| Abstract: | The present work derives motivation from the so called surface/interfacial magnetism in core shell structures and commercial samples of Fe3O4 and c Fe2O3 with sizes ranging from 20 to 30 nm were coated with polyaniline using plasma polymerization and studied. The High Resolution Transmission Electron Microscopy images indicate a core shell structure after polyaniline coating and exhibited an increase in saturation magnetization by 2 emu/g. For confirmation, plasma polymerization was performed on maghemite nanoparticles which also exhibited an increase in saturation magnetization. This enhanced magnetization is rather surprising and the reason is found to be an interfacial phenomenon resulting from a contact potential. |
| Description: | Appl. Phys. Lett. 103, 162414 (2013) |
| URI: | http://dyuthi.cusat.ac.in/purl/4422 |
| Files | Size |
|---|---|
| Contact potenti ... plasma polymerization.pdf | (1.752Mb) |
| Abstract: | Superparamagnetic nanocomposites based on g-Fe2O3 and sulphonated polystyrene have been synthesized by ion exchange process and the preparation conditions were optimized. Samples were subjected to cycling to study the effect of cycling on the magnetic properties of these composites. The structural and magnetization studies have been carried out. Magnetization studies show the dependence of magnetization on the number of ion exchange cycles. Doping of cobalt at the range in to the g-Fe2O3 lattice was effected in situ and the doping was varied in the atomic percentage range 1–10. The exact amount of cobalt dopant as well as the iron content was estimated by Atomic Absorption Spectroscopy. The effect of cobalt in modifying the properties of the composites was then studied and the results indicate that the coercivity can be tuned by the amount of cobalt in the composites. The tuning of both the magnetization and the coercivity can be achieved by a combination of cycling of ion exchange and the incorporation of cobalt |
| Description: | Journal of Magnetism and Magnetic Materials 283 (2004) 344–352 |
| URI: | http://dyuthi.cusat.ac.in/purl/4383 |
| Files | Size |
|---|---|
| Effect of cobal ... styrene nanocomposites.pdf | (177.9Kb) |
| Abstract: | Ferrofluids belonging to the series NixFe1 xFe2O4 were synthesised by two different procedures—one by standard co-precipitation techniques, the other by co-precipitation for synthesis of particles and dispersion aided by high-energy ball milling with a view to understand the effect of strain and size anisotropy on the magneto-optical properties of ferrofluids. The birefringence measurements were carried out using a standard ellipsometer. The birefringence signal obtained for chemically synthesised samples was satisfactorily fitted to the standard second Langevin function. The ball-milled ferrofluids showed a deviation and their birefringence was enhanced by an order. This large enhancement in the birefringence value cannot be attributed to the increase in grain size of the samples, considering that the grain sizes of sample synthesised by both modes are comparable; instead, it can be attributed to the lattice strain-induced shape anisotropy(oblation) arising from the high-energy ball-milling process. Thus magnetic-optical (MO) signals can be tuned by ball-milling process, which can find potential applications |
| Description: | Journal of Magnetism and Magnetic Materials 320 (2008) 815–820 |
| URI: | http://dyuthi.cusat.ac.in/purl/4433 |
| Files | Size |
|---|---|
| Enhanced shape ... birefringence by high.pdf | (285.7Kb) |
| Abstract: | Ferrofluids belonging to the series NixFe1 xFe2O4 were synthesised by two different procedures—one by standard co-precipitation techniques, the other by co-precipitation for synthesis of particles and dispersion aided by high-energy ball milling with a view to understand the effect of strain and size anisotropy on the magneto-optical properties of ferrofluids. The birefringence measurements were carried out using a standard ellipsometer. The birefringence signal obtained for chemically synthesised samples was satisfactorily fitted to the standard second Langevin function. The ball-milled ferrofluids showed a deviation and their birefringence was enhanced by an order. This large enhancement in the birefringence value cannot be attributed to the increase in grain size of the samples, considering that the grain sizes of sample synthesised by both modes are comparable; instead, it can be attributed to the lattice strain-induced shape anisotropy(oblation) arising from the high-energy ball-milling process. Thus magnetic-optical (MO) signals can be tuned by ball-milling process, which can find potential applications. |
| URI: | http://dyuthi.cusat.ac.in/purl/2831 |
| Files | Size |
|---|---|
| Dyuthi-P00387.pdf | (291.1Kb) |
