Sudha Kartha, C(Optical society of America, June 20, 2004)
[+]
[-]
Abstract:
A methylene-blue-sensitized polymer blend of polyvinyl alcohol and polyacrylic acid is fabricated and
tested for holographic recording. It was found to have good characteristics such as high sensitivity,
storage stability, ease of fabrication, and environmental stability. Optimization of the ratio of polyvinyl
alcohol polyacrylic acid, the sensitizer concentration, pH, energy, diffraction efficiency measurements,
etc., have been done. pH is found to have a great influence on the recovery of the dye in this matrix.
The results of experimental investigations into the properties of this new material are reported.
Sudha Kartha, C(Taylor and francis, October 20, 2003)
[+]
[-]
Abstract:
Polymer materials find application in optical storage technology,
namely in the development of high information density and fast access type
memories. A new polymer blend of methylene blue sensitized polyvinyl alcohol
(PVA) and polyacrylic acid (PAA) in methanol is prepared and characterized
and its comparison with methylene blue sensitized PVA in methanol and
complexed methylene blue sensitized polyvinyl chloride (CMBPVC) is presented.
The optical absorption spectra of the thin films of these polymers
showed a strong and broad absorption region at 670-650 nm, matching the
wavelength of the laser used. A very slow recovery of the dye on irradiation was
observed when a 7:3 blend of polyvinyl alcohol/polyacrylic acid at a pHof 3.8
and a sensitizer concentration of 4.67 10 5 g/ml were used. A diffraction
efficiency of up to 20% was observed for the MBPVA/alcohol system and an
energetic sensitivity of 2000 mJ/cm2 was obtained in the photosensitive films
with a spatial frequency of 588 lines/mm.