Abstract: | Invertase was adsorbed onto micro-porous acid-activated montmorillonite clay (K-10) by two procedures, namely adsorption and covalent binding. The immobilized enzymes were characterized by XRD, surface area measurements and 27Al NMR. XRD measurements revealed an expansion of clay layers due to immobilization which suggests that intercalation had taken place. Surface area measurements also support this observation. 27Al NMR showed that interaction of enzyme with tetrahedral and octahedral Al changes with the immobilization procedure. Sucrose hydrolysis was performed in a batch reactor. The immobilized enzymes showed enhanced pH and thermal stabilities. Optimum pH and temperature were found to increase upon immobilization. The effectiveness factor (η) and Michaelis constant (Km) suggest that diffusional resistances play a major role in the reaction. The immobilized invertase could be stored in buffer of pH 5 and 6 at 5 °C without any significant loss in activity for 20 days. |
URI: | http://dyuthi.cusat.ac.in/purl/2261 |
Files | Size |
---|---|
Dyuthi-SS53.pdf | (138.2Kb) |
Abstract: | Invertase was immobilized on acid activated montmorillonite via two independent procedures, adsorption and covalent binding. The immobilized enzymes were characterized by XRD, NMR and N2 adsorption measurements and their activity was tested in a fixed bed reactor. XRD revealed that the enzyme was situated on the periphery of the clay and the side chains of different amino acid residues were involved in intercalation with the clay matrix. NMR demonstrated that tetrahedral Al was linked to the enzyme during adsorption and the octahedral Al was involved during covalent binding. Secondary interaction of the enzyme with Al was also observed. N2 adsorption studies showed that covalent binding of enzymes caused pore blockage since the highly polymeric species were located at the pore entrance. The fixed bed reactor proved to be efficient for the immobilized invertase. The optimum pH and pH stability improved upon immobilization. The kinetic parameters calculated also showed an enhanced efficiency of the immobilized systems. They could be used continuously for long period. Covalently bound invertase demonstrated greater operational stability. |
URI: | http://dyuthi.cusat.ac.in/purl/2270 |
Files | Size |
---|---|
Dyuthi-SS60.pdf | (481.4Kb) |
Abstract: | Glucoamylase from Aspergillus Niger was immobilized on montmorillonite clay (K-10) by two procedures, adsorption and covalent binding. The immobilized enzymes were characterized using XRD, surface area measurements and 27Al MAS NMR and the activity of the immobilized enzymes for starch hydrolysis was tested in a fixed bed reactor (FBR). XRD shows that enzyme intercalates into the inter-lamellar space of the clay matrix with a layer expansion up to 2.25 nm. Covalently bound glucoamylase demonstrates a sharp decrease in surface area and pore volume that suggests binding of the enzyme at the pore entrance. NMR studies reveal the involvement of octahedral and tetrahedral Al during immobilization. The performance characteristics in FBR were evaluated. Effectiveness factor (η) for FBR is greater than unity demonstrating that activity of enzyme is more than that of the free enzyme. The Michaelis constant (Km) for covalently bound glucoamylase was lower than that for free enzyme, i.e., the affinity for substrate improves upon immobilization. This shows that diffusional effects are completely eliminated in the FBR. Both immobilized systems showed almost 100% initial activity after 96 h of continuous operation. Covalent binding demonstrated better operational stability. |
URI: | http://dyuthi.cusat.ac.in/purl/2316 |
Files | Size |
---|---|
Dyuthi-SS84.pdf | (422.1Kb) |
Abstract: | Invertase was immobilised on microporous montmorillonite K-10 via adsorption and covalent binding. The immobilised enzymes were tested for sucrose hydrolysis activity in a batch reactor. Km for immobilised systems was greater than free enzyme. The immobilised forms could be reused for 15 continuous cycles without any loss in activity. After 25 cycles, 85% initial activity was retained. A study on leaching of enzymes showed that 100% enzyme was retained even after 15 cycles of reuse. Leaching increased with reaction temperature. Covalent binding resisted leaching even at temperatures of 70 °C. |
URI: | http://dyuthi.cusat.ac.in/purl/2312 |
Files | Size |
---|---|
Dyuthi-SS80.pdf | (185.0Kb) |
Abstract: | Thermal diffusivity (TD) measurements were performed on some industrially important dyes – auramine O (AO), malachite green and methylene blue (MB) – adsorbed K-10 montmorillonites using photoacoustic method. The TD value for the dye-adsorbed clay mineral was observed to change with a variation in dye concentration. The contribution of the dye towards TD was also determined. The repeatedly adsorbed samples with MB and AO exhibited a lower TD than the single-adsorbed samples. TD values of sintered MB samples were also obtained experimentally. These sintered samples exhibit a higher TD, although they show a trend similar to that of non-sintered pellets. A variation in dye concentration and sintering temperature can be used for tuning the TD value of the clay mineral to the desired level |
Description: | Philosophical Magazine Vol. 89, No. 10, 1 April 2009, 895–905 |
URI: | http://dyuthi.cusat.ac.in/purl/3998 |
Files | Size |
---|---|
Thermal charact ... d K-10 montmorillonite.pdf | (388.6Kb) |
Abstract: | Thermal diffusivity (TD) measurements were performed on some industrially important dyes – auramine O (AO), malachite green and methylene blue (MB) – adsorbed K-10 montmorillonites using photoacoustic method. The TD value for the dye-adsorbed clay mineral was observed to change with a variation in dye concentration. The contribution of the dye towards TD was also determined. The repeatedly adsorbed samples with MB and AO exhibited a lower TD than the single-adsorbed samples. TD values of sintered MB samples were also obtained experimentally. These sintered samples exhibit a higher TD, although they show a trend similar to that of non-sintered pellets. A variation in dye concentration and sintering temperature can be used for tuning the TD value of the clay mineral to the desired level. |
URI: | http://dyuthi.cusat.ac.in/purl/2621 |
Files | Size |
---|---|
Dyuthi-P0182.pdf | (398.5Kb) |
Abstract: | Thermal diffusivity (TD) measurement on commercial K-10 and KSF montmorillonites was carried out by photoacoustic technique. The TD of the montmorillonites after methylene blue adsorption changed with the dye concentration. The repeatedly adsorbed samples showed a lesser TD than the single adsorbed samples. After methylene blue adsorption the acid leached K-10 samples showed well defined changes in TD when compared to the ordered KSF samples. |
URI: | http://dyuthi.cusat.ac.in/purl/1756 |
Files | Size |
---|---|
pdf 3.pdf | (325.8Kb) |
Abstract: | Thermal diffusivity (TD) measurement on commercial K-10 and KSF montmorillonites was carried out by photoacoustic technique. The TD of the montmorillonites after methylene blue adsorption changed with the dye concentration. The repeatedly adsorbed samples showed a lesser TD than the single adsorbed samples. After methylene blue adsorption the acid leached K-10 samples showed well defined changes in TD when compared to the ordered KSF samples |
Description: | Applied Clay Science 42 (2009) 483–487 http://dx.doi.org/10.1016/j.clay.2008.06.006 |
URI: | http://dyuthi.cusat.ac.in/purl/3999 |
Files | Size |
---|---|
Thermal charact ... ed montmorillonites by.pdf | (325.8Kb) |
Now showing items 1-8 of 8
Dyuthi Digital Repository Copyright © 2007-2011 Cochin University of Science and Technology. Items in Dyuthi are protected by copyright, with all rights reserved, unless otherwise indicated.