| Abstract: | Superparamagnetic nanocomposites based on Y-Fe2O3 and sulphonated polystyrene were synthesised by ion-exchange process and the structural characterisation has been carried out using X-ray diffraction technique. Doping of cobalt in to the Y-Fe2O3 lattice was effected in situ and the doping was varied in the atomic percentage range 1–10. The optical absorption studies show a band gap of 2.84 eV, which is blue shifted by 0.64 eV when compared to the reported values for the bulk samples (2.2 eV). This is explained on the basis of weak quantum confinement. Further size reduction can result in a strong confinement, which can yield transparent magnetic nanocomposites because of further blue shifting. The band gap gets red shifted further with the addition of cobalt in the lattice and this red shift increases with the increase in doping. The observed red shift can be attributed to the strain in the lattice caused by the anisotropy induced by the addition of cobalt. Thus, tuning of bandgap and blue shifting is aided by weak exciton confinement and further red shifting of the bandgap is assisted by cobalt doping. |
| URI: | http://dyuthi.cusat.ac.in/purl/2836 |
| Files | Size |
|---|---|
| Dyuthi-P00392.pdf | (199.0Kb) |
| Abstract: | Ferrofluids belonging to the series, Ni x Fe1-x Fe2O4 and Zn x Fe1-x Fe2O4, were synthesized using cold co-precipitation. Liquid films of these ferrofluids were prepared by encapsulating the ferrofluids in between two optically smooth and ultrasonically cleaned glass plates. Magnetic field induced laser transmission through these ferrofluid films has been investigated. Magnetic field values can be calibrated in terms of output laser power in the low field region in which the variation is linear. This set up can be used as a cheap optical gaussmeter in the low field regime. Using the same set-up, the saturation magnetization of the sample used can also be calculated with a sample that is pre-characterized. Hence both magnetization of the sample, as well as applied magnetic field can be sensed and calculated with a precalibrated sample. |
| URI: | http://dyuthi.cusat.ac.in/purl/2844 |
| Files | Size |
|---|---|
| Dyuthi-P00397.pdf | (176.9Kb) |
| Abstract: | Fine particles of cobalt ferrite were synthesized by the sol–gel method. Subsequent heat treatment at different temperatures yielded cobalt ferrites having different grain sizes. X-ray diffraction studies were carried out to elucidate the structure of all the samples. Dielectric permittivity and ac conductivity of all the samples were evaluated as a function of frequency, temperature and grain size. The variation of permittivity and ac conductivity with frequency reveals that the dispersion is due to Maxwell–Wagner type interfacial polarization in general, with a noted variation from the expected behaviour for the cold synthesized samples. High permittivity and conductivity for small grains were explained on the basis of the correlated barrier-hopping model |
| Description: | J. Phys. D: Appl. Phys. 40 (2007) 1593–1602 |
| URI: | http://dyuthi.cusat.ac.in/purl/4350 |
| Files | Size |
|---|---|
| Finite size eff ... e polarization effects.pdf | (975.7Kb) |
| Abstract: | Nanoparticles of nickel ferrite have been synthesized by the sol–gel method and the effect of grain size on its structural and magnetic properties have been studied in detail. X-ray diffraction (XRD) studies revealed that all the samples are single phasic possessing the inverse spinel structure. Grain size of the sol–gel synthesized powders has been determined from the XRD data and the strain graph. A grain size of 9 nm was observed for the as prepared powders of NiFe2O4 obtained through the sol–gel method. It was also observed that strain was induced during the firing process. Magnetization measurements have been carried out on all the samples prepared in the present series. It was found that the specific magnetization of the nanosized NiFe2O4 powders was lower than that of the corresponding coarse-grained counterparts and decreased with a decrease in grain size. The coercivity of the sol–gel synthesized NiFe2O4 nanoparticles attained a maximum value when the grain size was 15nm and then decreased as the grain size was increased further. |
| Description: | Journal of Magnetism and Magnetic Materials 302 (2006) 190–195 |
| URI: | http://dyuthi.cusat.ac.in/purl/4347 |
| Files | Size |
|---|---|
| Finite size eff ... esized NiFe2O4 powders.pdf | (265.1Kb) |
| Abstract: | Commercial samples of Magnetite with size ranging from 25–30nm were coated with polyaniline by using radio frequency plasma polymerization to achieve a core shell structure of magnetic nanoparticle (core)–Polyaniline (shell). High resolution transmission electron microscopy images confirm the core shell architecture of polyaniline coated iron oxide. The dielectric properties of the material were studied before and after plasma treatment. The polymer coated magnetite particles exhibited a large dielectric permittivity with respect to uncoated samples. The dielectric behavior was modeled using a Maxwell–Wagner capacitor model. A plausible mechanism for the enhancement of dielectric permittivity is proposed |
