Sudha Kartha,C(Indian academy of science, February 24, 2003)
[+]
[-]
Abstract:
Significant results of our experimental investigations on the dependence of pH on real time
transmission characteristics on recording media fabricated by doping PVC with complexed methylene blue
are presented. The optimum pH value for faster bleaching was found to be 4×5. In typical applications, the
illumination from one side, normal to the surface of this material, initiates a chemical sequence that records
the incident light pattern in the polymer. Thus direct imaging can be successfully done on this sample. The
recorded letters were very legible with good contrast and no scattering centres. Diffraction efficiency
measurements were also carried out on this material.
Sudha Kartha,C(Taylor and francis, October 20, 2003)
[+]
[-]
Abstract:
Polymer materials find application in optical storage technology,
namely in the development of high information density and fast access type
memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol
(PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized
and its comparison with methylene blue sensitized PVA in methanol and
complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented.
The optical absorption spectra of the thin films of these polymers
showed a strong and broad absorption region at 670-650 nm, matching the
wavelength of the laser used. A very slow recovery of the dye on irradiation was
observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8
and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction
efficiency of up to 20% was observed for the MBPVA/alcohol system and an
energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films
with a spatial frequency of 588 lines/mm.