ABSTRACT: The rheological and extrudate behaviour of natural rubber/latex
reclaim blends were evaluated using a capillary viscometer . The study shows
that the viscosity of natural rubber decreases marginally on the addition of
latex reclaim while the variation of viscosity with shear rate is not affected.
The temperature sensitivity of the blends is not affected significantly with the
addition of latex reclaim . The extrudates of natural rubber/latex reclaim
blends are smooth up to the addition of about 50 wt. percent latex reclaim in
filled natural rubber compounds.
Paraphenylenediamine and diphenylamine were chemically
attached to natural rubber during mastication . The rubber bound antioxidants
were characterized by TLC, 'H-NMR, IR and TGA. The efficiency and
permenance of these bound antioxidants were compared with a conventional
amine type antioxidant in filled natural rubber vulcanizates . The rubber
bound antioxidants were found to be less volatile and less extractable as compared
to conventional antioxidants. The vulcanizates showed improved ageing
resistance as compared to vulcanizates containing conventional antioxidants.
This semisolid rubber bound antioxidant can reduce the amount of plasticizer
required for compounding.
Para-phenylenediamine (PD) was chemically attached to depolymerized natural rubber by
a photochemical reaction . The rubber bound PD was characterized by TLC, 1H-NMR, IR,
and TGA. The efficiency and permanence of the bound PD were compared with conventional
antioxidants in NBR vulcanizates . The rubber bound PD was found to be less volatile and
more resistant to water and oil extraction . The vulcanizates showed improved aging resistance
in comparison to vulcanizates containing conventional antioxidants. The liquid rubber
bound antioxidant reduces the amount of plasticizer required for compounding
Rani, Joseph(OPA (Overseas Publishers Association), May 28, 1995)
[+]
[-]
Abstract:
Amine Terminated Liquid Natural Rubber (ATNR) was used as a plasticiser in filled NR and NBR
compounds replacing oil/DOP. The scorch time and cure time were found to be lowered when ATNR
was used as the plasticiser. ATNR was found to improve the mechanical properties like tensile strength,
tear strength and modulus of the vulcanizates . The ageing resistance of the vulcanizates containing ATNR
was superior compared to the vulcanizates containing oil/DOP.