Abstract:
|
The rheological behavior of a short-polyester-fiber-filled polyurethane
elastomer composite containing different bonding agents
has been studied in the temperature range 120-160°C and in the
shear rate range 63-608 s-'. The composite with and without
bonding agents showed a pseudoplastic behavior which decreased
with the increase of temperature. Composites containing bonding
agents based on polypropyleneglycol and 4,4'-diphenylmethanediisocyanate
showed the lowest viscosity values at a particular
shear rate, whereas composites containing a glycerol- (GL) based
bonding agent showed the highest viscosity. The viscosity of the
composite decreased sharply after a particular temperature (140°C) and the fall was less drastic in the composite containing
a GL-based bonding agent. |