Sankara Raman, S; Nampoori, V P N; Vallabhan, C P G; Ambadas, G; Sugunan, S(American Institute of Physics, February 1, 1999)
[+]
[-]
Abstract:
The effect of the chemisorbed hydroxyl groups on the thermal diffusivity of gama alumina is determined
by evaluating the thermal diffusivity at various degassing temperatures and by doping it with rare
earth oxide using photoacoustic technique. The thermal diffusivity is found to decrease with the
increase in degassing temperature as well as with the increase in the doping concentration of rare
earth oxide. This decrease has been attributed to the loss of hydroxyl ion from the y-Al2O3.
Radhakrishnan, P; Girijavallabhan, C P; Nibu, A George; Aneeshkumar, B(Journal of Physics D : Applied Physics, April 7, 1999)
[+]
[-]
Abstract:
The photobleaching of the lasing dye Rhodamine 6G embedded in the solid
matrix poly(methyl methacrylate) was investigated using a photoacoustic technique.
Chopped laser radiation from an argon ion laser at four different wavelengths was used for
the study. Experimental results indicate that the photobleaching rate is directly proportional
to the incident laser power while it decreases with increase in concentration of the dye
molecules. In the present case we have not observed any dependence of photobleaching on
the chopping frequency. One-photon absorption is found to be responsible for the
photobleaching of the dye within the selected range of laser power.
Girijavallabhan, C P; Radhakrishnan, P; Nibu, A George; Aneeshkumar, B(Journal of Physics D : Applied Physics, April 7, 1999)
[+]
[-]
Abstract:
The photobleaching of the lasing dye Rhodamine 6G embedded in the solid
matrix poly(methyl methacrylate) was investigated using a photoacoustic technique.
Chopped laser radiation from an argon ion laser at four different wavelengths was used for
the study. Experimental results indicate that the photobleaching rate is directly proportional
to the incident laser power while it decreases with increase in concentration of the dye
molecules. In the present case we have not observed any dependence of photobleaching on
the chopping frequency. One-photon absorption is found to be responsible for the
photobleaching of the dye within the selected range of laser power
Annieta, Philip K; Lyjo, Joseph K; Litty, Mathew Irimpan; Radhakrishnan, P; Nampoori, V P N(IOP, 2005)
[+]
[-]
Abstract:
The photosensitivity of dye mixture-doped polymethyl methacrylate (PMMA) films are investigated as a function of laser power, concentration of the dyes, modulation frequency and the irradiation wavelength. Energy transfer from a donor molecule to an acceptor molecule affects the emission output of the dye mixture system. Photosensitivity is found to change with changes in donor–acceptor concentrations. PMMA samples doped with the dye mixture are found to be more photosensitive when the dyes are mixed in the same proportion.
Sajan, D George; Aji, A Anapara; Warrier, P R S; Warrier, K G K; Radhakrishnan, P; Nampoori, V P N; Vallabhan, C P G(Elsevier, September , 2008)
[+]
[-]
Abstract:
Laser-induced nondestructive photoacoustic (PA) technique has been employed to determine the thermal diffusivity of nanometal (Ag) dispersed ceramic alumina matrix sintered at different temperatures. The thermal diffusivity values are evaluated by knowing the transition frequency from the amplitude spectrum of PA signal using the one-dimensional heat flow model of Rosencwaig and Gersho. Analysis of the data shows that heat transport and hence the thermal diffusivity value is greatly affected by the influence of incorporation of foreign atom. It is also seen that sintering temperature affects the thermal diffusivity value in a substantial manner. The results are interpreted in terms of variation in porosity and carrier-assisted heat transport mechanism in nanometal dispersed ceramics.
Sajan, D George; Rajesh, K; Warrier, K G K; Radhakrishnan, P; Nampoori, V P N; Vallabhan, C P G(October 29, 2011)
[+]
[-]
Abstract:
The laser induced non-destructive photoacoustic technique has been employed
to measure the thermal diffusivity of lanthanum phosphate ceramics prepared
by the sol–gel route. The thermal diffusivity value was evaluated by knowing
the transition frequency between the thermally thin to thermally thick region
from the log–log plot of photoacoustic amplitude versus chopping frequency.
Analysis of the data was carried out on the basis of the one-dimensional
model of Rosencwaig and Gersho. The present investigation reveals that the
sintering temperature has great influence on the propagation of heat carriers
and hence on the thermal diffusivity value. The results were interpreted
in terms of variations in porosity with sintering temperature as well as with
changes in grain size.
