Sudha Kartha,C(American Institute of Physics., January 13, 2007)
[+]
[-]
Abstract:
Poly(methyl)methacrylate was made photoconducting by molecular doping and the
photoconductivity was investigated using modulated photocurrent technique . Low-temperature
current-voltage measurements showed that the transport mechanism was thermally activated
hopping. An experimental investigation of the photoconductivity action spectrum along with
theoretical calculation enabled an estimation of the diffusion coefficient of the material. The
presence of states with a distribution of lifetimes could be understood from the frequency response
of the photocurrent . The photocurrent was due to the field-assisted dissociation of these states.
Sudha Kartha,C(Taylor and francis, March 13, 2005)
[+]
[-]
Abstract:
A new photopolymerizable recording media is introduced based on poly
(vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed
that this MBPVA/VAc system can be reused a number of times without
significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized
at 2:1. Diffraction efficiency of 6.3% was obtained without any fixing at a dye
concentration of 9.3 10 4 mol/l at an exposure of 750 mJ/cm2. The material is
attractive on account of its reusability.
A new photopolymerizable recording media is introduced based on poly
(vinyl alcohol) and vinyl acetate sensitized with methylene blue. It is observed
that this MBPVA/VAc system can be reused a number of times without
significant decrease in diffraction efficiency. The PVA-VAc ratio was optimized
at 2:1. Diffraction efcienc4y of 6.3% was obtained without any fixing at a dye
concentration of 9.3 x 10- mol/l at an exposure of 750mJ/cm2. The material is
attractive on account of its reusability.