| Abstract: | A new photopolymerizable recording media is introduced based on poly (vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed that this MBPVA/VAc system can be reused a number of times without significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is attractive on account of its reusability. |
| URI: | http://dyuthi.cusat.ac.in/purl/796 |
| Files | Size |
|---|---|
| Beena Mary John ... recording...,march2005.PDF | (7.043Mb) |
| Abstract: | We describe the synthesis of diblock and triblock copolymers by sequential atom transfer radical polymerization of styrene and acetoxymethylstyrene. Contrary to the usual block copolymerization involving isolation of the macroinitiator, a convenient one-pot procedure is developed. This is possible because of the preferential polymerization of acetoxymethylstyrene, even in the presence of residual styrene, as inferred from characterization of the intermediate polystyrenes and the block copolymers by size exclusion chromatography, 1H NMR, Fourier transform infrared spectroscopy, differential scanning calorimetry, and GPEC techniques. The latent acetoxy functionalities in these block copolymers are shown to be easily unmasked to OOH and OBr functionalities, with the potential for block ionomers and dense graft architectures. |
| URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1995 |
| Files | Size |
|---|---|
| Diblock and triblock....pdf | (136.8Kb) |
| Abstract: | Reactive extrusion is an attractive means of polymer processing since the shaping and reaction take place in a single operation. In this paper we report the silane grafting of polyethylenes in a single screw extruder. The optimum conditions for silane grafting, viz. temperature, shear rate, silane and DCP concentrations, were determined on a torque rheometer and then actual extrusion was performed using these conditions. The study shows that an optimum low level of grafting/ crosslinking can be introduced into polyethylene during its extrusion for better mechanical behavior and=or thermal stability without affecting the processability. |
| URI: | http://dyuthi.cusat.ac.in/xmlui/purl/1997 |
| Files | Size |
|---|---|
| Silance grafting....pdf | (386.9Kb) |
| Abstract: | Polypyrrole/poly (vinyl chloride) semi-interpenenzrtirtg networks of different compositions are prepared using anunonitun per sulfate initiator at room temperature in pellet.form and lilrrt form and their dielectric properties are studied at different microwave frequencies. An HP 8510 Vector network analyzer interfaced with a computer is used. The cavity-perturbation technique is employed for the study |
| URI: | http://dyuthi.cusat.ac.in/purl/802 |
| Files | Size |
|---|---|
| Honey John and ... dielectric...,Dec2005.PDF | (2.487Mb) |
| Abstract: | Natural rubber/isora fibre composites were cured at various temperatures. The solvent swelling characteristics of natural rubber composites containing both untreated and alkali treated fibres were investigated in aromatic and aliphatic solvents like toluene, and n-hexane. The diffusion experiments were conducted by the sorption gravimetric method. The restrictions on elastomer swelling exerted by isora fibre as well as the anisotropy of swelling of the composite have been confirmed by this study. Composite cured at 100°C shows the lowest percentage swelling. The uptake of aromatic solvent is higher than that of aliphatic solvent for the composites cured at all temperatures. The effect of fibre loading on the swelling behaviour of the composite was also investigated in oils like petrol, diesel, lubricating oil etc. The % swelling index and swelling coefficient of the composite were found to decrease with increase in fibre loading. This is due to the increased hindrance exerted by the fibres at higher fibre loadings and also due to the good fibre-rubber interactions. Maximum uptake of solvent was observed with petrol followed by diesel and then lubricating oil. The presence of bonding agent in the composites restrict the swelling considerably due to the strong interfacial adhesion. At a fixed fibre loading, the alkali treated fibre composite showed lower percentage swelling compared to the untreated one. |
| URI: | http://dyuthi.cusat.ac.in/purl/807 |
| Files | Size |
|---|---|
| Lovely Mathew a ... g behavior..,Sept.2005.PDF | (6.644Mb) |