Rani, Joseph(American Institute of Physics, January 13, 2007)
[+]
[-]
Abstract:
Poly(methyl)methacrylate was made photoconducting by molecular doping and the
photoconductivity was investigated using modulated photocurrent technique . Low-temperature
current-voltage measurements showed that the transport mechanism was thermally activated
hopping. An experimental investigation of the photoconductivity action spectrum along with
theoretical calculation enabled an estimation of the diffusion coefficient of the material. The
presence of states with a distribution of lifetimes could be understood from the frequency response
of the photocurrent . The photocurrent was due to the field-assisted dissociation of these states
Sudha Kartha, C(American Institute of Physics., January 13, 2007)
[+]
[-]
Abstract:
Poly(methyl)methacrylate was made photoconducting by molecular doping and the
photoconductivity was investigated using modulated photocurrent technique . Low-temperature
current-voltage measurements showed that the transport mechanism was thermally activated
hopping. An experimental investigation of the photoconductivity action spectrum along with
theoretical calculation enabled an estimation of the diffusion coefficient of the material. The
presence of states with a distribution of lifetimes could be understood from the frequency response
of the photocurrent . The photocurrent was due to the field-assisted dissociation of these states.
The heterogeneous photocatalytic degradation of methylorange over TiO2 is studied
and is found to be cost effective. Effect of Zirconium metal incorporation over titania system is investigated. Photocatalytic degradation of methylorange using solar radiation is
found to be highly economical when compared with the processes using artificial UV
radiation, which require substantial electrical power input. The characterization of titania as
well as modified zirconium metal doped titania systems are done using XRD, FTIR and
EDAX measurements. The catalytic activities of different systems are also compared and is
tried to correlate with the crystallite size and presence of dopant metal.
Sasi Kumar, P R; Nampoori, V P N; Vallabhan, C P G(IOP, 1994)
[+]
[-]
Abstract:
Laser-induced photoelectric and photoemission optogalvanic effects in a Ne-Nd hollow cathode discharge have been studied using a continuous wave laser source. The potential barrier for photoinduced electron emission from the cathode decreases as the applied voltage is increased. Owing to secondary electron emission in the plasma, the photocurrent is greater than that without discharge. The multiplication of secondary electrons and the quantum efficiency are also investigated.
Sasi Kumar, P R; Nampoori, V P N; Vallabhan, C P G(Elsevier, August 1, 1995)
[+]
[-]
Abstract:
The photoemission optogalvanic (POG) effect has been investigated in a neon-neodymium hollow cathode discharge using
cw laser excitation. Both positive and negative effects were observed. It was found that the amplitude of the POG signal was
unstable near the instability region of the discharge.
Sasi Kumar, P R; Nampoori, V P N; Vallabhan, C P G(IOP, 1993)
[+]
[-]
Abstract:
A two-photon induced photoemission optogalvanic effect which brings about a change in the discharge voltage when a pulsed dye laser beam is focused on a tungsten electrode has been described. The experiment is performed with N2, NO2 and Ar discharges. The magnitude of the signal voltage is studied as a function of laser energy and discharge current. The effective quantum efficiency in the discharge is found to be larger than that in the vacuum condition.
Sasi Kumar, P R; Nampoori, V P N; Vallabhan, C P G(IOP, 1993)
[+]
[-]
Abstract:
A two-photon induced photoemission optogalvanic effect which brings about a change in the discharge voltage when a pulsed dye laser beam is focused on a tungsten electrode has been described. The experiment is performed with N2, NO2 and Ar discharges. The magnitude of the signal voltage is studied as a function of laser energy and discharge current. The effective quantum efficiency in the discharge is found to be larger than that in the vacuum condition.
Ajith Prasad, K C; Nampoori, V P N; Vallabhan, C P G(Elsevier, 1996)
[+]
[-]
Abstract:
Photoemission optogalvanaic (POG) effect has been observed by irradiating copper target electrode, in a nitrogen discharge cell using 1.06 μm and frequency doubled 532 nm Nd:YAG laser pulse. Measurement of the nature of the variation of POG signal strength with 532 nm laser fluence confirms the two photon induced photoelectric emission from copper. However, using 1.06 μm laser pulses thermally assisted photoemission is observed.
