ABSTRACT: The rheological and extrudate behaviour of natural rubber/latex
reclaim blends were evaluated using a capillary viscometer . The study shows
that the viscosity of natural rubber decreases marginally on the addition of
latex reclaim while the variation of viscosity with shear rate is not affected.
The temperature sensitivity of the blends is not affected significantly with the
addition of latex reclaim . The extrudates of natural rubber/latex reclaim
blends are smooth up to the addition of about 50 wt. percent latex reclaim in
filled natural rubber compounds.
Paraphenylenediamine and diphenylamine were chemically
attached to natural rubber during mastication . The rubber bound antioxidants
were characterized by TLC, 'H-NMR, IR and TGA. The efficiency and
permenance of these bound antioxidants were compared with a conventional
amine type antioxidant in filled natural rubber vulcanizates . The rubber
bound antioxidants were found to be less volatile and less extractable as compared
to conventional antioxidants. The vulcanizates showed improved ageing
resistance as compared to vulcanizates containing conventional antioxidants.
This semisolid rubber bound antioxidant can reduce the amount of plasticizer
required for compounding.
Para-phenylenediamine (PD) was chemically attached to depolymerized natural rubber by
a photochemical reaction . The rubber bound PD was characterized by TLC, 1H-NMR, IR,
and TGA. The efficiency and permanence of the bound PD were compared with conventional
antioxidants in NBR vulcanizates . The rubber bound PD was found to be less volatile and
more resistant to water and oil extraction . The vulcanizates showed improved aging resistance
in comparison to vulcanizates containing conventional antioxidants. The liquid rubber
bound antioxidant reduces the amount of plasticizer required for compounding
Rani, Joseph(OPA (Overseas Publishers Association), May 28, 1995)
[+]
[-]
Abstract:
Amine Terminated Liquid Natural Rubber (ATNR) was used as a plasticiser in filled NR and NBR
compounds replacing oil/DOP. The scorch time and cure time were found to be lowered when ATNR
was used as the plasticiser. ATNR was found to improve the mechanical properties like tensile strength,
tear strength and modulus of the vulcanizates . The ageing resistance of the vulcanizates containing ATNR
was superior compared to the vulcanizates containing oil/DOP.
Sankara Raman, S; Nampoori, V P N; Vallabhan, C P G; Ambadas, G; Sugunan, S(American Institute of Physics, 1995)
[+]
[-]
Abstract:
The thermal diffusivity of y-alumina is determined by the photoacoustic method. The method is
calibrated by determining the thermal diffusivity of copper and aluminum. The effect of the
chemisorbed hydroxyl groups or thermal diffusivity is studied by degassing the sample at different
temperatures.
Sugunan, S; Thomas, B(American Chemical Society, 1995)
[+]
[-]
Abstract:
The Setschenow parameter and thermodynamic parameters of transfer of 2- and 4-aminobenzoic acids
from water to salt solutions have been reported. The results are discussed in terms of the structure- breaking
effects of the ions of the salts, the localized hydrolysis model, and the internal pressure theory.
Sugunan, S; Ramankutty, C G(American Chemical Society, 1995)
[+]
[-]
Abstract:
The enthalpies of formation of charge-transfer complexes of benzene, chlorobenzene, and 1,3-dichlorobenzene
as donors with 7,7,8,8-tetracyanoquinodimethane as acceptor were determined. The thermochemical
data show an increased stability of charge-transfer complexes of donors with permanent dipole moment.
The results confirm the importance of electrostatic forces in bonding and stabilizing weak complexes.
The approximate formation constants of the complexes are also reported.
Sugunan, S; Jalaja, J M(Indian Journal of Chemistry, March , 1995)
[+]
[-]
Abstract:
The electron donating properties of Ce02 and its mixed
oxides with alumina have been determined from the studies
of adsorption of electron acceptors of various electron
affinities on the surface of these oxides. The catalytic
activity of these oxides towards some reactions such as
oxidation of alcohols and reduction of ketones have been
Correlated with their surface electrondonor properties. The
surface acidity/basicity of these oxides have also been
determined by titration method using a set of Hammett
indicators.
The electron-donor properties of Sm2O3 activated at 300, 500, and 800°C are reported from studies on the adsorption of electron acceptors of various electron affinities (electron affinity values in eV are given in parentheses): 7,7,8,8-tetracyanoquino-dimethane (2.84), 2,3,5,6-tetrachloro-1,4-benzoquinone (2.40), p-dinitrobenzene (1.77), and m-dinitrobenzene (1.26) in acetonitrile and 1,4-dioxane. The extent of electron transfer during the adsorption was determined from magnetic measurements. The acid-base properties of Sm2O3 at different activation temperatures are reported using a set of Hammett indicators. Electron donor-acceptor interactions at interfaces are important in elucidating the adhesion forces.