| Abstract: | Isora fibre-reinforced natural rubber (NR) composites were cured at 80, 100, 120 and 150°C using a low temperature curing accelerator system. Composites were also prepared using a conventional accelerator system and cured at 150°C. The swelling behavior of these composites at varying fibre loadings was studied in toluene and hexane. Results show that the uptake of solvent and volume fraction of rubber due to swelling was lower for the low temperature cured vulcanizates which is an indication of the better fibre/rubber adhesion. The uptake of aromatic solvent was higher than that of aliphatic solvent, for all the composites. As the fibre content increased, the solvent uptake decreased, due to the superior solvent resistance of the fibre and good fibre-rubber interactions. The bonding agent improved the swelling resistance of the composites due to the strong interfacial adhesion. Due to the improved adhesion between the fibre and rubber, the ratio of the change in volume fraction of rubber due to swelling to the volume fraction of rubber in the dry sample (V,) was found to decrease in the presence of bonding agent. At a fixed fibre loading, the alkali treated fibre composite showed a lower percentage swelling than untreated one for both systems showing superior rubber-fibre interactions. |
| URI: | http://dyuthi.cusat.ac.in/purl/806 |
| Files | Size |
|---|---|
| Lovely Mathew a ... of curing...,July2005.PDF | (6.828Mb) |
| Abstract: | The thermal degradation of short nylon-6 fiber reinforced acrylonitrile butadiene rubber (NBR) composites with and without epoxy-based bonding agent has been studied by thermogravimetric analysis (TGA). It was found that the onset of degradation shifted from 330.5 to 336.1°C in the presence of short nylon fiber, the optimum fiber loading being 20 phr. The maximum rate of degradation of the composites was lower than that of the unfilled rubber compound, and it decreased with increase in fiber concentration. The presence of epoxy resin-based bonding agent in the virgin elastomer and the composites improved the thermal stability. Results of kinetic studies showed that the degradation of NBR and the short nylon fiber reinforced composites followed first-order kinetics. |
| URI: | http://dyuthi.cusat.ac.in/purl/892 |
| Files | Size |
|---|---|
| SEEMA, A, S. K. ... ORT NYLON-6 FIBRE......PDF | (3.742Mb) |
| Abstract: | The rheological characteristics of short Nylon-6 fiber reinforced styrene butadiene rubber (SBR) were studied using a capillary rheometer. The study was done with respect to the effect of shear rate, fiber concentration, and temperature on shear viscosity and die swell. All the melts showed pseudoplastic nature, which decreased with increasing temperature. Shear viscosity increased in the presence of fibers. Introduction of fiber reduces the temperature sensitivity of the rubber matrix. A reduction in die swell was found in presence of fibers. |
| URI: | http://dyuthi.cusat.ac.in/purl/894 |
| Files | Size |
|---|---|
| SEEMA, A, S. K. ... REINFORCED............PDF | (6.615Mb) |
| Abstract: | The mechanism of devulcanization of sulfur-vulcanized natural rubber with aromatic disulfides and aliphatic amines has been studied using 23-dimethyl-2-butene (C5H1,) as a low-molecular weight model compound. First C6H12 was vulcanized with a mixture of sulfur, zinc stearate and N-cyclohexyl-2-benzothiazylsulfenamide (CBS) as accelerator at 140 °C, resulting in a mixture of addition products (C(,H 1 i-S,-C5H 1 i ). The compounds were isolated and identified by High Performance Liquid Chromatography (HPLC) with respect to their various sulfur ranks. In it second stage, the vulcanized products were devulcanized using the agents mentioned above at 200 °C. The kinetics and chemistry of the breakdown of the sulfur-hridges were monitored. Both devulcanization agents decompose sulfidic vulcanization products with sulfur ranks equal or higher than 3 quite effectively and with comparable speed. Di phenyldisulfide as devulcanization agent gives rise to a high amount of mono- and disulfidic compounds formed during the devulcanization, hexadecylamine, as devulcanization agent, prevents these lower sulfur ranks from being formed. |
| URI: | http://dyuthi.cusat.ac.in/purl/819 |
| Files | Size |
|---|---|
| V V Rajan and others,Mdel compound studies....PDF | (9.175Mb) |
| Abstract: | Latex waste like glove waste was effectively modified using a new reclaiming agent, thiocarbanilide. This modified waste was blended with linear low-density polyethylene (LLDPE) to develop a novel thermoplastic elastomer. Both uncrosslinked and dynamically crosslinked blends were prepared and their properties were studied. The results were found to be comparable to those of conventional thermoplastic elastomers. |
| URI: | http://dyuthi.cusat.ac.in/purl/810 |
| Files | Size |
|---|---|
| S Rajalekshmi and Rani Joseph,studies on...PDF | (7.257Mb) |