Dielectric properties of polyaniline at different frequencies were studied. Cavity perturbation technique was employed for the
study. Poly aniline in the powder and pelletised forms were prepared under different environmental conditions. Different samples of
poly aniline exhibit high conductivity. However, the conductivity of samples prepared under different environmental conditions is
found to vary. All the samples in the powder form have high conductivity irrespective of the method of preparation. The high
conductivity at microwave frequency makes it possible to be used for developing microwave components like filters.
A novel method of blending natural rubber with polyvinylchloride in the latex
stage was developed, Dioctyl phthalate (DOP) and Amine terminated natural rubber
(ATNR) were used as plasticisers, for improving the mechanical properties of
these blends. Properties of the latex stage blends were compared with those of
dry blends. Latex stage blends showed superior mechanical properties compared
to the blends prepared in the dry state. The ageing resistance, oil resistance and
processability were found to be improved by latex stage blending.
Sunil K Narayanankutty(John Wiley & Sons. Inc., June 21, 2001)
[+]
[-]
Abstract:
The effect of diphenylmethane diisocyanate
(MDI) -polyethyleneglycol (PEG) resin on the cure characteristics and mechanical
properties of nitrile rubber/whole tyre eclaim-short nylon fiber
composite-was studied. At a constant loading of 5 phr, the resin composition
was varied. The minimum torque .,id (maximum - minimum) torque increased
with isocyanate concentration. Scorch time and cure time showed a reduction on
introduction of bonding agent. Properties like tensile strength, tear strength, and
abrasion resistance increased with increase in MDI/PEG ratio, and these
properties are higher in the longitudinal direction of fiber orientation.
Compression set increased with isocyanate concentration and the resilience
remain unchanged.
Sunil K Narayanankutty(Taylor & Francis Inc., March 26, 2001)
[+]
[-]
Abstract:
Cure characteristics and mechanical properties of styrene butadiene rubber
reclaimed rubber blends were studied. The blends showed improved processability,
as indicated by the minimum torque values. Cure characteristics like minimum
torque, (maximum-minimum) torque, cure time and cure rate decreased in the
presence of reclaimed rubber. Tensile strength, tear strength, elongation at break
were higher for blends. Resilience decreased with reclaim content. Compression set
and abrasion loss were higher in the blends.
Rani, Joseph(John Wiley & Sons, Inc., June 21, 2001)
[+]
[-]
Abstract:
ABSTRACT: Polyaniline was synthesized by using ammonium persulfate initiator in the
presence of 1M HC1. It was dried under different drying conditions like room temperature
drying (for 48 h), oven drying (at 50-60°C for 8 h under a vacuum), and vacuum
drying (at room temperature for 16 h). The conductivities of these samples were
measured at microwave frequencies. These samples were also pelletized and the
measurements were repeated. The cavity perturbation technique was used for the
study.
Rani, Joseph(Optical Society of America, October 29, 2001)
[+]
[-]
Abstract:
A new polymer matrix sensitized with methylene blue for use as an optical recording material is described
here. The characterization is done to determine the optimal recording conditions. These films need no
chemical development and are found to be stable for several months. The matrix has excellent shelf life
and needs an exposure only as short as 20 s. Direct imaging was done on this material.