Sunil,K Narayanankutty(Sage Publications, April , 2002)
[+]
[-]
Abstract:
Acrylonitrile butadiene rubber (NBR) matrix was reinforced with
different levels of short nylon fiber loading. Cure characteristics and mechanical
properties of composites in longitudinal and transverse directions have been
studied. Cure time was reduced while processability, as indicated by the
minimum torque, was marginally reduced with increase in fiber loading. Tensile
and tear properties improved with fiber concentration and the values were
higher in longitudinal direction of fiber orientation. Abrasion resistance,
resilience and compression set were increased in presence of fibers. Elongation
at break values showed a drastic drop on introduction of fibers. Heat build up
was higher for composites.
The cure characteristics of short fiber-polyurethane elastomer
were studied with respect to different fiber-matrix bonding agents. A hexamethylenetetramine-
resorcinol -hydrated silica based bonding agent was found to affect
the stability of the composite. A new bonding agent, TP resin, based on polymeric
toluenediisocyanate and polypropylene glycol has been developed. Cure characteristics
of the composite with and without TP resin at different fiber loadings were
also compared. Minimum torque, scorch time and optimum cure time increased
with fiber content. Maximum torque was consistently higher with TP resin at all
fiber loadings.
Rani, Joseph(OPA (Overseas Publishers Association), May 28, 1995)
[+]
[-]
Abstract:
Amine Terminated Liquid Natural Rubber (ATNR) was used as a plasticiser in filled NR and NBR
compounds replacing oil/DOP. The scorch time and cure time were found to be lowered when ATNR
was used as the plasticiser. ATNR was found to improve the mechanical properties like tensile strength,
tear strength and modulus of the vulcanizates . The ageing resistance of the vulcanizates containing ATNR
was superior compared to the vulcanizates containing oil/DOP.