Shali, N B; Sugunan, S(Springer Netherlands, 2007)
[+]
[-]
Abstract:
Lanthana modified sol-gel titania is prepared
through particulate sol-gel route and the physico-chemical
characterizations of the prepared systems were done using
X-Ray diffration, EDX, BET surface area-pore volume measurements
and TG-DTG analysis. Benzophenone was observed
to be the sole product in the TiO2 photocatalyzed
oxidation of benzhydrol in oxygen purged acetonitrile. The
influence of various parameters, like irradiation time, amount
of catalyst, concentration of the catalyst and other factors on
the photocatalytic oxidation has been investigated. The proposed
mechanism envisages the involvement of a superoxide
radical anion.
ZnO micro particles in the range 0.4-0.6 μm were synthesized by microwave irradiation
method. The XRD analysis reveals that the sample is in the wurtzite phase with orientation
along the (101) plane. SAED pattern of the sample reveals the single crystalline nature of
the micro grains. TEM images show the formation of cylindrical shaped ZnO micro
structures with hexagonal faces. The optical phonon modes were slightly shifted in the
Raman spectrum,attributed to the presence of various crystalline defects and laser induced
local heating at the grain boundaries. A broad transmission profile was observed in the
FTIR spectrum from 1550-3400 cm-1 which falls in the atmospheric transparency window
region. PL spectrum centered at 500 nm with a broad band in the region 420-570 nm
comprised of different emission peaks attributed to transition between defect levels.
Various emission levels in the sample were expliained with a band diagram
Description:
Journal of Optoelectronics and Biomedical Materials Vol. 4, Issue 1, January-March 2012, p. 1 - 7
Junaid, Bushiri M; Saji, Chacko; Vaidyan, V K(IOP Publishing LTD, October 20, 2006)
[+]
[-]
Abstract:
SnO2 nanocrystalline thin films were deposited on glass substrates by the
spray pyrolysis technique in air atmosphere at 375, 400, 425, 450 and
500 ◦C substrate temperatures. The obtained films were characterized by
using XRD. The room temperature photoluminescence (PL) spectra of these
films have near band edge (NBE) and deep level emission under the
excitation of 325 nm radiation. NBE PL peak intensity decreased
consistently with temperatures for samples prepared at 400, 450 and 500 ◦C,
while a sudden reduction in intensity is observed for the sample prepared at
425 ◦C. A similar effect was observed for the optical transmittance spectra.
These effects can be explained on the basis of the change in population of
oxygen vacancies as indicated by the change in a values
Lyjo, Joseph K; Dayas, K R; Soniya, Damodar; Bindu, Krishnan; Krishnankutty, K; Nampoori, V P N; Radhakrishnan, P(Elsevier, December 15, 2008)
[+]
[-]
Abstract:
The laser-induced luminescence studies of the rare earth titanates (R2Ti2O7) (R = La, Nd and Gd) using 355 nm radiation from an Nd:YAG laser are presented. These samples with submicron or nanometer size are prepared by the self-propagating high temperature synthesis (SHS) method and there is no known fluorescence shown by these rare earths in the visible region. Hence, the luminescence transitions shown by the La2Ti2O7 near 610 nm and Gd2Ti2O7 near 767 nm are quite interesting. Though La3+ ions with no 4f electrons have no electronic energy levels that can induce excitation and luminescence processes in the visible region, the presence of the Ti3+ ions leads to luminescence in this region.
Anantharaman, M R; Saravanan, S; Joseph, Mathai C; Venkatachalam, S; Avasthi, D K; Singh, F(Elsevier, November 15, 2005)
[+]
[-]
Abstract:
Conjugated polymers in the form of thin films play an important role in the field of materials science due to their interesting properties. Polymer
thin films find extensive applications in the fabrication of devices, such as light emitting devices, rechargeable batteries, super capacitors, and
are used as intermetallic dielectrics and EMI shieldings. Polymer thin films prepared by plasma-polymerization are highly cross-linked, pinhole
free, and their permittivity lie in the ultra low k-regime. Electronic and photonic applications of plasma-polymerized thin films attracted the
attention of various researchers. Modification of polymer thin films by swift heavy ions is well established and ion irradiation of polymers can
induce irreversible changes in their structural, electrical, and optical properties. Polyaniline and polyfurfural thin films prepared by RF plasmapolymerization
were irradiated with 92MeV silicon ions for various fluences of 1×1011 ions cm−2, 1×1012 ions cm−2, and 1×1013 ions cm−2.
FTIR have been recorded on the pristine and silicon ion irradiated polymer thin films for structural evaluation. Photoluminescence (PL) spectra
were recorded for RF plasma-polymerized thin film samples before and after irradiation. In this paper the effect of swift heavy ions on the structural
and photoluminescence spectra of plasma-polymerized thin films are investigated.