Sugunan, S; Nampoori, V P N; Radhakrishnan, P; Sanjay, G; Suja, H; Lyjo, Joseph K(Elsevier, June 28, 2008)
[+]
[-]
Abstract:
Thermal diffusivity (TD) measurement on commercial K-10 and KSF montmorillonites was carried out by
photoacoustic technique. The TD of the montmorillonites after methylene blue adsorption changed with the
dye concentration. The repeatedly adsorbed samples showed a lesser TD than the single adsorbed samples.
After methylene blue adsorption the acid leached K-10 samples showed well defined changes in TD when
compared to the ordered KSF samples
Sugunan, S; Suja, H; Sanjay, G; Joseph, L K; Nampoori, V P N; Radhakrishnan, P(Taylor & Francis, April 1, 2009)
[+]
[-]
Abstract:
Thermal diffusivity (TD) measurements were performed on some industrially
important dyes – auramine O (AO), malachite green and methylene blue (MB) –
adsorbed K-10 montmorillonites using photoacoustic method. The TD value for
the dye-adsorbed clay mineral was observed to change with a variation in dye
concentration. The contribution of the dye towards TD was also determined. The
repeatedly adsorbed samples with MB and AO exhibited a lower TD than the
single-adsorbed samples. TD values of sintered MB samples were also obtained
experimentally. These sintered samples exhibit a higher TD, although they show
a trend similar to that of non-sintered pellets. A variation in dye concentration
and sintering temperature can be used for tuning the TD value of the clay mineral
to the desired level
Description:
Philosophical Magazine
Vol. 89, No. 10, 1 April 2009, 895–905
Vanadia/ceria catalysts (2–10 wt% of V2O5) were prepared by wet impregnation of ammonium metavanadate in oxalic acid solution. Structural characterization was done with energy dispersive X-ray analysis (EDX), powder X-ray diffraction (XRD), BET surface area measurements, FT-IR spectroscopy and nuclear magnetic spectral analysis (51V MASNMR). XRD and 51V MASNMR results show highly dispersed vanadia species at lower loadings and the formation of CeVO4 phase at higher V2O5 loading. The catalytic activity of catalysts was conducted in liquid phase oxidation of ethylbenzene with H2O2 as oxidant. The oxidation activity is increased with loading up to 8 wt% V2O5 and then decreased with further increase in V2O5 content to 10 wt%. Different vanadia species evidenced by various techniques were found to be selective towards ethylbenzene oxidation. The CeVO4 formation associated with increased concentration of vanadia on ceria results the production of acetophenone along with 2-hydroxyacetophenone.
Cyclohexanol decomposition activity of supported vanadia catalysts is ascribed to the high surface area, total acidity and interaction between supported vanadia and the amorphous support. Among the supported catalysts, the effect of vanadia over various wt% V2O5 (2–10) loading indicates that the catalyst comprising of 6 wt% V2O5 exhibits higher acidity and decomposition activity. Structural characterization of the catalysts has been done by techniques like energy dispersive X-ray analysis, X-ray diffraction and BET surface area. Acidity of the catalysts has been measured by temperature programmed desorption using ammonia as a probe molecule and the results have been correlated with the activity of catalysts.
Sunajadevi, K R; Sugunan, S(Elsevier, September , 2005)
[+]
[-]
Abstract:
Titania, sulfated titania and chromium loaded sulfated titania were prepared by sol–gel method and characterized using different technique. Phenol is nitrated regioselectively by nitric acid using chromium loaded sulfated titania catalysts. A remarkable ortho selectivity is observed in solid state nitration to yield exclusively ortho-nitrophenol. Compared to the conventional process, phenol nitration over solid acid catalyst is a clean and environment friendly process. Catalytic activity well correlates with the Brönsted acid sites of these catalysts.