O4 with x varying from 0 to 1in steps of 0.2, structrural, magnetic and electrical characterization of Ni1-XZnXFe2O4, preparation and evaluation of Cure characteristics of Rubber Ferrite Composites (RFCs), magnetic characterization of RFCs using vibrating sample magnetometer (VSM), electrical characterization of RFCs and estimation of magnetostriction constant form HL parameters. The study deals with the structural and magnetic properties of ceramic fillers, variation of coercivity with composition and the variation of magnetization for different filler loadings are compared and correlated. The dielectric properties of ceramic Ni1-XZnXFe2O4 and rubber ferrite composites containing Ni1-XZnXFe2O4 were evaluated and the ac electrical conductivity (ac) of ceramic as well as composite samples can be calculated by using a simple relationship of the form ac = 2f tan 0r, with the data available from dielectric measurements. The results suggest that the ac electrical conductivity is directly proportional to the frequency |
URI: | http://dyuthi.cusat.ac.in/purl/1001 |
Files | Size |
---|---|
Dyuthi-T0206.pdf | (4.767Mb) |
Abstract: | Rubber ferrite composites containing various mixed ferrites were prepared for different compositions and various loadings. The magnetic and dielectric properties of the fillers as well as the ferrite filled matrixes were evaluated separately. The results are correlated. Simple equations are proposed to predetermine the magnetic and dielectric properties. The validity of these equations is verified and they are found to be in good agreement. These equations are useful in tailoring the magnetic and dielectric properties of these composites with predetermined properties |
Description: | Bull. Mater. Sci., Vol. 24, No. 6, December 2001, pp. 623–631 |
URI: | http://dyuthi.cusat.ac.in/purl/4361 |
Files | Size |
---|---|
Tailoring magne ... taining mixed ferrites.pdf | (198.4Kb) |
Now showing items 1-8 of 8
Dyuthi Digital Repository Copyright © 2007-2011 Cochin University of Science and Technology. Items in Dyuthi are protected by copyright, with all rights reserved, unless otherwise indicated.