| Description: | Applied Physics Letters 104, 121603 (2014) |
| URI: | http://dyuthi.cusat.ac.in/purl/4421 |
| Files | Size |
|---|---|
| Large enhanced ... plasma polymerization.pdf | (1.105Mb) |
| Abstract: | Lead free magneto electrics with a strong sub resonant (broad frequency range) magneto electric coupling coefficient (MECC) is the goal of the day which can revolutionise the microelectronics and microelectromechanical systems (MEMS) industry. We report giant resonant MECC in lead free nanograined Barium Titanate–CoFe (Alloy)-Barium Titanate [BTO-CoFe-BTO] sandwiched thin films. The resonant MECC values obtained here are the highest values recorded in thin films/ multilayers. Sub-resonant MECC values are quite comparable to the highest MECC reported in 2-2 layered structures. MECC got enhanced by two orders at a low frequency resonance. The results show the potential of these thin films for transducer, magnetic field assisted energy harvesters, switching devices, and storage applications. Some possible device integration techniques are also discussed |
| Description: | JOURNAL OF APPLIED PHYSICS 114, 064309 (2013) |
| URI: | http://dyuthi.cusat.ac.in/purl/4430 |
| Files | Size |
|---|---|
| Lead free heter ... l systems applications.pdf | (2.457Mb) |
| Abstract: | Fine magnetic particles (sizeffi100A ˚ ) belonging to the series ZnxFe1 xFe2O4 were synthesized by cold co-precipitation methods and their structural properties were evaluated using X-ray diffraction. Magnetization studies have been carried out using vibrating sample magnetometry (VSM) showing near-zero loss loop characteristics. Ferrofluids were then prepared employing these fine magnetic powders using oleic acid as surfactant and kerosene as carrier liquid by modifying the usually reported synthesis technique in order to induce anisotropy and enhance the magneto-optical signals. Liquid thin films of these fluids were prepared and field-induced laser transmission through these films was studied. The transmitted light intensity decreases at the centre with applied magnetic field in a linear fashion when subjected to low magnetic fields and saturate at higher fields. This is in accordance with the saturation in cluster formation. The pattern exhibited by these films in the presence of different magnetic fields was observed with the help of a CCD camera and was recorded photographically |
| Description: | Journal of Magnetism and Magnetic Materials 305 (2006) 28–34 |
| URI: | http://dyuthi.cusat.ac.in/purl/4403 |
| Files | Size |
|---|---|
| Magnetic field- ... ubstituted ferrofluids.pdf | (290.9Kb) |
| Abstract: | We report an optical limiter based on ferrofluids which has a very high shelf life and remarkable thermal stability, which are important requirements for sustainable use with intense lasers. The colloidal suspensions contain nanosized particles of approximately 80 Å diameter, with a number density of the order of 1022 /m3. The nonlinear optical transmission of the samples is studied using nanosecond and femtosecond laser pulses. Excited state absorption phenomena contribute to enhanced limiting in the nanosecond excitation regime. An advantageous feature of ferrofluids in terms of device applications is that their optical properties are controllable by an external magnetic field. |
| Description: | Appl. Phys. Lett. 92, 171908 2008 |
| URI: | http://dyuthi.cusat.ac.in/purl/4357 |
| Files | Size |
|---|---|
| An optical limiter based on ferrofluids.pdf | (316.9Kb) |
| Abstract: | Fine particles of lithium ferrite were synthesized by the sol-gel method. By subsequent heat treatment at different temperatures, lithium ferrites of different grain sizes were prepared. A structural characterization of all the samples was conducted by the x-ray diffraction technique. A grain size of around 12 nm was observed for Li0.5Fe2.5O4 obtained through the sol-gel method. Magnetic properties of lithium ferrite nanoparticles with grain size ranging from 12 to 32 nm were studied. Magnetization measurements showed that Li0.5Fe2.5O4 fine particles exhibit a deviation from the predicted magnetic behaviour. The as-prepared sample of lithium ferrite showed a maximum saturation magnetization of 75 emu g−1. Variation of coercivity is attributed to the transition from multi-domain to single domain nature. Dielectric permittivity and ac conductivity of all the samples were evaluated as a function of frequency, temperature and grain size. Variation of permittivity and ac conductivity with frequency reveals that the dispersion is due to the Maxwell–Wagner type interfacial polarization |
| Description: | J. Phys. D: Appl. Phys. 39 (2006) 900–910 |
| URI: | http://dyuthi.cusat.ac.in/purl/4349 |
| Files | Size |
|---|---|
| Structural, mag ... Fe2.5O4 fine particles.pdf | (665.9Kb) |
Now showing items 1-13 of 13